US4814264A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Silver halide photographic material and method for preparation thereof
Assignee: Fujifilm Holdings Corp
•
Filing: 1987-12-17
•
Granted: 1989-03-21
•
Expires: 2007-12-17
Abstract
Abstract A silver halide light-sensitive material is disclosed, comprising a support having thereon at least one light-sensitive silver halide emulsion layer comprising silver halide grains and a binder, at least about 50 wt % of said silver halide grains comprising a silver halide grain matrix having thereon from about 10 to 10,000 protrusions per square micrometer of grain matrix surface, said individual protrusions having an average projected area diameter of up to about 0.15 mu m, and a halogen composition of said protrusions differing from that of the grain matrix; said silver halide emulsion being chemically sensitized with at least one compound selected from the group consisting of a sulfur compound, a selenium compound, a reducing compound and a noble metal compound; and said silver halide emulsion being spectrally sensitized with a methine dye. A method for preparing a silver halide light-sensitive material comprising a support having thereon at least one light-sensitive silver halide emulsion layer comprising the steps of: (a) preparing an emulsion comprising a silver halide grain matrix; (b) forming protrusions on said silver halide grain matrix at a silver electric potential of at least about +110 mV, at least about 50 wt % of said silver halide grain matrix having thereon from about 10 to 10,000 protrusions per square micrometer of grain matrix surface, said individual protrusions having an average projected area diameter of up to about 0.15 mu m, and a halogen composition of said protrusions having a halogen composition differing from that of said grain matrix; (c) stabilizing the grains obtained in step (b) with a grain formation-stopping agent; and (d) then chemically sensitizing said stabilized grains.
Inventors
- 👤 Seiichiro Kishida
- 👤 Minoru Sato
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 07:19
CPC Classifications
G; G03; G03C; G03C1/00; G03C1/005; G03C1/0051; G03C1/06; G03C1/07; G03C1/08; G03C1/09; G03C1/10; G03C1/12; G03C1/14; G03C1/16; G03C1/18; G03C1/20; G03C1/22; G03C1/26
Claims Analysis
Total Claims: 29
Claim 1
Independent Claim
129 words
A silver halide light-sensitive material comprising a support having thereon at least one light-sensitive silver halide emulsion layer comprising silver halide grains and a binder, at least about 50 wt% of said silver halide grains comprising a silver halide grain matrix having thereon from about 10 to 10,000 protrusions per square micrometer of grain matrix surface, said individual protrusions having an average projected area diameter of up to about 0.15 μm, and a halogen composition of said protrusions differing from that of the grain matrix; said silver halide emulsion being chemically sensitized with at least one compound selected from the group consisting of a sulfur compound, a selenium compound, a reducing compound and a noble metal compound; and said silver halide emulsion being spectrally sensitized with a methine dye.
Claim 2
Dependent Claim
129 words
A silver halide light-sensitive material comprising a support having thereon at least one light-sensitive silver halide emulsion layer comprising silver halide grains and a binder, at least about 50 wt% of said silver halide grains comprising a silver halide grain matrix having thereon from about 10 to 10,000 protrusions per square micrometer of grain matrix surface, said individual protrusions having an average projected area diameter of up to about 0.15 μm, and a halogen composition of said protrusions differing from that of the grain matrix; said silver halide emulsion being chemically sensitized with at least one compound selected from the group consisting of a sulfur compound, a selenium compound, a reducing compound and a noble metal compound; and said silver halide emulsion being spectrally sensitized with a methine dye.
Claim 3
Dependent Claim
44 words
The silver halide light-sensitive material as claimed in claim 1, wherein prior to the chemical sensitization of the silver halide emulsion containing silver halide grain matrixes having protrusions on the surface thereof, the shape of the grain is stabilized with a grain formation-stopping agent.
Claim 4
Dependent Claim
31 words
The method as claimed in claim 2, wherein said grain formation-stopping agent is selected from the group consisting of a mercapto compound, an azole compound, a dye, and a combination thereof.
Claim 5
Dependent Claim
19 words
The silver halide light-sensitive material as claimed in claim 3, wherein the grain formation-stopping agent is a cyanine dye.
