Tetragonal system tunnel-structured compound AX(GA8MYGA(8+X)-YTI16-X0 56), and cation conductor and heat insulating material composed thereof
Assignee: National Institute for Materials Science
•
Filing: 1987-02-11
•
Granted: 1989-04-04
•
Expires: 2007-02-11
Abstract
Abstract A tetragonal system tunnel-structured compound having the formula: A.sub.x [Ga.sub.8 M.sub.y Ga.sub.(8+x)-y Ti.sub.16-x O.sub.56 ](I) wherein A is at least one alkali metal selected from the group consisting of K, Rb and Cs, or a solid solution of such alkali metal with lithium, sodium or barium, M is at least one trivalent metal selected from the group consisting of Al, Fe and Cr, x is a number of from 0.1 to 2.0, and y is a number of from 0 to 10.
Inventors
- 👤 Yoshinori Fujiki
- 👤 Mamoru Watanabe
- 👤 Takayoshi Sasaki
- 👤 Yoshito Onoda
- 👤 Tadashi Ohachi
- 👤 Takefumi Mitsuhashi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 22:13
CPC Classifications
C; C30; C30B; C30B9/00; C04; C04B; C04B35/00; C04B35/01; C04B35/46; C04B35/462; C30B29/00; C30B29/10; C30B29/16; C30B29/22; C30B29/32; C30B29/60; C30B29/62
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
81 words
A tetragonal system tunnel-structured compound having the formula: A.sub.x[Ga.sub.8 M.sub.y Ga.sub.(8+x)-y Ti.sub.16-x O.sub.56 ](I) wherein A is at least one alkali metal selected from the group consisting of K, Rb and Cs, or a solid solution of such alkali metal with lithium, sodium or barium, M is at least one trivalent metal selected from the group consisting of Al, Fe and Cr, x is a number of from 0.1 to 2.0, and y is a number of from 0 to 10.
Claim 2
Dependent Claim
81 words
A tetragonal system tunnel-structured compound having the formula: A.sub.x[Ga.sub.8 M.sub.y Ga.sub.(8+x)-y Ti.sub.16-x O.sub.56 ](I) wherein A is at least one alkali metal selected from the group consisting of K, Rb and Cs, or a solid solution of such alkali metal with lithium, sodium or barium, M is at least one trivalent metal selected from the group consisting of Al, Fe and Cr, x is a number of from 0.1 to 2.0, and y is a number of from 0 to 10.
Claim 3
Dependent Claim
24 words
The compound according to claim 1, which has the A.sub.x [Ga.sub.8 Ga.sub.8+x Ti.sub.16-x O.sub.56] wherein A and x are as defined in claim 1.
Claim 4
Dependent Claim
16 words
The compound according to claim 2, wherein up to 50% of Ti is substituted by Mn.
Claim 5
Independent Claim
209 words
A method for preparing a tetragonal system tunnel-structured compound having the formula: A.sub.x[Ga.sub.8 M.sub.y Ga.sub.(8+x)-y Ti.sub.16-x O.sub.56 ](I) wherein A is at least one alkali metal selected from the group consisting of K, Rb and Cs, or a solid solution of such alkali metal with lithium, sodium or barium, M is at least one trivalent metal selected from the group consisting of Al, Fe and Cr, x is a number of from 0.1 to 2.0, and y is a number of from 0 to 10, which comprises mixing an alkali metal oxide selected from the group consisting of K 2 O, Rb 2 O and Cs 2 O or a compound decomposable into such an alkali metal oxide when heated, titanium oxide or a compound decomposable into titanium oxide when heated, gallium oxide or a compound decomposable into gallium oxide when heated, and a trivalent metal compound selected from the group consisting of aluminum oxide, iron oxide and chromium oxide, or a compound decomposable into such a trivalent metal oxide when heated, to have a composition represented by the formula: A.sub.x [Ga.sub.8 M.sub.y Ga.sub.(8+x)-y Ti.sub.16-x O.sub.56 ] wherein A, M, x and y are as defined above, and sintering the mixture at a temperature of at least 1000° C.
Claim 6
Independent Claim
209 words
A method for preparing a tetragonal system tunnel-structured compound having the formula: A.sub.x[Ga.sub.8 M.sub.y Ga.sub.(8+x)-y Ti.sub.16-x O.sub.56 ](I) wherein A is at least one alkali metal selected from the group consisting of K, Rb and Cs, or a solid solution of such alkali metal with lithium, sodium or barium, M is at least one trivalent metal selected from the group consisting of Al, Fe and Cr, x is a number of from 0.1 to 2.0, and y is a number of from 0 to 10, which comprises mixing an alkali metal oxide selected from the group consisting of K 2 O, Rb 2 O and Cs 2 O or a compound decomposable into such an alkali metal oxide when heated, titanium oxide or a compound decomposable into titanium oxide when heated, gallium oxide or a compound decomposable into gallium oxide when heated, and a trivalent metal compound selected from the group consisting of aluminum oxide, iron oxide and chromium oxide, or a compound decomposable into such a trivalent metal oxide when heated, to have a composition represented by the formula: A.sub.x [Ga.sub.8 M.sub.y Ga.sub.(8+x)-y Ti.sub.16-x O.sub.56 ] wherein A, M, x and y are as defined above, and sintering the mixture at a temperature of at least 1000° C.
