Forming optical fiber having abrupt index change
Assignee: Corning Glass Works
•
Filing: 1987-08-05
•
Granted: 1989-03-07
•
Expires: 2007-08-05
Abstract
Abstract A method is disclosed for making a step-index optical fiber having a steep refractive index gradient between core and cladding. Core glass particles comprising a base glass and a refractive index-increasing dopant are deposited on a mandrel. The mandrel is removed and the resultant soot preform is consolidated to form a core preform having a dopant-poor surface region. The core glass preform is stretched and the hole therein is closed to form a core bait rod. Cladding glass soot is deposited on the core bait rod at a density which is at least 0.5 g/cc. This is accomplished by directing the flame from an auxiliary burner onto the core bait rod immediately prior to the deposition of cladding soot thereon. The resultant preform is consolidated and drawn into an optical fiber. In another embodiment, the etched core preform is overclad with a layer of cladding glass, and the composite preform is stretched prior to applying a second overclad layer.
Inventors
- 👤 John W. Gilliland
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 10:57
CPC Classifications
C; C03; C03B; C03B37/00; C03B37/01; C03B37/012; C03B37/014; C03B37/01466; C03B37/01446; C03B37/01473; C03B2201/00; C03B2201/06; C03B2201/08; C03B2201/20; C03B2201/28; C03B2201/30; C03B2201/31; C03B2201/32; C03B2201/40; C03B2201/42; C03B2203/00; C03B2203/10; C03B2203/22
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
170 words
A method of making an optical fiber preform comprising forming a glass rod the composition of which includes a base glass and at least one dopant, the concentration of said dopant changing radially from an acceptable level within said rod to an unacceptable level in a surface layer of said rod, immersing said rod in an etchant to remove said surface layer, the step of etching being sufficiently severe that it results in the formation of etch pits in the surface of said rod, heating and stretching said rod to smooth said etch pits and provide a better surface on which to deposit cladding soot, the step of stretching resulting in the formation of an elongated core bait rod, and thereafter applying to said rod a layer of glass having a composition different from that of said rod by depositing a plurality of layers of particles of glass on said elongated core bait rod and heating the resultant assembly to consolidate said glass particles and form said layer of glass.
Claim 2
Independent Claim
170 words
A method of making an optical fiber preform comprising forming a glass rod the composition of which includes a base glass and at least one dopant, the concentration of said dopant changing radially from an acceptable level within said rod to an unacceptable level in a surface layer of said rod, immersing said rod in an etchant to remove said surface layer, the step of etching being sufficiently severe that it results in the formation of etch pits in the surface of said rod, heating and stretching said rod to smooth said etch pits and provide a better surface on which to deposit cladding soot, the step of stretching resulting in the formation of an elongated core bait rod, and thereafter applying to said rod a layer of glass having a composition different from that of said rod by depositing a plurality of layers of particles of glass on said elongated core bait rod and heating the resultant assembly to consolidate said glass particles and form said layer of glass.
Claim 3
Independent Claim
128 words
A method of making an optical fiber preform comprising forming a glass rod the composition of which includes a base glass and at least one dopant, the concentration of said dopant changing radially from an acceptable level within said rod to an unacceptable level in a surface layer of said rod, removing said surface layer, applying to said rod a layer of glass having a composition different from that of said rod, said layer of glass being free from said dopant, whereby the surface of the composite body formed of said rod and said layer is also free from said dopant, heating and stretching said composite body to form a bait rod of reduced diameter, and applying a second layer of glass to said reduced diameter bait rod.
Claim 4
Independent Claim
128 words
A method of making an optical fiber preform comprising forming a glass rod the composition of which includes a base glass and at least one dopant, the concentration of said dopant changing radially from an acceptable level within said rod to an unacceptable level in a surface layer of said rod, removing said surface layer, applying to said rod a layer of glass having a composition different from that of said rod, said layer of glass being free from said dopant, whereby the surface of the composite body formed of said rod and said layer is also free from said dopant, heating and stretching said composite body to form a bait rod of reduced diameter, and applying a second layer of glass to said reduced diameter bait rod.
Claim 5
Independent Claim
108 words
A method of making an optical fiber preform comprising forming a glass rod the composition of which includes a base glass and at least one dopant, the concentration of said dopant changing radially from an acceptable level within said rod to an unacceptable level in a surface layer of said rod, immersing said glass rod in an etchant to remove said surface layer, and thereafter depositing a plurality of layers of particles of glass on said etched rod, at least the first of said layers of glass particles being deposited with a density of at least 0.5 g/cc, and heating the resultant assembly to consoldiate said glass particles.
Claim 6
Independent Claim
108 words
A method of making an optical fiber preform comprising forming a glass rod the composition of which includes a base glass and at least one dopant, the concentration of said dopant changing radially from an acceptable level within said rod to an unacceptable level in a surface layer of said rod, immersing said glass rod in an etchant to remove said surface layer, and thereafter depositing a plurality of layers of particles of glass on said etched rod, at least the first of said layers of glass particles being deposited with a density of at least 0.5 g/cc, and heating the resultant assembly to consoldiate said glass particles.
Claim 7
Dependent Claim
32 words
A method in accordance with claim 1 wherein the step of depositing comprises depositing at least the first of said layers of glass particles with a density of at least 0.5 g/cc.
Claim 8
Dependent Claim
36 words
A method in accordance with claim 4 wherein the step of depositing comprises directing a heating flame onto the surface of said bait rod immediately preceding the application of the first layer of glass particles thereto.
