Process for the production of microporous polybenzimidazole articles
Assignee: Hoechst Celanese Chemical Co
•
Filing: 1987-08-20
•
Granted: 1989-05-09
•
Expires: 2007-08-20
Abstract
Abstract Disclosed herein are microporous polybenzimidazole articles prepared by the addition of a leachable additive to a polybenzimidazole polymer solution or dope and the subsequent leaching of the additive from the polybenzimidazole article. The microporous polybenzimidazole article may be formed into filaments or films. The micropores of the microporous polybenzimidazole article may be filled with an absorbent resin which will act to absorb chemicals or other harmful products. The microporous polybenzimidazole article with absorbent material may be formed into clothing which is highly resistant to both chemicals and heat.
Inventors
- 👤 John W. Soehngen
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 04:52
CPC Classifications
B; B01; B01D; B01D71/00; B01D71/06; B01D71/58; B01D71/62; B01D67/00; B01D67/0002; B01D67/0023; B01D67/003; C; C08; C08J; C08J9/00; C08J9/26; C08J9/28; C08J2201/00; C08J2201/04; C08J2201/044; C08J2201/0444; C08J2201/05; C08J2201/0502; C08J2379/00; C08J2379/04
Claims Analysis
Total Claims: 26
Claim 1
Independent Claim
86 words
A microporous polybenzimidazole product produced by a process comprising the steps of: (a) preparing a polybenzimidazole polymer solvent solution; (b) mixing with the polybenzimidazole polymer solution a leachable additive to form a polybenzimidazole polymer with an interspersed leachable additive; (c) forming a polybenzimidazole shaped article from the polybenzimidazole polymer with leachable additive interspersed within its structure; and (d) removing the leachable additive from the polybenzimidazole shaped article to form a microporous polybenzimidazole article with a pore size ranging from about 0.01 microns to about 0.5 microns.
Claim 2
Dependent Claim
86 words
A microporous polybenzimidazole product produced by a process comprising the steps of: (a) preparing a polybenzimidazole polymer solvent solution; (b) mixing with the polybenzimidazole polymer solution a leachable additive to form a polybenzimidazole polymer with an interspersed leachable additive; (c) forming a polybenzimidazole shaped article from the polybenzimidazole polymer with leachable additive interspersed within its structure; and (d) removing the leachable additive from the polybenzimidazole shaped article to form a microporous polybenzimidazole article with a pore size ranging from about 0.01 microns to about 0.5 microns.
Claim 3
Dependent Claim
82 words
A microporous polybenzimidazole filament produced by process comprising the steps of: (a) preparing a polybenzimidazole polymer solvent solution; (b) mixing with the polybenzimidazole polymer solution a leachable additive to form a polybenzimidazole polymer with an interspersed leachable additive; (c) spinning the polybenzimidazole polymer with interspersed leachable additive into a polybenzimidazole filamentary material; and (d) removing the leachable additive from the polybenzimidazole filamentary material to form a microporous polybenzimidazole filament with a pore size ranging from about 0.01 microns to about 0.5 microns.
Claim 4
Dependent Claim
82 words
A microporous polybenzimidazole filament produced by process comprising the steps of: (a) preparing a polybenzimidazole polymer solvent solution; (b) mixing with the polybenzimidazole polymer solution a leachable additive to form a polybenzimidazole polymer with an interspersed leachable additive; (c) spinning the polybenzimidazole polymer with interspersed leachable additive into a polybenzimidazole filamentary material; and (d) removing the leachable additive from the polybenzimidazole filamentary material to form a microporous polybenzimidazole filament with a pore size ranging from about 0.01 microns to about 0.5 microns.
Claim 5
Dependent Claim
82 words
A microporous polybenzimidazole film produced by a process comprising the steps of: (a) preparing a polybenzimidazole polymer solvent solution; (b) mixing with the polybenzimidazole polymer solution a leachable additive to form a polybenzimidazole polymer with an interspersed leachable additive; (c) casting the polybenzimidazole polymer with interspersed leachable additive into a polybenzimidazole film; and (d) removing the leachable additive from the polybenzimidazole film to form a microporous polybenzimidazole polymer film with a pore size ranging from about 0.01 microns to about 0.5 microns.