Claim 6
Dependent Claim
19 words
The silver halide light-sensitive material as claimed in claim 3, wherein the grain formation-stopping agent is a merocyanine dye.
Claim 7
Dependent Claim
26 words
The silver halide light-sensitive material as claimed in claim 3, wherein the grain formation-stopping agent is selected from the group consisting of D-1 to D-45; ##STR4##
Claim 8
Dependent Claim
33 words
The silver halide light-sensitive material as claimed in claim 1, wherein said silver halide grain matrix comprises silver bromide or silver bromoiodide and said protrusions comprise silver bromide, silver bromochloride, or silver chloride.
Claim 9
Dependent Claim
46 words
The silver halide light-sensitive material as claimed in claim 7, wherein said silver halide grain matrix comprises silver bromoiodide containing up to about 10 mol% of silver iodide and said protrusions comprise silver bromochloride or silver chloride containing at least about 50 mol% of silver chloride.
Claim 10
Dependent Claim
28 words
The silver halide light-sensitive material as claimed in claim 7, wherein said protrusions comprise silver chloride or silver bromochloride containing at least about 30 mol% of silver chloride.
Claim 11
Dependent Claim
28 words
The silver halide light-sensitive material as claimed in claim 9, wherein said protrusions comprise silver chloride or silver bromochloride containing at least about 75 mol% of silver chloride.
Claim 12
Dependent Claim
45 words
The silver halide light-sensitive material as claimed in claim 1, wherein said silver halide grain matrix has the (111) plane and the total surface area of the (111) planes of the grain matrix is at least about 50% of the total grain matrix surface area.
Claim 13
Dependent Claim
29 words
The silver halide light-sensitive material as claimed in claim 1, wherein said silver halide grain matrix is a tabular grain having an aspect ratio of about 5 to 20.
Claim 14
Dependent Claim
47 words
The silver halide light-sensitive material as claimed in claim 1, wherein at least about 70 wt% of said silver halide grains comprise the silver halide grain matrix having thereon from about 10 to 10,000 of said protrusions per square micrometer of said silver halide grain matrix surface.
Claim 15
Dependent Claim
26 words
The silver halide light-sensitive material as claimed in claim 1, wherein the average projected area diameter of said individual protrusions is up to about 0.13 μm.
Claim 16
Dependent Claim
27 words
The silver halide light-sensitive material as claimed in claim 14, wherein the average projected area diameter of said individual protrusions is from about 0.01 to 0.11 μm.
Claim 17
Dependent Claim
32 words
The silver halide light-sensitive material as claimed in claim 1, wherein said silver halide grains each have from about 20 to 10,000 of said protrusions per square micrometer of grain matrix surface.
Claim 18
Dependent Claim
17 words
The silver halide light-sensitive material as claimed in claim 1, wherein said protrusions are substantially triangular pyramids.
Claim 19
Dependent Claim
32 words
The silver halide light-sensitive material as claimed in claim 1, wherein the ratio of the average height of the protrusions to the average projected area diameter thereof is at least about 0.4/1.
Claim 20
Independent Claim
135 words
A method for preparing a silver halide light-sensitive material comprising a support having thereon at least one light-sensitive silver halide emulsion layer comprising the steps of: (a) preparing an emulsion comprising a silver halide grain matrix; (b) forming protrusions on said silver halide grain matrix at a silver potential of at least about +110 mV, at least about 50 wt% of said silver halide grain matrix having thereon from about 10 to 10,000 protrusions per square micrometer of grain matrix surface, said individual protrusions having an average projected area diameter of up to about 0.15 μm, and a halogen composition of said protrusions having a halogen composition differing from that of said grain matrix; (c) stabilizing the grains obtained in step (b) with a grain formation-stopping agent; and (d) then chemically sensitizing said stabilized grains.