Claim 9
Dependent Claim
65 words
A method in accordance with claim 4 wherein the step of depositing comprises directing onto the surface of said bait rod a flame hydrolysis burner flame containing said glass particles, and directing a heating flame onto the surface of said bait rod immediately preceding the application of the first layer of glass particles thereto, said flame hydrolysis burner flame being contiguous with said heating flame.
Claim 10
Dependent Claim
91 words
A method in accordance with claim 1 wherein the step of applying a layer of glass comprises applying a plurality of layers of particles of glass on said elongated core bait rod and heating the resultant assembly to consolidate said glass particles and form said layer of glass, said glass particles being formed of a base glass and a dopant which lowers the softening point thereof so that, during the step of heating to consolidate said glass particles, said particles flow and fill in surface imperfections in said core bait rod.
Claim 11
Dependent Claim
36 words
A method in accordance with claim 3 wherein the step of depositing comprises directing a heating flame onto the surface of said bait rod immediately preceding the application of the first layer of glass particles thereto.
Claim 12
Dependent Claim
65 words
A method in accordance with claim 3 wherein the step of depositing comprises directing onto the surface of said bait rod a flame hydrolysis burner flame containing said glass particles, and directing a heating flame onto the surface of said bait rod immediately preceding the application of the first layer of glass particles thereto, said flame hydrolysis burner flame being contiguous with said heating flame.
Claim 13
Independent Claim
159 words
A method of making a step-index optical fiber preform having an abrupt refractive index change between the core and adjacent cladding, said method comprising forming a porous glass preform comprising a base glass and a dopant which increases the refractive index of said base glass, heating said porous preform to a temperature that is sufficiently high that it consolidates to a non-porous preform, the out-diffusion of dopant during said consolidation step resulting in a dopant-poor region that extends into said consolidated core preform a given distance from the surface thereof, removing said dopant-poor region, and applying cladding glass to the resultant consolidated core preform by depositing a plurality of layers of cladding glass particles on said consolidated core preform, a flame being directed onto the surface of said core preform immediately preceding the application of the first layer of glass particles thereto, at least the first layer of cladding glass particles having a density of at least 0.6 g/cc.
Claim 14
Independent Claim
159 words
A method of making a step-index optical fiber preform having an abrupt refractive index change between the core and adjacent cladding, said method comprising forming a porous glass preform comprising a base glass and a dopant which increases the refractive index of said base glass, heating said porous preform to a temperature that is sufficiently high that it consolidates to a non-porous preform, the out-diffusion of dopant during said consolidation step resulting in a dopant-poor region that extends into said consolidated core preform a given distance from the surface thereof, removing said dopant-poor region, and applying cladding glass to the resultant consolidated core preform by depositing a plurality of layers of cladding glass particles on said consolidated core preform, a flame being directed onto the surface of said core preform immediately preceding the application of the first layer of glass particles thereto, at least the first layer of cladding glass particles having a density of at least 0.6 g/cc.
Claim 15
Independent Claim
143 words
A method of making an optical fiber preform comprising forming a porous glass preform comprising a base glass and a dopant which increases the refractive index of said base glass, heating said porous preform to a temperature that is sufficiently high that it consolidates to a non-porous preform, the out-diffusion of dopant during said consolidation step resulting in a dopant-poor region that extends into said consolidated core preform a given distance from the surface thereof, immersing non-porous preform in an etchant to remove said dopant-poor region, heating said non-porous preform and applying tensile force thereto to form an elongated core bait rod, depositing a plurality of layers of cladding glass particles on said elongated core bait rod, at least the first layer of particles having a density of at least 0.5 g/cc, and heating the resultant assembly to consolidate said cladding glass particles.
Claim 16
Independent Claim
143 words
A method of making an optical fiber preform comprising forming a porous glass preform comprising a base glass and a dopant which increases the refractive index of said base glass, heating said porous preform to a temperature that is sufficiently high that it consolidates to a non-porous preform, the out-diffusion of dopant during said consolidation step resulting in a dopant-poor region that extends into said consolidated core preform a given distance from the surface thereof, immersing non-porous preform in an etchant to remove said dopant-poor region, heating said non-porous preform and applying tensile force thereto to form an elongated core bait rod, depositing a plurality of layers of cladding glass particles on said elongated core bait rod, at least the first layer of particles having a density of at least 0.5 g/cc, and heating the resultant assembly to consolidate said cladding glass particles.
Claim 17
Dependent Claim
38 words
A method in accordance with claim 11 wherein the step of depositing a plurality of layers of cladding glass particles comprises locally heating said elongated core bait rod immediately prior to the deposition of cladding glass particles thereon.
Claim 18
Dependent Claim
75 words
A method in accordance with claim 11 wherein the step of depositing a plurality of layers of cladding particles comprises rotating and longitudinally traversing said elongated core bait rod with respect to a stream of cladding glass particles so that said particles deposit on said bait rod along a helical path and directing a flame toward said bait rod in a region adjacent to that region wherein said stream of particles contacts said bait rod.
Claim 19
Dependent Claim
54 words
A method in accordance with claim 11 wherein, prior to the step of heating and stretching said consolidated core preform, a plurality of layers of cladding glass particles is deposited on the surface of said consolidated core preform and the resultant composite body is subjected to a temperature sufficiently high to consolidate said particles.
References Cited (Backward Citations)
US4421539A
Cited
US4494968A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-03-06 | 1992-09-05 | 1993-03-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-03-06 | 1996-09-05 | 1997-03-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-03-06 | 2000-09-05 | 2001-03-07 | $7700.00 | Window Closed / Lapsed |