Process for producing expanded particles of styrene-acrylonitrile-butadiene copolymer
Assignee: Mitsubishi Chemical BASF Co Ltd
•
Filing: 1987-08-18
•
Granted: 1989-03-14
•
Expires: 2007-08-18
Abstract
Abstract A process for producing expanded particles of a styrene-acrylonitrile-butadiene copolymer is disclosed, comprising dispersing styrene-acrylonitride-butadiene copolymer particles in water in a closed vessel, feeding a volatile blowing agent to the aqueous dispersion in the closed vessel, heating the aqueous dispersion to a temperature higher than a glass transition point of the copolymer particles by at least 20 DEG C. to impregnate the volatile blowing agent into the copolymer particles, and opening one end of the closed vessel to release the aqueous dispersion containing the expandable copolymer particles into a low pressure zone having a pressure lower than the inner pressure of the closed vessel. The resulting expanded particles have a degree of expansion of from 10 to 50.
Inventors
- 👤 Hiroshi Endo
- 👤 Toshihiro Gotoh
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 09:42
CPC Classifications
C; C08; C08J; C08J9/00; C08J9/16; C08J9/18; C08J9/04; C08J9/12; C08J9/14; C08J9/141; C08J2355/00; C08J2355/02
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
137 words
A process for producing expanded particles of a styrene-acrylonitrile-butadiene copolymer which comprises dispersing styrene-acrylonitrile-butadiene copolymer particles in water in a closed vessel, feeding a volatile blowing agent to the aqueous dispersion in the closed vessel, heating the aqueous dispersion to a temperature higher than the glass transition point of the copolymer particles by at least 20° C. wherein the heated aqueous dispersion is maintained at the heated temperature for a period of from 5 minutes to 5 hours to impregnate said volatile blowing agent into the copolymer particles, and opening one end of the closed vessel to release the aqueous dispersion containing the expandable copolymer particles into a low pressure zone having a pressure lower than the inner pressure of the closed vessel, wherein said expanded particles have a bulk density of from 10 to 70 g/liter.
Claim 2
Dependent Claim
137 words
A process for producing expanded particles of a styrene-acrylonitrile-butadiene copolymer which comprises dispersing styrene-acrylonitrile-butadiene copolymer particles in water in a closed vessel, feeding a volatile blowing agent to the aqueous dispersion in the closed vessel, heating the aqueous dispersion to a temperature higher than the glass transition point of the copolymer particles by at least 20° C. wherein the heated aqueous dispersion is maintained at the heated temperature for a period of from 5 minutes to 5 hours to impregnate said volatile blowing agent into the copolymer particles, and opening one end of the closed vessel to release the aqueous dispersion containing the expandable copolymer particles into a low pressure zone having a pressure lower than the inner pressure of the closed vessel, wherein said expanded particles have a bulk density of from 10 to 70 g/liter.
Claim 3
Dependent Claim
27 words
A process as in claim 1, wherein said releasing of the aqueous dispersion is effected under a pressure of an inorganic gas into an atmospheric pressure zone.
Claim 4
Dependent Claim
12 words
A process as in claim 1, wherein said blowing agent is butane.
Claim 5
Dependent Claim
48 words
A process as in claim 1, wherein said heating of the dispersion is at a temperature between a temperature higher than the glass transition point of the copolymer particles by 25° C. and a temperature higher than the glass transition point of the copolymer particles by 55° C.
Claim 6
Dependent Claim
26 words
A process as in claim 1, wherein the heated aqueous dispersion is maintained at the heating temperature for a period of from 0.5 to 5 hours.
Claim 7
Dependent Claim
20 words
A process as in claim 1, wherein the expanded particles have a ratio of closed cell of 80% or more.
Claim 8
Dependent Claim
20 words
A process as in claim 1, wherein the expanded particles have a cell diameter of from 20 to 200 μm.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-03-13 | 1992-09-12 | 1993-03-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-03-13 | 1996-09-12 | 1997-03-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-03-13 | 2000-09-12 | 2001-03-14 | $7700.00 | Window Closed / Lapsed |