Production of porous mullite bodies
Assignee: Imerys Minerals Ltd
•
Filing: 1988-08-08
•
Granted: 1989-05-02
•
Expires: 2008-08-08
Abstract
Abstract A particulate porous material suitable for use as a high surface area column packing material comprises particles substantially all of which are not smaller than 5 micrometers and not larger than 1 millimeter in diameter, and each particle is in the form of a substantially cellular body and consists predominantly of an open, three-dimensional matrix of crystals of mullite which define between them interconnecting pores having a width in the range of from 5 nanometers to about 2 micrometers. The particles can be coated with a reactive layer. There is also disclosed a process for producing the particulate porous material wherein a particulate product comprising particles substantially all of which are between 5 micrometers and 1 millimeter in diameter and consisting predominantly of a mixture of mullite crystals and silica is treated with a concentrated aqueous solution of an alkali metal hydroxide at a temperature of at least 50° C.; and the treated particulate product is then washed, dewatered and dried. The particulate porous material may be used as a packing material for a chromatographic or ion exchange column, or for performing biochemical separations, and is particularly useful for immobilizing biological components such as biological macromolecules or biological cells.
Inventors
- 👤 Thomas R. Jones
- 👤 Caryl Gould
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 11:52
CPC Classifications
B; B01; B01J; B01J20/00; B01J20/02; B01J20/10; B01J20/16; D; D21; D21H; D21H17/00; D21H17/63; D21H17/67; D21H17/68; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2982; Y10T428/2991; Y10T428/2993; Y10T428/2998; Y10T428/31504; Y10T428/31652; Y10T428/31663
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
189 words
A process for producing a particulate porous material which process comprises: (a) preparing a particulate product comprising particles substantially all of which are between 5 micrometers and 1 millimeter in diameter, each particle being in the form of a substantially cellular body and consisting predominantly of a mixture of mullite crystals and silica, by heat-treating by soak calcination an aluminosilcate material having an SiO 2 ·Al 2 O 3 molar ratio of at least 0.75:1 at a temperature in the range of from 1300° C. to 1800° C. for at least one hour; (b) treating the particulate product formed in (a) with a concentrated aqueous solution of an alkali metal hydroxide at a temperature of at least 50° C. whereby the silica is removed to leave mullite crystals which define between them interconnecting pores having a width in the range of from 5 nanometers to 5 micrometers; (c) washing the alkali metal hydroxide-treated particulate product formed in (b) until the washing medium is substantially free of silicate and alkali metal ions; and (d) dewatering and drying the washed product obtained in (c) to obtain the desired particulate porous material.
Claim 2
Dependent Claim
189 words
A process for producing a particulate porous material which process comprises: (a) preparing a particulate product comprising particles substantially all of which are between 5 micrometers and 1 millimeter in diameter, each particle being in the form of a substantially cellular body and consisting predominantly of a mixture of mullite crystals and silica, by heat-treating by soak calcination an aluminosilcate material having an SiO 2 ·Al 2 O 3 molar ratio of at least 0.75:1 at a temperature in the range of from 1300° C. to 1800° C. for at least one hour; (b) treating the particulate product formed in (a) with a concentrated aqueous solution of an alkali metal hydroxide at a temperature of at least 50° C. whereby the silica is removed to leave mullite crystals which define between them interconnecting pores having a width in the range of from 5 nanometers to 5 micrometers; (c) washing the alkali metal hydroxide-treated particulate product formed in (b) until the washing medium is substantially free of silicate and alkali metal ions; and (d) dewatering and drying the washed product obtained in (c) to obtain the desired particulate porous material.
Claim 3
Dependent Claim
43 words
A process according to claim 1, wherein the mixture of mullite crystals and silica is formed by heat-treating an aluminosilicate material having a SiO 2 ·Al 2 O 3 molar ratio of at least 0.75:1 at a temperature no greater than 1600° C.
Claim 4
Dependent Claim
42 words
A process according to claim 1, wherein the mixture of mullite crystals and silica is formed by heat-treating an aluminosilicate material having a SiO 2 .Al 2 O 3 molar ratio of at least 0.75:1 at a temperature greater than 1350° C.
Claim 5
Dependent Claim
20 words
A process according to claim 1, wherein said heat treatment by soak calcination is perfomed for at least 5 hours.
Claim 6
Dependent Claim
40 words
A process according to claim 1, wherein the particulate product of step (a) is prepared in the form of substantially cellular bodies, each of which is a substantially spherical hollow particle, by spray-drying an aqueous suspension of the aluminosilicate material.
Claim 7
Dependent Claim
50 words
A process according to claim 1, wherein the particulate product of step (a) is in the form of a substantially cellular body prepared by forming an aqueous suspension of the aluminosilicate material which is permitted to dry and set to a substantially rigid foam comprising a plurality of internal cavities.
Claim 8
Dependent Claim
32 words
A process according to claim 1, wherein the product prepared in step (a) comprises particles substantially all of which have a size in the range of from 10 microns to 100 microns.
Claim 9
Dependent Claim
22 words
A process according to claim 1, wherein in step (b) the alkali metal hydroxide solution has a molarity of at least 3M.
Claim 10
Dependent Claim
43 words
A process according to claim 1, wherein in step (b) the product of step (a) is treated with the alkali metal hydroxide solution at a temperature in the range of from 80° C. to the boiling point of the alkali metal hydroxide solution.
Claim 11
Dependent Claim
49 words
A process according to claim 1, wherein in step (c) the alkali-treated product of step (b) is washed first with an alkaline solution weaker than that used in step (b) and then repeatedly with water until the washing medium is substantially free of silicate ions and alkali metal ions.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-05-01 | 1992-10-31 | 1993-05-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-05-01 | 1996-10-31 | 1997-05-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-05-01 | 2000-10-31 | 2001-05-02 | $7700.00 | Window Closed / Lapsed |