Resin-fortified emulsion polymers and methods of preparing the same
Assignee: SC Johnson Commercial Markets Inc
•
Filing: 1988-06-09
•
Granted: 1989-04-11
•
Expires: 2008-06-09
Abstract
Abstract The stability and physical properties of high molecular weight emulsion polymers are improved by the addition of a low molecular weight support resin during the emulsion polymerization process. The resin is soluble or dispersible in water or alkali and has a number average molecular weight between 500 and 20,000.
Inventors
- 👤 Sheng-Liang Tsaur
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 16:49
CPC Classifications
C; C08; C08F; C08F2/00; C08F2/12; C08F2/16; C08F2/22
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
203 words
A method of preparing a resin-fortified polymer emulsion having Newtonian-like flow characteristics, the method comprising: (a) emulsion-polymerizing a first monomer charge comprising at least one emulsion-polymerizable monomer in the presence of a surfactant and an initiator under emulsion-polymerization reaction conditions effective for initiating emulsion polymerization of the emulsion-polymerizable monomer, for producing an emulsion-polymerization mixture which includes an emulsion polymer product, the surfactant being present in an amount effective for preventing coagulation of emulsion polymer particles which are forming in the emulsion-polymerization mixture; and thereafter (b) adding to the emulsion-polymerization mixture, while emulsion polymerization of the emulsion-polymerizable monomer is occurring, an effective amount of at least one support resin for controllably affecting the physical characteristics of the emulsion polymer product, said resin being selected from the group consisting of water soluble resins, water dispersible resins, alkali soluble resins, alkali dispersible resins and mixtures thereof, said resin having been produced either by a solution-polymerization method or by a bulk-polymerization method, wherein the resin is produced from at least one ethylenically-unsaturated monomer selected from the group consisting of olefins, mono vinylidene aromatics, alpha beta ethylenically-unsaturated carboxylic acids and esters thereof, ethylenically-unsaturated dicarboxylic anhydrides, and mixtures thereof, for producing a resin-fortified polymer emulsion having Newtonian-like flow characteristics.
Claim 2
Independent Claim
203 words
A method of preparing a resin-fortified polymer emulsion having Newtonian-like flow characteristics, the method comprising: (a) emulsion-polymerizing a first monomer charge comprising at least one emulsion-polymerizable monomer in the presence of a surfactant and an initiator under emulsion-polymerization reaction conditions effective for initiating emulsion polymerization of the emulsion-polymerizable monomer, for producing an emulsion-polymerization mixture which includes an emulsion polymer product, the surfactant being present in an amount effective for preventing coagulation of emulsion polymer particles which are forming in the emulsion-polymerization mixture; and thereafter (b) adding to the emulsion-polymerization mixture, while emulsion polymerization of the emulsion-polymerizable monomer is occurring, an effective amount of at least one support resin for controllably affecting the physical characteristics of the emulsion polymer product, said resin being selected from the group consisting of water soluble resins, water dispersible resins, alkali soluble resins, alkali dispersible resins and mixtures thereof, said resin having been produced either by a solution-polymerization method or by a bulk-polymerization method, wherein the resin is produced from at least one ethylenically-unsaturated monomer selected from the group consisting of olefins, mono vinylidene aromatics, alpha beta ethylenically-unsaturated carboxylic acids and esters thereof, ethylenically-unsaturated dicarboxylic anhydrides, and mixtures thereof, for producing a resin-fortified polymer emulsion having Newtonian-like flow characteristics.
Claim 3
Dependent Claim
21 words
The method of claim 1 wherein the resin has a number average molecular weight of from about 500 to about 20,000.
Claim 4
Dependent Claim
29 words
The method of claim 2 which includes the additional step of: (c) adding a second monomer charge comprising at least one monomer simultaneously with addition of the support resin.
Claim 5
Dependent Claim
21 words
The method of claim 3 wherein the resin has a number average molecular weight of from about 500 to about 20,000.
Claim 6
Dependent Claim
17 words
The method of claim 1 wherein the first monomer charge includes at least one ethylenically unsaturated monomer.
Claim 7
Dependent Claim
42 words
The method of claim 5 wherein said ethylenically unsaturated monomer is selected from the group consisting of olefins, monovinylidene aromatics, alpha, beta-ethylenically unsaturated carboxylic acids, esters of alpha, beta-ethylenically unsaturated carboxylic acid, ethylenically unsaturated dicarboxylic anhydrides, halo substituted olefins, and mixtures thereof.
Claim 8
Dependent Claim
20 words
The method of claim 1 wherein the polymerization is conducted at a temperature of from about 60° to 100° C.
Claim 9
Dependent Claim
22 words
The method of claim 3 wherein the monomers of the first monomer charge and the second monomer charge are ethylenically unsaturated monomers.
Claim 10
Dependent Claim
42 words
The method of claim 8 wherein said ethylenically unsaturated monomers are selected from the group consisting of olefins, monovinylidene aromatics, alpha, beta-ethylenically unsaturated carboxylic acids, esters of alpha, beta-ethylenically unsaturated carboxylic acid, ethylenically unsaturated dicarboxylic anhydrides, halo substituted olefins, and mixtures thereof.
Claim 11
Dependent Claim
20 words
The method of claim 3 wherein the polymerization is conducted at a temperature of from about 60° to 100° C.
Claim 12
Dependent Claim
40 words
The method of claim 1 which includes the additional step of: (c) thereafter adding a second monomer charge comprising at least one additional monomer to the polymerization mixture (a) and (b) above under conditions to emulsion polymerize said additional monomer.
Claim 13
Dependent Claim
22 words
The method of claim 11 wherein the monomers of the first monomer charge and the second monomer charge are ethylenically unsaturated monomers.
Claim 14
Dependent Claim
42 words
The method of claim 12 wherein said ethylenically unsaturated monomers are selected from the group consisting of olefins, monovinylidene aromatics, alpha, bets-ethylenically unsaturated carboxylic acids, esters of alpha, beta-ethylenically unsaturated carboxylic acid, ethylenically unsaturated dicarboxylic anhydrides, halo substituted olefins, and mixtures thereof.
Claim 15
Dependent Claim
20 words
The method of claim 11 wherein the polymerization is conducted at a temperature of from about 60° to 100° C.
References Cited (Backward Citations)
CA814528A
Cited
US2848434A
Cited
US3244655A
Cited
US3666704A
Cited
US3882057A
Cited
US4009138A
Cited
US4179417A
Cited
US4151143A
Cited
US4226752A
Cited
US4414370A
Cited
US4426482A
Cited
US4530956A
Cited
US4529787A
Cited
US4529787B1
Cited
US4539361A
Cited
US4546160A
Cited
US4668730A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-04-10 | 1992-10-10 | 1993-04-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-04-10 | 1996-10-10 | 1997-04-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-04-10 | 2000-10-10 | 2001-04-11 | $7700.00 | Window Closed / Lapsed |