Fixing roller and its manufacturing process
Assignee: Minolta Co Ltd
•
Filing: 1987-05-22
•
Granted: 1989-04-04
•
Expires: 2007-05-22
Abstract
Abstract A fixing roller of the present invention comprising at least an electrically conductive core member and a PFA dispersion layer formed from a polytetrafluoro ethylene perfluoro alkoxy ethylene co-polymer (PFA resin) with carbon black or like conductive material dispersed therein by means of a dispersing agent. A roller of this construction effectively prevents triboelectrically-induced offset caused by the electrostatic attraction of the toner by a surface charge on the outer peripheral surface of the roller. Since the release properties of said roller are superior, offset caused by thermal adhesion of the toner to the roller is also effectively prevented.
Inventors
- 👤 Moriyoshi Matsushiro
- 👤 Etsuaki Urano
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 13:50
CPC Classifications
G; G03; G03G; G03G15/00; G03G15/20; G03G15/2003; G03G15/2014; G03G15/2053; G03G15/2057
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
90 words
A fixing roller for use in a copying apparatus comprising: an electrically conductive core member; a primer layer formed on said electrically conductive core member and comprising a primer having incorporated therein an electrically conductive material; a dispersion layer formed on said primer layer by dispersing a polytetrafluoroethylene perfluoro alkoxy ethylene co-polymer (PFA resin) with a conductive material in a dispersing agent; and a powdery resin layer having release properties and formed on said dispersion layer with said conductive material exposed at the outer surface of said powdery resin layer.
Claim 2
Dependent Claim
90 words
A fixing roller for use in a copying apparatus comprising: an electrically conductive core member; a primer layer formed on said electrically conductive core member and comprising a primer having incorporated therein an electrically conductive material; a dispersion layer formed on said primer layer by dispersing a polytetrafluoroethylene perfluoro alkoxy ethylene co-polymer (PFA resin) with a conductive material in a dispersing agent; and a powdery resin layer having release properties and formed on said dispersion layer with said conductive material exposed at the outer surface of said powdery resin layer.
Claim 3
Dependent Claim
20 words
A fixing roller as claimed in claim 1, wherein said conductive material incorporated in said dispersion layer is carbon black.
Claim 4
Dependent Claim
26 words
A fixing roller as claimed in claim 2, wherein said carbon black is preferably incorporated in said dispersion layer in an amount of less than 9%.
Claim 5
Dependent Claim
166 words
A process for preparing a fixing roller which comprises an electrically conductive core member and a resin layer having release properties and is used in a copying apparatus, said process comprising: a first step of heating said core member to a predetermined temperature for a predetermined time; a second step of coating a primer layer on said electrically conductive core member, said primer layer comprising a primer having therein an electrically conductive material; a third step of coating a dispersion layer on said primer layer, said dispersion layer being formed by dispersing a polytetrafluoro ethylene perfluoro alkoxy ethylene co-polymer (PFA resin) with a conductive material in a dispersing agent; a fourth step of coating a powdery resin layer having release properties on said dispersion layer; a fifth step of drying and sintering said powdery resin layer; and a sixth step of grinding said powdery resin layer after said fifth step so as to expose said conductive material at the outer surface of said powdery resin layer.
Claim 6
Dependent Claim
166 words
A process for preparing a fixing roller which comprises an electrically conductive core member and a resin layer having release properties and is used in a copying apparatus, said process comprising: a first step of heating said core member to a predetermined temperature for a predetermined time; a second step of coating a primer layer on said electrically conductive core member, said primer layer comprising a primer having therein an electrically conductive material; a third step of coating a dispersion layer on said primer layer, said dispersion layer being formed by dispersing a polytetrafluoro ethylene perfluoro alkoxy ethylene co-polymer (PFA resin) with a conductive material in a dispersing agent; a fourth step of coating a powdery resin layer having release properties on said dispersion layer; a fifth step of drying and sintering said powdery resin layer; and a sixth step of grinding said powdery resin layer after said fifth step so as to expose said conductive material at the outer surface of said powdery resin layer.
Claim 7
Dependent Claim
19 words
A process as claimed in claim 4, wherein said conductive material incorporated in said dispersion layer is carbon black.
Claim 8
Dependent Claim
102 words
A fixing roller for use in a copying apparatus comprising: an electrically conductive core member; a primer layer formed on said electrically conductive core member and comprising a primer having incorporated therein an electrically conductive material; and a resin separation layer formed on said primer layer and comprising a conductive material, said resin layer being comprised of a dispersion layer formed by dispersing a polytetrafluoroethylene perfluoro alkoxy ethylene copolymer (PFA resin) and a powdery resin layer having release properties and formed on said dispersion layer, said conductive material content in the powdery resin layer being less than that of the dispersion layer.
Claim 9
Dependent Claim
102 words
A fixing roller for use in a copying apparatus comprising: an electrically conductive core member; a primer layer formed on said electrically conductive core member and comprising a primer having incorporated therein an electrically conductive material; and a resin separation layer formed on said primer layer and comprising a conductive material, said resin layer being comprised of a dispersion layer formed by dispersing a polytetrafluoroethylene perfluoro alkoxy ethylene copolymer (PFA resin) and a powdery resin layer having release properties and formed on said dispersion layer, said conductive material content in the powdery resin layer being less than that of the dispersion layer.
Claim 10
Dependent Claim
21 words
A fixing roller as claimed in claim 6, wherein said conductive material incorporated in said resin separation layer is carbon black.
References Cited (Backward Citations)
US3776760A
Cited
US3940518A
Cited
US4199626A
Cited
US4179601A
Cited
JPS54109845A
Cited
US4257699A
Cited
JPS56133770A
Cited
US4503179A
Cited
JPS582864A
Cited
JPS585770A
Cited
US4434355A
Cited
US4568275A
Cited
JPS58214180A
Cited
US4550243A
Cited
US4596920A
Cited
EP0186314A2
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-04-03 | 1992-10-03 | 1993-04-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-04-03 | 1996-10-03 | 1997-04-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-04-03 | 2000-10-03 | 2001-04-04 | $7700.00 | Window Closed / Lapsed |