US4822683A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method for preparing an adhesive bond with a curable composition having reduced shrinkage during cure
Assignee: PPG Industries Inc
•
Filing: 1987-11-06
•
Granted: 1989-04-18
•
Expires: 2007-11-06
Abstract
Abstract A method of forming an adhesive bond between two surfaces to form a bonded structure involves the steps I. applying to at least one of the surfaces a curable composition containing: (i) one or more epoxide group containing materials containing at least two epoxide groups per molecule; (ii) a positive amount of an effectively thermoplastic polyester, which does not react into the curable composition and is present as a blended ingredient, which does not exceed 40 percent by weight based on the total weight of the epoxide and polyester components of the composition, said polyester having a weight average molecular weight from about 1,000 to about 8,000, being nonreactive with the one or more epoxide group containing materials of (a) and being insoluble in the one or more epoxide group containing materials of (i); and (iii) a curing agent adapted to cure the epoxide group containing materials of (i); and II. at least partially curing the curable composition to form the bonded structure.
Inventors
- 👤 Raymond F. Schappert
- 👤 Robert M. Piccirilli
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 19:26
CPC Classifications
C; C08; C08G; C08G59/00; C08G59/18; C08G59/40; C08G59/50; C08L; C08L63/00; Y; Y10; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31511; Y10T428/31515
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
174 words
A method for preparing an adhesive bond between two surfaces to form a bonded structure which comprises: I. applying to at least one of the surfaces a curable composition comprising: (i) one or more epoxide group containing materials containing at least two epoxide groups per molecule; (ii) a positive amount of an effectively thermoplastic polyester, which does not react into the curable composition and is present as a blended ingredient, which does not exceed 40 percent by weight based on the total weight of the epoxide and polyester components of the composition, said polyester having a weight average molecular weight of from about 1,000 to about 8,000, being nonreactive with the one or more epoxide group containing materials of (a) and being insoluble in the one or more epoxide group containing materials of (i); and (iii) a curing agent adapted to cure the epoxide group containing the materials of (i); II. placing the surfaces in contact with the composition therebetween; and III. at least partially curing the curable composition to form the bonded structure.
Claim 2
Independent Claim
174 words
A method for preparing an adhesive bond between two surfaces to form a bonded structure which comprises: I. applying to at least one of the surfaces a curable composition comprising: (i) one or more epoxide group containing materials containing at least two epoxide groups per molecule; (ii) a positive amount of an effectively thermoplastic polyester, which does not react into the curable composition and is present as a blended ingredient, which does not exceed 40 percent by weight based on the total weight of the epoxide and polyester components of the composition, said polyester having a weight average molecular weight of from about 1,000 to about 8,000, being nonreactive with the one or more epoxide group containing materials of (a) and being insoluble in the one or more epoxide group containing materials of (i); and (iii) a curing agent adapted to cure the epoxide group containing the materials of (i); II. placing the surfaces in contact with the composition therebetween; and III. at least partially curing the curable composition to form the bonded structure.
Claim 3
Dependent Claim
10 words
A bonded structure prepared by the method of claim 1.
Claim 4
Dependent Claim
14 words
The method of claim 1 wherein the effectively thermoplastic polyester is a saturated polyester.
Claim 5
Dependent Claim
36 words
The method of claim 1 wherein the thermoplastic polyester contains no more than about 10 percent by weight of unsaturated units, the percentage based on the total weight of all of the ingredients of the polyester.
Claim 6
Dependent Claim
16 words
The method of claim 3 wherein the thermoplastic saturated polyester is substantially free of aromatic units.
Claim 7
Dependent Claim
36 words
The method of claim 5 wherein the saturated polyester contains no more than about 10 percent by weight of aromatic units, the percentage based on the total weight of all of the ingredients of the polyester.
Claim 8
Dependent Claim
23 words
The method of claim 1 wherein (i) is comprised of a single epoxide group containing material which is glycidyl ether of bisphenol A.
Claim 9
Dependent Claim
20 words
The method of claim 1 wherein (i) is comprised of a mixture of two or more epoxide group containing materials.
Claim 10
Dependent Claim
14 words
The method of claim 1 wherein the curing agent is an amine curing agent.
Claim 11
Dependent Claim
12 words
The method of claim 9 wherein the amine curing agent is dicyandiamide.
Claim 12
Dependent Claim
32 words
The method of claim 1 wherein the effectively thermoplastic polyester is present in the curable composition in an amount ranging from about 1 percent by weight to about 35 percent by weight.
Claim 13
Dependent Claim
41 words
The method of claim 1 wherein the curing agent is present in the curable composition in an amount ranging from about 1 percent by weight to about 50 percent by weight, the percentages based on the total weight of the composition.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-04-17 | 1992-10-17 | 1993-04-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-04-17 | 1996-10-17 | 1997-04-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-04-17 | 2000-10-17 | 2001-04-18 | $7700.00 | Window Closed / Lapsed |