Claim 6
Dependent Claim
82 words
A microporous polybenzimidazole film produced by a process comprising the steps of: (a) preparing a polybenzimidazole polymer solvent solution; (b) mixing with the polybenzimidazole polymer solution a leachable additive to form a polybenzimidazole polymer with an interspersed leachable additive; (c) casting the polybenzimidazole polymer with interspersed leachable additive into a polybenzimidazole film; and (d) removing the leachable additive from the polybenzimidazole film to form a microporous polybenzimidazole polymer film with a pore size ranging from about 0.01 microns to about 0.5 microns.
Claim 7
Dependent Claim
114 words
A microporous polybenzimidazole filament produced by a process comprising the steps of: (a) preparing a polybenzimidazole polymer solvent solution; (b) mixing the polybenzimidazole polymer solvent solution with an inorganic metal salt to form a polybenzimidazole polymer with interspersed inorganic metal salt; (c) spinning the polybenzimidazole polymer with interspersed inorganic metal salt into a polybenzimidazole filamentary material; and (d) washing the filament in water at a temperature from about 30° C. to about 100° C. for a period of about 30 seconds to several hours to remove the inorganic metal salt from the polybenzimidazole filamentary material to form a microporous polybenzimidazole filament with a pore size ranging from about 0.01 microns to about 0.5 microns.
Claim 8
Dependent Claim
114 words
A microporous polybenzimidazole filament produced by a process comprising the steps of: (a) preparing a polybenzimidazole polymer solvent solution; (b) mixing the polybenzimidazole polymer solvent solution with an inorganic metal salt to form a polybenzimidazole polymer with interspersed inorganic metal salt; (c) spinning the polybenzimidazole polymer with interspersed inorganic metal salt into a polybenzimidazole filamentary material; and (d) washing the filament in water at a temperature from about 30° C. to about 100° C. for a period of about 30 seconds to several hours to remove the inorganic metal salt from the polybenzimidazole filamentary material to form a microporous polybenzimidazole filament with a pore size ranging from about 0.01 microns to about 0.5 microns.
Claim 9
Dependent Claim
123 words
A microporous polybenzimidazole film produced by a process comprising the steps of: (a) preparing a polybenzimidazole polymer solvent solution; (b) mixing with the polybenzimidazole polymer solvent solution lithium chloride comprising about 10 to about 40 percent by weight based on the total polymer weight to form a polybenzimidazole polymer with interspersed lithium chloride; (c) casting the polybenzimidazole polymer with interspersed lithium chloride solution into a polybenzimidazole film; (d) washing the film in water maintained at a temperature from about 0° C. to about 100° C. for a period of about 30 seconds to several hours to remove the lithium chloride from the polybenzimidazole film to form a microporous polybenzimidazole film with a pore size ranging from about 0.01 microns to about 0.5 microns.
Claim 10
Dependent Claim
123 words
A microporous polybenzimidazole film produced by a process comprising the steps of: (a) preparing a polybenzimidazole polymer solvent solution; (b) mixing with the polybenzimidazole polymer solvent solution lithium chloride comprising about 10 to about 40 percent by weight based on the total polymer weight to form a polybenzimidazole polymer with interspersed lithium chloride; (c) casting the polybenzimidazole polymer with interspersed lithium chloride solution into a polybenzimidazole film; (d) washing the film in water maintained at a temperature from about 0° C. to about 100° C. for a period of about 30 seconds to several hours to remove the lithium chloride from the polybenzimidazole film to form a microporous polybenzimidazole film with a pore size ranging from about 0.01 microns to about 0.5 microns.
Claim 11
Dependent Claim
43 words
The product as in any of claims 1, 2 or 3 wherein the leachable additive employed is soluble in the polybenzimidazole solvent solution and is selected from the group consisting of inorganic metal salts, low molecular weight esters, polyols and polyalkelene oxide-based surfactants.
