Millimeter size single crystals of superconducting YBa2 Cu3 O.sub.
Assignee: Iowa State University Research Foundation Inc
•
Filing: 1987-09-10
•
Granted: 1989-04-25
•
Expires: 2007-09-10
Abstract
Abstract A method of growing large, up to 1 mm size single crystals of superconducting YBa 2 Cu 3 O x , wherein x equals from 6.5 to 7.2.
Inventors
- 👤 Michael A. Damento
- 👤 Karl A. Gschneidner, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 11:37
CPC Classifications
C; C30; C30B; C30B29/00; C30B29/10; C30B29/16; C30B29/22; C30B29/225; C30B9/00; H; H10; H10N; H10N60/00; H10N60/01; H10N60/0268
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
191 words
A method of growing superconductive crystals of YBa 2 Cu 3 O x wherein x equals from 6.5 to 7.2, comprising (a) subdividing of mixture of oxides of copper and yttrium, and carbonate of barium, said mixture containing an excess of copper oxide over the stoichiometric amount needed for formation of YBa 2 Cu 3 O x ; (b) heating the subdivided mixture until it forms a melt flux wherein the oxides and carbonates are melted; (c) cooling the melt flux at a rapid rate sufficient to prevent the melt flux from separating into phases, to room temperature; (d) reheating the mixture for a time and temperature sufficient to again form a melt flux; (e) holding the melt flux at temperatures above the melting point of said melt flux but below the melting point of crystals of YBa 2 Cu 3 O x to allow formation of millimeter size or larger crystals; and thereafter (f) slowly cooling the mixture to room temperature in an oxygen containing atmosphere at a rate to allow oxygen to enter said crystals sufficient to form said superconductive crystals of YBa 2 Cu 3 O x .
Claim 2
Independent Claim
191 words
A method of growing superconductive crystals of YBa 2 Cu 3 O x wherein x equals from 6.5 to 7.2, comprising (a) subdividing of mixture of oxides of copper and yttrium, and carbonate of barium, said mixture containing an excess of copper oxide over the stoichiometric amount needed for formation of YBa 2 Cu 3 O x ; (b) heating the subdivided mixture until it forms a melt flux wherein the oxides and carbonates are melted; (c) cooling the melt flux at a rapid rate sufficient to prevent the melt flux from separating into phases, to room temperature; (d) reheating the mixture for a time and temperature sufficient to again form a melt flux; (e) holding the melt flux at temperatures above the melting point of said melt flux but below the melting point of crystals of YBa 2 Cu 3 O x to allow formation of millimeter size or larger crystals; and thereafter (f) slowly cooling the mixture to room temperature in an oxygen containing atmosphere at a rate to allow oxygen to enter said crystals sufficient to form said superconductive crystals of YBa 2 Cu 3 O x .
Claim 3
Dependent Claim
15 words
The process of claim 1 wherein the crystals grown average about 1 mm in width.
Claim 4
Dependent Claim
21 words
The process of claim 1 wherein the amount of copper oxide is from about 1.2 to 3.0 times the stoichiometric amount.
Claim 5
Dependent Claim
22 words
The process of claim 3 wherein the amount of copper oxide is from about 1.2 to about 2.0 times the stoichiometric amount.
Claim 6
Dependent Claim
18 words
The process of claim 1 wherein the heating step (b) is to a temperature less than 1200° C.
Claim 7
Dependent Claim
15 words
The process of claim 5 wherein the heating step (b) is in a platinum crucible.
Claim 8
Dependent Claim
23 words
The process of claim 5 wherein the heating step (b) is at a temperature of from about 1150° C. to about 1200° C.
Claim 9
Dependent Claim
19 words
The process of claim 7 wherein the heating step (b) is for from about 0.5 to about 2.0 hours.
Claim 10
Dependent Claim
42 words
The process of claim 1 wherein in the rapid cooling of step (c) the melt is cooled to about 900° C. at about a 100° per minute, and then cooled to room temperature within from about 20 minutes to about 1.0 hours.
Claim 11
Dependent Claim
23 words
The process of claim 1 wherein reheating step (d) occurs to a temperature equaling at least the melting point of copper oxide flux.
Claim 12
Dependent Claim
21 words
The process of claim 1 wherein reheating is to a temperature within the range of from 900° C. to 950° C.
Claim 13
Dependent Claim
26 words
The process of claim 1 wherein the time for holding the melt flux to allow crystal formation is from about one day to about seven days.
Claim 14
Dependent Claim
19 words
The process of claim 1 wherein the slow cooling is for from about 1.0 hours to about 24.0 hours.
Claim 15
Dependent Claim
15 words
The process of claim 13 wherein the cooling was at about 1° C. per minute.
Claim 16
Independent Claim
201 words
A method of growing superconductive crystals of YBa 2 Cu 3 O x wherein x equals from 6.5 to 7.2, comprising: (a) subdividing of mixture of oxides of copper and yttrium, and carbonate of barium, said mixture containing an excess of copper oxide over the stoichiometric amount need for formation of YBa 2 Cu 3 O x ; (b) heating the subdivided mixture to no more than 1200° C. for two hours or less until it forms a melt flux wherein the oxides and carbonates are melted; (c) cooling the melt flux, at a rapid rate sufficient to prevent the melt from separating into phases to room temperature; (d) reheating the mixture for a time and temperature sufficient to again form a melt flux; (e) holding the melt flux at temperatures above the melting point of said melt flux but below the melting point of crystals of YBa 2 Cu 3 O x to allow formation of millimeter size or larger crystals; and thereafter (f) slowly cooling the mixture to room temperature in an oxygen containing atmosphere at a rate to allow oxygen to enter said crystals sufficient to form said superconductive crystals of YBa 2 Cu 3 O x .
Claim 17
Independent Claim
201 words
A method of growing superconductive crystals of YBa 2 Cu 3 O x wherein x equals from 6.5 to 7.2, comprising: (a) subdividing of mixture of oxides of copper and yttrium, and carbonate of barium, said mixture containing an excess of copper oxide over the stoichiometric amount need for formation of YBa 2 Cu 3 O x ; (b) heating the subdivided mixture to no more than 1200° C. for two hours or less until it forms a melt flux wherein the oxides and carbonates are melted; (c) cooling the melt flux, at a rapid rate sufficient to prevent the melt from separating into phases to room temperature; (d) reheating the mixture for a time and temperature sufficient to again form a melt flux; (e) holding the melt flux at temperatures above the melting point of said melt flux but below the melting point of crystals of YBa 2 Cu 3 O x to allow formation of millimeter size or larger crystals; and thereafter (f) slowly cooling the mixture to room temperature in an oxygen containing atmosphere at a rate to allow oxygen to enter said crystals sufficient to form said superconductive crystals of YBa 2 Cu 3 O x .
References Cited (Backward Citations)
US3458455A
Cited
US3896055A
Cited
US4049789A
Cited
DE2605585A1
Cited
US3983077A
Cited
US4086189A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-04-24 | 1992-10-24 | 1993-04-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-04-24 | 1996-10-24 | 1997-04-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-04-24 | 2000-10-24 | 2001-04-25 | $7700.00 | Window Closed / Lapsed |