Liquid phase sintering of silicon carbide
Assignee: Ceramatec Inc
•
Filing: 1988-04-21
•
Granted: 1989-05-09
•
Expires: 2008-04-21
Abstract
Abstract Liquid phase sintering is used to densify silicon carbide based ceramics using a compound comprising a rare earth oxide and aluminum oxide to form liquids at temperatures in excess of 1600° C. The resulting sintered ceramic body has a density greater than 95% of its theoretical density and hardness in excess of 23 GPa. Boron and carbon are not needed to promote densification and silicon carbide powder with an average particle size of greater than one micron can be densified via the liquid phase process. The sintered ceramic bodies made by the present invention are fine grained and have secondary phases resulting from the liquid phase.
Inventors
- 👤 Raymond A. Cutler
- 👤 Anil V. Virkar
- 👤 Andrew C. Hurford
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 22:34
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/515; C04B35/56; C04B35/565; C04B35/575; C04B35/5755
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
144 words
A process for liquid phase sintering of silicon carbide comprising: forming a mixture consisting essentially of silicon carbide particles having a size of from about 2 to about 5 microns and from about 0.5 percent to about 19.5 percent by weight of a rare earth oxide and from about 0.5 percent to about 19.5 percent by weight alumina; forming a shape with said mixture; and sintering said mixture at a temperature of from about 1700° to about 2200° centrigrade for about 1 minute to about 30 minutes to form a liuqid phase and a resultant sintered ceramic body having a hardness exceeding about 22 GPa comprising 2% to 20% by weight of a compound wherein the molar ratio of rare earth oxide to alumina in said compound is at least three to five and from about 80% to about 98% by weight silicon carbide.
Claim 2
Dependent Claim
144 words
A process for liquid phase sintering of silicon carbide comprising: forming a mixture consisting essentially of silicon carbide particles having a size of from about 2 to about 5 microns and from about 0.5 percent to about 19.5 percent by weight of a rare earth oxide and from about 0.5 percent to about 19.5 percent by weight alumina; forming a shape with said mixture; and sintering said mixture at a temperature of from about 1700° to about 2200° centrigrade for about 1 minute to about 30 minutes to form a liuqid phase and a resultant sintered ceramic body having a hardness exceeding about 22 GPa comprising 2% to 20% by weight of a compound wherein the molar ratio of rare earth oxide to alumina in said compound is at least three to five and from about 80% to about 98% by weight silicon carbide.
Claim 3
Dependent Claim
16 words
The process of claim 1 wherein said silicon carbide particles are alpha phase silicon carbide particles.
Claim 4
Dependent Claim
16 words
The process of claim 1 wherein said silicon carbide particles are beta phase silicon carbide particles.
Claim 5
Dependent Claim
22 words
The process of claim 1 wherein said silicon carbide particles comprise a mixture of alpha phase and beta phase silicon carbide particles.
Claim 6
Dependent Claim
16 words
The process of claim 1 wherein said sintering temperature is between about 1900° and 2100° centigrade.
Claim 7
Dependent Claim
30 words
The process according to claim 1 wherein said mixture of silicon carbide particles, rare earth oxide and alumina is sintered for for about 1 minute to less than 15 minutes.
Claim 8
Dependent Claim
30 words
The process according to claim 1 including hot isostatically pressing said densified mixture at a pressure and for a period of time to increase the density of said sintered body.
Claim 9
Dependent Claim
38 words
The process of claim 1 including hot isostatically pressing said densified mixture at a pressure and for a period of time to increase the density of said sintered silicon carbide body to greater than about 99% of theoretical.
Claim 10
Dependent Claim
57 words
The process of claim 8 wherein said sintering and hot isostatic steps are combined so that a green ceramic body is first sintered to a state of closed porosity in a pressure of less than about 15 MPa and said resultant ceramic body is then pressurized at pressures of at least 35 MPa to reduce the porosity.
Claim 11
Dependent Claim
80 words
A sintered ceramic body comprising a uniform mixture of: from about 80% to about 98% by weight silicon carbide, and from about 2% to about 23% by weight of a compound, said compound comprising: alumina, and a rare earth oxide, wherein the molar ratio of rare earth oxide to alumina in said compound is at least three to five, and wherein said sintered ceramic body has a density greater than 95% of theoretical, and a hardness greater than 20 GPa.
Claim 12
Dependent Claim
80 words
A sintered ceramic body comprising a uniform mixture of: from about 80% to about 98% by weight silicon carbide, and from about 2% to about 23% by weight of a compound, said compound comprising: alumina, and a rare earth oxide, wherein the molar ratio of rare earth oxide to alumina in said compound is at least three to five, and wherein said sintered ceramic body has a density greater than 95% of theoretical, and a hardness greater than 20 GPa.
Claim 13
Dependent Claim
21 words
The sintered ceramic body of claim 10 wherein said molar ratio of rare earth oxide to alumina is at least 1:1.
Claim 14
Dependent Claim
19 words
The sintered ceramic body of claim 11 wherein said molar ratio of rare earth oxide to alumina is 2:1.
Claim 15
Dependent Claim
18 words
The sintered ceramic body of claim 10 wherein said rare earth oxide is Y 2 O 3 .
Claim 16
Dependent Claim
20 words
The sintered ceramic body of claim 13 wherein the silicon carbide has average grain sizes of less than ten micrometers.
Claim 17
Dependent Claim
28 words
The sintered ceramic body of claim 10 wherein said compound of rare earth oxide and alumina comprises less than 10 percent by weight of the sintered ceramic body.
Claim 18
Dependent Claim
18 words
The sintered ceramic body of claim 10 wherein said ceramic body has a hardness which exceeds 23 GPa.
Claim 19
Dependent Claim
19 words
The sintered ceramic body of claim 10 wherein said sintered ceramic body has a hardness which exceeds 26 GPa.
References Cited (Backward Citations)
US4097293A
Cited
SU391106A1
Cited
US4158687A
Cited
US4146379A
Cited
US4141740A
Cited
JPS55116669A
Cited
US4341533A
Cited
GB2140823A
Cited
JPS5717465A
Cited
JPS57166370A
Cited
JPS5836376A
Cited
JPS5891146A
Cited
JPS5891070A
Cited
JPS5891069A
Cited
GB2125066A
Cited
GB2133042A
Cited
US4569922A
Cited
US4502983A
Cited
JPS6033263A
Cited
US4581295A
Cited
DE3516587A1
Cited
EP0188129A2
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-05-08 | 1992-11-07 | 1993-05-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-05-08 | 1996-11-07 | 1997-05-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-05-08 | 2000-11-07 | 2001-05-09 | $7700.00 | Window Closed / Lapsed |