Process for the manufacture of molded parts from fibrous material and fiber matting for the manufacture of molded parts
Assignee: LIGNOTOK GmbH
•
Filing: 1985-04-02
•
Granted: 1989-05-09
•
Expires: 2005-04-02
Abstract
Abstract A process for the manufacture of molded parts from fibrous material, particularly cellulose-containing fibers. A particulate binder is incorporated into a fiber filling after which the mixture is precompacted into a fiber mat which is subjected to a hot steam treatment and is finally molded into the finished part under pressure and heat. The binder consists of thermoplastic particles into which a blowing agent is incorporated by forming an alloy-like state which is activated prior to final molding of the part, preferably by means of hot steam treatment, and a binder which cross-links when exposed to heat applied to the surface of the particles.
Inventors
- 👤 Gunter H. Kiss
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 17:31
CPC Classifications
B; B27; B27N; B27N3/00; B27N3/005; Y; Y10; Y10S; Y10S264/00; Y10S264/18; Y10T; Y10T428/00; Y10T428/249921; Y10T428/249953; Y10T428/249986; Y10T442/00; Y10T442/20; Y10T442/2762; Y10T442/277; Y10T442/2861; Y10T442/60
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
143 words
A process for the manufacture of molded parts from fibrous material comprising the steps of: blending the fibrous material with a particulate binder material, the binder material being a thermoplastic resin material with a blowing agent integrally blended therein and, the thermoplastic binder coated with at least one heat-activated cross-linking agent; the blended fibrous material and binder material into a loose matting; placing the loose matting into a mold; heating the emitting to a first elevated temperature to activate the blowing agent and soften the thermoplastic material, the first elevated temperature being below that sufficient to initiate cross-linking of the heat-activated cross-linked agent; compressing the matting within the closed mold after activating the blowing agent; and, then heating the matting compressed in the mold to a second elevated temperature, the second elevated temperature sufficiently high to permit activation of the heat-activated cross-linking agent.
Claim 2
Dependent Claim
143 words
A process for the manufacture of molded parts from fibrous material comprising the steps of: blending the fibrous material with a particulate binder material, the binder material being a thermoplastic resin material with a blowing agent integrally blended therein and, the thermoplastic binder coated with at least one heat-activated cross-linking agent; the blended fibrous material and binder material into a loose matting; placing the loose matting into a mold; heating the emitting to a first elevated temperature to activate the blowing agent and soften the thermoplastic material, the first elevated temperature being below that sufficient to initiate cross-linking of the heat-activated cross-linked agent; compressing the matting within the closed mold after activating the blowing agent; and, then heating the matting compressed in the mold to a second elevated temperature, the second elevated temperature sufficiently high to permit activation of the heat-activated cross-linking agent.
Claim 3
Dependent Claim
37 words
The process of claim 1 wherein the binder material is a homogeneous mixture of the thermoplastic binder and the blowing agent incorporated in particulate form, the particles being coated with at least one heat activated cross-linking agent.
Claim 4
Dependent Claim
19 words
The process of claim 2 wherein the first elevated temperature is achieved by exposing the matting to hot steam.
Claim 5
Dependent Claim
14 words
The process of claim 1 wherein cellulose-containing fibers are used as the fibrous material.
Claim 6
Dependent Claim
45 words
The process of claim 1 further comprising the steps of: spraying said particulate thermoplastic material into which a blowing agent has been integrally blended with a liquid heat-activated cross-linking agent; and drying the resulting particles prior to addition of the particles to the fibrous material.
Claim 7
Dependent Claim
21 words
The process of claim 5 wherein the thermoplastic resin binder material is incorporated in the fibrous material in a dry state.
Claim 8
Dependent Claim
49 words
The process of claim 1 wherein the thermoplastic resin binder is present as particles and is sprayed with the heat-activated cross-linking agent in liquid form in order to coat the former, and the mixture is subsequently incorporated in the fibrous material of the matting by spraying the particles therein.
Claim 9
Dependent Claim
63 words
The process of claim 1 wherein the concentration of the particulate thermoplastic binder containing the blowing agent and coated with at least one binder which cross-links when exposed to heat incorporated in the fiber matting varies with respect to the thickness of the fiber matting such that the concentration is less at the surface areas of the fiber matting than in its center.
Claim 10
Dependent Claim
26 words
The process of claim 8 further comprising the step of introducing an additional amount of cross-linking agent into the outer surface area of the fiber matting.
Claim 11
Dependent Claim
17 words
The process of claim 9 wherein the heat-activated cross-linking agents consist of substances with varying cross-linking characteristics.
Claim 12
Dependent Claim
31 words
The process of claim 1 wherein between about 10 and about 30 percent by weight binder material based on the overall weight of the matting are blended with the fibrous material.
Claim 13
Dependent Claim
44 words
A fiber matting for the manufacture of molded parts according to the process of claim 1 wherein a particulate thermoplastic binder containing a blowing agent and coated with at least one heat-activated cross-linking is incorporated in fibrous material after the fibrous material is computed.
Claim 14
Dependent Claim
13 words
The fiber matting of claim 12 wherein the thermoplastic binder particles are spherical.
Claim 15
Dependent Claim
18 words
The fiber matting of claim 12 wherein the thermoplastic binder particles have an elongated, particularly a thread-like, form.
Claim 16
Dependent Claim
17 words
The fiber matting of claim 12 wherein the heat-activated cross-linking agent contains elastomeric substances such as acrylonitrile-butadiene.
Claim 17
Dependent Claim
29 words
The fiber matting of claim 12 wherein the thermoplastic binder containing a blowing agent consists essentially of non-expanded polystyrene particles having a grain size between 0.1 and 1.0 mm.
Claim 18
Dependent Claim
28 words
The fiber matting of claim 13 wherein the fibrous material is selected from the group consisting of cellulose-containing fibers, synthetic textile fibers, natural textile fibers or mixtures thereof.
References Cited (Backward Citations)
US3764428A
Cited
US3671377A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-05-08 | 1992-11-07 | 1993-05-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-05-08 | 1996-11-07 | 1997-05-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-05-08 | 2000-11-07 | 2001-05-09 | $7700.00 | Window Closed / Lapsed |