Biaxially drawn polyester vessel having resistance to heat distortion and gas barrier properties and process for preparation thereof
Assignee: Toyo Seikan Group Holdings Ltd
•
Filing: 1987-03-02
•
Granted: 1989-04-04
•
Expires: 2007-03-02
Abstract
Abstract The present invention is based on the finding that when a multi-layer blow-formed body is heat-treated, cooled and taken out, an intermediate layer of a gas-barrier resin in the multi-layer blow-formed body acts as a heat-insulating layer and if the blow-formed body is cooled from the interior by a cooling fluid, a shape-retaining property necessary for taking out the blow-formed body from the mold can be promptly obtained. A biaxially drawn polyester vessel excellent in the resistance to thermal contraction and gas-barrier properties can be prepared at a high manufacturing speed with a reduced number of steps by preheating or temeprature-adjusting a multi-layer preform comprising inner and outer layers of a polyester composed mainly of ethylene terephthalate units and at least one intermediate layer composed of a gas-barrier resin to a temperature suitable for drawing, carrying out the biaxial draw-blow forming of the preform and the heat treatment of the blow-formed body in a mold maintained at a heat-setting temperature, changing over a compressed fluid for the blow-forming to a fluid for internal cooling, cooling the blow-formed body to a temperature at which deformation is not caused when the blow-formed body is taken out from the mold, while contacting the blow-formed body with the surface of the mold cavity, and taking out the formed body from the mold.
Inventors
- 👤 Shunsaku Hirata
- 👤 Shigezo Nohara
- 👤 Sadao Hirata
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 09:14
CPC Classifications
B; B32; B32B; B32B27/00; B32B27/06; B32B27/08; B29; B29C; B29C49/00; B29C49/22; B29C49/42; B29C49/64; B29C49/6472; B29C49/66; B32B1/00; B32B27/36; B65; B65D; B65D1/00; B65D1/02; B65D1/0207; B65D1/0215; B29C2949/00; B29C2949/07; B29C2949/0715; B29C2949/20; B29C2949/22; B29C2949/24; B29C2949/26; B29C2949/28; B29C2949/30; B29C2949/3008; B29C2949/3012; B29C2949/3016; B29C2949/302; B29C2949/3024; B29C2949/3026; B29C2949/3028; B29C2949/303; B29C2949/3032; B29C2949/3034; B29C2949/3036; B29C2949/3038; B29C2949/3041; B29C2949/3042; B29C2949/3044; B29C2949/3046; B29C2949/3086; B29C2949/3088; B29C2949/3092; B29C49/02; B29C49/06; B29C49/4273; B29C49/4283; B29C49/42832; B29C49/6604; B29C49/6605; B29K; B29K2067/00; B29K2077/00; B29K2995/00; B29K2995/0012; B29K2995/0017; B29K2995/0037; B29K2995/0041; B29K2995/0043; B29K2995/0065; B29K2995/0067; B29K2995/0068; B29K2995/0069; B32B2307/00; B32B2307/50; B32B2307/514; B32B2307/518; B32B2307/70; B32B2307/724; B32B2307/7242; B32B2367/00; B32B2439/00; B32B2439/40; B32B2439/60; Y; Y10; Y10T; Y10T428/00; Y10T428/13; Y10T428/1352; Y10T428/1379; Y10T428/1383
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
254 words
A biaxially drawn polyester vessel having good resistance to heat distortion and gas-barrier properties, which is prepared by biaxially draw-blow forming of a preform comprising inner and outer layers of a polyester composed mainly of ethylene terephthalate units and at least one intermediate layer composed of a gas-barrier resin with the temperature conductivity of the gas-barrier resin being 1/2 to 1/3 the temperature conductivity of the polyester, wherein the barrel of the vessel has pillar convexities having a relatively large diameter and a short circumference and panel-like concavities having a relatively small diameter and a long circumference, which are alternately arranged in the circumferential direction of the barrel where the circumferential size of the panel-like concavities is 10 to 50 mm, the axial size of the panel-like concavities is 40 to 160 mm and the step between the panel-like concavities and the pillar convexities is 1 to 8 mm, the panel-like concavities having a function of expanding and contracting in the diameter direction of the barrel according to the change of the pressure in the vessel, the inner and outer layers in the panel portion are biaxially and molecularly oriented so that the in-plane orientation degree (l+m) is at least 0.350, and the inner and outer layers in the panel portion are heat-set so that the crystallization degree, determined by the density method, of the outer layer in the panel portion is at least 30% and is higher by at least 2% than the crystallization degree of the inner layer in the panel portion.
Claim 2
Dependent Claim
254 words
A biaxially drawn polyester vessel having good resistance to heat distortion and gas-barrier properties, which is prepared by biaxially draw-blow forming of a preform comprising inner and outer layers of a polyester composed mainly of ethylene terephthalate units and at least one intermediate layer composed of a gas-barrier resin with the temperature conductivity of the gas-barrier resin being 1/2 to 1/3 the temperature conductivity of the polyester, wherein the barrel of the vessel has pillar convexities having a relatively large diameter and a short circumference and panel-like concavities having a relatively small diameter and a long circumference, which are alternately arranged in the circumferential direction of the barrel where the circumferential size of the panel-like concavities is 10 to 50 mm, the axial size of the panel-like concavities is 40 to 160 mm and the step between the panel-like concavities and the pillar convexities is 1 to 8 mm, the panel-like concavities having a function of expanding and contracting in the diameter direction of the barrel according to the change of the pressure in the vessel, the inner and outer layers in the panel portion are biaxially and molecularly oriented so that the in-plane orientation degree (l+m) is at least 0.350, and the inner and outer layers in the panel portion are heat-set so that the crystallization degree, determined by the density method, of the outer layer in the panel portion is at least 30% and is higher by at least 2% than the crystallization degree of the inner layer in the panel portion.
Claim 3
Dependent Claim
37 words
The biaxially drawn polyester vessel according to claim 1, wherein said polyester is polyethylene terephthalate or a copolyester comprising ethylene terephthalate units as main units and a small amount of units copolymerizable with said ethylene terephthalate units.
Claim 4
Dependent Claim
23 words
The biaxially drawn polyester vessel according to claim 1, wherein the biaxially draw-blow forming is at a temperature of 120° to 230° C.
Claim 5
Dependent Claim
35 words
The biaxially drawn polyester vessel according to claim 1, wherein the crystallization degree of the outer layer is higher by at least 3% than the crystallization degree of the inner layer in the panel portion.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-04-03 | 1992-10-03 | 1993-04-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-04-03 | 1996-10-03 | 1997-04-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-04-03 | 2000-10-03 | 2001-04-04 | $7700.00 | Window Closed / Lapsed |