Claim 12
Dependent Claim
64 words
The product as in any of claims 1, 2 or 3 wherein the leachable additive includes inorganic metal salts soluble in the solvent for the polybenzimidazole selected from the group consisting of lithium, sodium, potassium and strontium metals formed into a salt with anions selected from the group consisting of carboxylate materials having from one to 12 atoms, sulfonates, halides, phosphates, and the like.
Claim 13
Dependent Claim
43 words
The product as in any of claims 1, 2 or 3 wherein the leachable additive employed is a low molecular weight ester (molecular weight less than about 2000) selected from the group consisting of ethyl acetate, methyl acetate, methyl proprionate and methyl butyrate.
Claim 14
Dependent Claim
33 words
The product as in any of claims 1, 2, or 3 wherein the leachable additive employed is a polyol selected from the group consisting of propylene glycol, hexamethylene glycol, glycerine, trimethylopropane and trimethyloethane.
Claim 15
Dependent Claim
18 words
The product as in any of claims 1, 2 or 3 wherein the leachable additive is lithium chloride.
Claim 16
Dependent Claim
18 words
The product as in any of claims 1, 2 or 3 wherein the leachable additive is triethylene glycol.
Claim 17
Dependent Claim
22 words
The product as in any of claims 1, 2 or 3 wherein the leachable additive is a polyethylene or polypropylene oxide-based surfactant.
Claim 18
Dependent Claim
37 words
The product as in any of claims 1, 2 or 3 wherein the leachable additive comprises from about 10 to about 40 percent by weight based on the total weight of the polybenzimidazole polymer in the solution.
Claim 19
Dependent Claim
37 words
The product as in any of claims 1, 2 or 3 wherein the leachable additive is removed from the polybenzimidazole product by a solvent for the leachable additive which is also a nonsolvent for the polybenzimidazole polymer.
Claim 20
Dependent Claim
17 words
The product of claim 12 wherein the solvent employed for removal of the leachable additive is water.
Claim 21
Dependent Claim
39 words
The product as in any of claims 1, 2 or 3 wherein the leachable additive is removed by washing the polybenzimidazole article with a solvent for the leachable additive for a period from about 30 seconds to several hours.
Claim 22
Dependent Claim
98 words
The product as in any of claims 1, 2, 3, 4 or 5 wherein the polybenzimidazole polymer consists essentially of recurring units of the formula: ##STR4## wherein R is a tetravalent aromatic nucleus, with the nitrogen atoms forming the benzimidazole rings paired upon adjacent carbon atoms of said aromatic nucleus, and R' is selected from the group consisting of (1) an aromatic ring, (2) an alkylene group having from four to eight carbon atoms, and (3) a heterocyclic ring selected from the group consisting of (a) pyridine, (b) pyrazine, (c) furan, (d) quinoline, (e) thiophene, and (f) pyran.
Claim 23
Dependent Claim
50 words
The product as in any of claims 1, 2, 3, 4 or 5 wherein the polybenzimidazole polymer consists essentially of the recurring units of the formula: ##STR5## wherein Z is an aromatic nucleus having the nitrogen atoms forming the benzimidazole ring paired upon adjacent carbon atoms of the aromatic nucleus.
Claim 24
Dependent Claim
19 words
The product as in any of claims 1, 2, 3, 4 or 5 wherein the polybenzimidazole polymer is poly-2,2'-(m-phenylene)-5,5'-bibenzimidazole.
Claim 25
Dependent Claim
35 words
The product produced as in any of claims 1, 2, 3, 4 or 5 wherein a chemical absorbant is mixed with the microporous polybenzimidazole solvent solution prior to the formation of the microporous polybenzimidazole article.
Claim 26
Dependent Claim
12 words
The product of claim 20 wherein the chemical absorbant is acivated charcoal.
References Cited (Backward Citations)
US3720607A
Cited
US3699038A
Cited
US3737042A
Cited
US3951920A
Cited
US3841492A
Cited
US4020142A
Cited
US4448687A
Cited
US4512894A
Cited
US4628067A
Cited
US4693824A
Cited
US4693825A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-05-08 | 1992-11-07 | 1993-05-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-05-08 | 1996-11-07 | 1997-05-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-05-08 | 2000-11-07 | 2001-05-09 | $7700.00 | Window Closed / Lapsed |