Claim 7
Independent Claim
371 words
A method for preparing a tetragonal system tunnel-structured compound having the formula: A.sub.x [Ga.sub.8 M.sub.y Ga.sub.(8+x)-y Ti.sub.16-x O.sub.56 ](I) wherein A is at least one alkali metal selected from the group consisting of K, Rb and Cs, or a solid solution of such alkali metal with lithium, sodium or barium, M is at least one trivalent metal selected from the group consisting of Al, Fe and Cr, x is a number of from 0.1 to 2.0, and y is a number of from 0 to 10, which comprises mixing an alkali metal oxide selected from the group consisting of K 2 O, Rb 2 O and Cs 2 O, or a compound decomposable into such an alkali metal oxide when heated, TiO 2 or a compound decomposable into TiO 2 when heated, Ga 2 O 3 or a compound decomposable into Ga 2 O 3 when heated, and a trivalent metal oxide selected from the group consisting of Al 2 O 3 , Fe 2 O 3 and Cr 2 O 3 , or a compound decomposable into such a trivalent metal oxide when heated, to obtain a crystal material having a composition represented by the formula: (A.sub.2 O).sub.a (TiO.sub.2).sub.b (M.sub.2 O.sub.3).sub.c (Ga.sub.2 O.sub.3).sub.d wherein A and M are as defined above, each of a and b is a number of from 0.1 to 2.0, c is a number of from 0 to 1.0, and d is a number of from 0.1 to 1.0, mixing MoO 3 or a compound decomposable into MoO 3 when heated, and an alkali metal oxide selected from the group consisting of K 2 O, Rb 2 O and Cs 2 O, or a compound decomposable into such an alkali metal oxide when heated, to obtain a flux material having a composition represented by the formula: A.sub.2 O.n(MoO.sub.3) wherein A is as defined above, and n is a number of from 1 to 2, then mixing the crystal material and the flux material in a molar ratio of from 30:70 to 10:90, heating and melting the mixture at a temperature of from 1200° to 1400° C., and gradually cooling the melt to a temperature of from 900° to 1000° C. to let a single crystal grow.
Claim 8
Independent Claim
371 words
A method for preparing a tetragonal system tunnel-structured compound having the formula: A.sub.x [Ga.sub.8 M.sub.y Ga.sub.(8+x)-y Ti.sub.16-x O.sub.56 ](I) wherein A is at least one alkali metal selected from the group consisting of K, Rb and Cs, or a solid solution of such alkali metal with lithium, sodium or barium, M is at least one trivalent metal selected from the group consisting of Al, Fe and Cr, x is a number of from 0.1 to 2.0, and y is a number of from 0 to 10, which comprises mixing an alkali metal oxide selected from the group consisting of K 2 O, Rb 2 O and Cs 2 O, or a compound decomposable into such an alkali metal oxide when heated, TiO 2 or a compound decomposable into TiO 2 when heated, Ga 2 O 3 or a compound decomposable into Ga 2 O 3 when heated, and a trivalent metal oxide selected from the group consisting of Al 2 O 3 , Fe 2 O 3 and Cr 2 O 3 , or a compound decomposable into such a trivalent metal oxide when heated, to obtain a crystal material having a composition represented by the formula: (A.sub.2 O).sub.a (TiO.sub.2).sub.b (M.sub.2 O.sub.3).sub.c (Ga.sub.2 O.sub.3).sub.d wherein A and M are as defined above, each of a and b is a number of from 0.1 to 2.0, c is a number of from 0 to 1.0, and d is a number of from 0.1 to 1.0, mixing MoO 3 or a compound decomposable into MoO 3 when heated, and an alkali metal oxide selected from the group consisting of K 2 O, Rb 2 O and Cs 2 O, or a compound decomposable into such an alkali metal oxide when heated, to obtain a flux material having a composition represented by the formula: A.sub.2 O.n(MoO.sub.3) wherein A is as defined above, and n is a number of from 1 to 2, then mixing the crystal material and the flux material in a molar ratio of from 30:70 to 10:90, heating and melting the mixture at a temperature of from 1200° to 1400° C., and gradually cooling the melt to a temperature of from 900° to 1000° C. to let a single crystal grow.
Claim 9
Dependent Claim
14 words
A cation conductor material consisting essentially of the compound as defined in claim 1.
Claim 10
Dependent Claim
16 words
A heat resistant heat insulating material consisting essentially of the compound as defined in claim 1.
Claim 11
Dependent Claim
43 words
The method according to claim 4, wherein said compound decomposable into said alkali metal oxide, gallium oxide, titanium oxide or said trivalent metal oxide when heated is selected from the group consisting of the respective metal carbonates, percarbonates, hydroxides, nitrates, halides and oxyhalides.
Claim 12
Dependent Claim
43 words
The method according to claim 5, wherein said compound decomposable into said alkali metal oxide, gallium oxide, titanium oxide or said trivalent metal oxide when heated is selected from the group consisting of the respective metal carbonates, percarbonates, hydroxides, nitrates, halides and oxyhalides.
Claim 13
Dependent Claim
16 words
The tetragonal system tunnel-structured compound according to claim 1, wherein x is from 0.6 to 1.2.
Claim 14
Dependent Claim
28 words
The tetragonal system tunnel-structured compound according to claim 1, wherein said alkali metal is K, Rb or a solid solution of K or Rb with Li or Na.
Claim 15
Dependent Claim
28 words
The cation conductor material according to claim 6, which is in a crystalline form having a face perpendicular to the axis of the tunnel structure which is well-developed.
Claim 16
Dependent Claim
25 words
The cation conductor material according to claim 12, which is a needle-shaped or fiber-shaped single crystal extending in parallel with the c-axis of the crystal.
Claim 17
Dependent Claim
16 words
The heat resistant heat insulating material according to claim 7, which is in a crystalline form.
References Cited (Backward Citations)
US4034144A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-04-03 | 1992-10-03 | 1993-04-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-04-03 | 1996-10-03 | 1997-04-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-04-03 | 2000-10-03 | 2001-04-04 | $7700.00 | Window Closed / Lapsed |