Process for restricted lead content soldering of copper with controlled copper contamination of the molten solder reservoir
Assignee: Siemens Energy Inc
•
Filing: 1987-06-15
•
Granted: 1989-04-04
•
Expires: 2007-06-15
Abstract
Abstract This is a process which provides the first essentially continuous high tin flow soldering method for attaching copper-based fins to non-copper-based tubing. This invention avoids sludge buildup in the reservoir and generally avoids lead carbonate formation when the heat produced having a braze-like joint with eta phase layers exchanger is in service. In addition, a novel structure is adjacent to copper-containing surfaces. The invention utilizes an essentially lead-free, high tin solder cascade onto a preferably cool tube, genrally with a limited time of contact between the liquid solder and the tube, and with a combination air quench and wipe to remove excess solder and solidify the remaining solder. Thus a braze-like joint is achieved having better heat conduction and closer thermal expansion match. This finned heat exchanger tubing is generally useful for liquid to gas-type heat exchangers.
Inventors
- 👤 Homer G. Hargrove
- 👤 Jay L. Kratz
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 14:51
CPC Classifications
B; B23; B23K; B23K1/00; B23K1/08; B23K1/085; B23K1/0008; B23K1/0012; B23K35/00; B23K35/22; B23K35/24; B23K35/26; B23K35/262
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
141 words
An improved method for continuous metal fusion bonding of copper-based fin to non-copper-based heat exchanger tubing, said improved method comprising a. assembling said fin to said tubing; b. applying flux to said fin-tubing assembly; c. controlling the temperature of an essentially lead-free, high tin solder reservoir; d. flowing solder from said reservoir on said fin tubing assembly; e. returning excess solder to the reservoir; and f. wiping each portion of said soldered finned tubing with an air quench in less than 15 seconds from the time that solder was flowed on that portion and return the excess solder wiped from said finned tubing to said reservoir, whereby the solder is rapidly solidified and essentially all of the high temperature melting copper-tin alloy which is formed is retained adjacent to the fin surfaces thus avoiding copper-tin alloy sludge formation in the reservoir.
Claim 2
Dependent Claim
141 words
An improved method for continuous metal fusion bonding of copper-based fin to non-copper-based heat exchanger tubing, said improved method comprising a. assembling said fin to said tubing; b. applying flux to said fin-tubing assembly; c. controlling the temperature of an essentially lead-free, high tin solder reservoir; d. flowing solder from said reservoir on said fin tubing assembly; e. returning excess solder to the reservoir; and f. wiping each portion of said soldered finned tubing with an air quench in less than 15 seconds from the time that solder was flowed on that portion and return the excess solder wiped from said finned tubing to said reservoir, whereby the solder is rapidly solidified and essentially all of the high temperature melting copper-tin alloy which is formed is retained adjacent to the fin surfaces thus avoiding copper-tin alloy sludge formation in the reservoir.
Claim 3
Dependent Claim
19 words
The process of claim 1, wherein said flux is water soluble, and is essentially free of ammonia and chloride.
Claim 4
Dependent Claim
40 words
The process of claim 1, wherein said solder is a tin-antimony solder which contains less than about 2.2% copper and the temperature of the reservoir is controlled to less than about 150° F. above the liquidus point of the solder.
Claim 5
Dependent Claim
19 words
The process of claim 3, wherein said solder contains 5.0-6.0% antimony, 1.8-2.2% copper and less than about 0.22% lead.
Claim 6
Dependent Claim
20 words
The process of claim 4, wherein essentially 95 tin, 5 antimony solder is at least periodically added to said reservoir.
Claim 7
Dependent Claim
18 words
The process of claim 4, wherein said solder reservoir is maintained at a temperature of about 560°-570° F.
Claim 8
Dependent Claim
25 words
The process of claim 1 wherein said solder is flowed on a given portion of said fin tubing assembly for less than about 10 seconds.
Claim 9
Independent Claim
219 words
A method for continuous metal fusion bonding of copper-based fin to non-copper-based heat exchanger tubing without solder reservoir reprocessing, said method comprising: a. assembling said fin to said tubing; b. applying a flux which is water soluble, and is essentially free of ammonia and chloride to said fin-tubing assembly; c. controlling a solder reservoir containing solder consisting essentially of 5.0-6.0% antimony, less than about 2.2% copper, less than about 0.22% lead, and a balance of tin to a temperature of 560°-570° F; d. flowing said solder from said reservoir on said fin-tubing assembly, limiting the time said solder is flowed on a given portion of said fin-tubing assembly to less than about 10 seconds, and without preheating said fin-tubing assembly; e. capturing excess solder and returning said excess solder to said reservoir; f wiping said fin-tubing assembly with an air quench of non-preheated air and return the excess solder wiped from said finned tubing to said reservoir, limiting the time between soldering and wiping to less than 5 seconds, whereby said solder is rapidly solidified and essentially all of the high temperature melting copper-tin alloy which is formed is retained adjacent to the fin surfaces thus avoiding copper-tin alloy sludge formation in said reservoir; and g. at least periodically adding essentially 95 tin, 5 antimony solder to said reservoir.
Claim 10
Independent Claim
219 words
A method for continuous metal fusion bonding of copper-based fin to non-copper-based heat exchanger tubing without solder reservoir reprocessing, said method comprising: a. assembling said fin to said tubing; b. applying a flux which is water soluble, and is essentially free of ammonia and chloride to said fin-tubing assembly; c. controlling a solder reservoir containing solder consisting essentially of 5.0-6.0% antimony, less than about 2.2% copper, less than about 0.22% lead, and a balance of tin to a temperature of 560°-570° F; d. flowing said solder from said reservoir on said fin-tubing assembly, limiting the time said solder is flowed on a given portion of said fin-tubing assembly to less than about 10 seconds, and without preheating said fin-tubing assembly; e. capturing excess solder and returning said excess solder to said reservoir; f wiping said fin-tubing assembly with an air quench of non-preheated air and return the excess solder wiped from said finned tubing to said reservoir, limiting the time between soldering and wiping to less than 5 seconds, whereby said solder is rapidly solidified and essentially all of the high temperature melting copper-tin alloy which is formed is retained adjacent to the fin surfaces thus avoiding copper-tin alloy sludge formation in said reservoir; and g. at least periodically adding essentially 95 tin, 5 antimony solder to said reservoir.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-04-03 | 1992-10-03 | 1993-04-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-04-03 | 1996-10-03 | 1997-04-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-04-03 | 2000-10-03 | 2001-04-04 | $7700.00 | Window Closed / Lapsed |