Claim 21
Independent Claim
135 words
A method for preparing a silver halide light-sensitive material comprising a support having thereon at least one light-sensitive silver halide emulsion layer comprising the steps of: (a) preparing an emulsion comprising a silver halide grain matrix; (b) forming protrusions on said silver halide grain matrix at a silver potential of at least about +110 mV, at least about 50 wt% of said silver halide grain matrix having thereon from about 10 to 10,000 protrusions per square micrometer of grain matrix surface, said individual protrusions having an average projected area diameter of up to about 0.15 μm, and a halogen composition of said protrusions having a halogen composition differing from that of said grain matrix; (c) stabilizing the grains obtained in step (b) with a grain formation-stopping agent; and (d) then chemically sensitizing said stabilized grains.
Claim 22
Dependent Claim
17 words
The method as claimed in claim 19, wherein said silver potential is at least about +120 mV.
Claim 23
Dependent Claim
40 words
The method as claimed in claim 19, wherein said stabilizing step comprises adding to said emulsion from about 1×10 -4 mol to 5×10 -2 mol of a grain formation-stopping agent per mol of silver contained in said silver halide grains.
Claim 24
Dependent Claim
31 words
The method as claimed in claim 19, wherein said grain formation-stopping agent is selected from the group consisting of a mercapto compound, an azole compound, a dye, and a combination thereof.
Claim 25
Dependent Claim
16 words
The method as claimed in claim 22, wherein the grain formation-stopping agent is a cyanine dye.
Claim 26
Dependent Claim
16 words
The method as claimed in claim 22, wherein the grain formation-stopping agent is a merocyanine dye.
Claim 27
Dependent Claim
23 words
The method as claimed in claim 22, wherein the grain formation-stopping agent is selected from the group consisting of D-1 to D-45; ##STR5##
Claim 28
Dependent Claim
323 words
The method as claimed in claim 22, wherein said dye is a merocyanine dye represented by formula (I): ##STR6## wherein Z represents an atomic group necessary for forming a 5- or 6-membered heterocyclic ring; Q 1 and Q 2 each represents a sulfur atom, a selenium atom, or a >N--R 5 group, wherein R 5 represents a substituted or unsubstituted alkyl group containing from 1 to 8 carbon atoms, and a monocyclic aryl group which may contain an oxygen atom, a sulfur atom or a nitrogen atom in the carbon chain and may be substituted by a hydroxyl group, a halogen atom, an alkylaminocarbonyl group, an alkoxycarbonyl group, a carbonyl group, or a phenyl group which may be further substituted; Y represents a sulfur atom or a selenium atom; R 1 represents a substituted or unsubstituted alkyl group containing 1 to 8 carbon atoms, a substituted or unsubstituted alkenyl group containing 1 to 8 carbon atoms, which may contain an oxygen atom and a sulfur atom in the carbon chain; R 2 and R 4 each represents a substituted or unsubstituted alkyl group containing 1 to 8 carbon atoms, a substituted or unsubstituted alkenyl group containing 1 to 8 carbon atoms, which may contain an oxygen atom and a sulfur atom in the carbon chain, a hydrogen atom, or a substituted or unsubstituted monocyclic aryl group containing up to 8 carbon atoms; R 3 represents a hydrogen atom, a substituted or unsubstituted phenyl group containing up to 8 carbon atoms, or a substituted or unsubstituted alkyl group containing 1 to 6 carbon atoms; j is 0 or 1; m is 0, 1, 2 or 3; n is 0 or 1; provided that when m is 2 or 3, the plural R 3 groups may be linked to form a 5- or 6-membered ring; and further provided that at most one of R 1 , R 2 and R 4 contains a sulfo group.
Claim 29
Dependent Claim
23 words
The method as claimed in claim 19, wherein said chemically sensitizing step comprises sulfur sensitization, selenium sensitization, reduction sensitization or noble metal sensitization.
References Cited (Backward Citations)
US4386156A
Cited
US4414310A
Cited
US4433048A
Cited
US4434226A
Cited
US4435501A
Cited
US4439520A
Cited
US4585729A
Cited
US4735894A
Cited
US4758504A
Cited
US4769315A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-03-20 | 1992-09-19 | 1993-03-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-03-20 | 1996-09-19 | 1997-03-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-03-20 | 2000-09-19 | 2001-03-21 | $7700.00 | Window Closed / Lapsed |