Composite material in rod, tube, strip, sheet or plate shape with reversible thermomechanical properties and process for its production
Assignee: BBC Brown Boveri AG Switzerland
•
Filing: 1986-09-26
•
Granted: 1989-02-28
•
Expires: 2006-09-26
Abstract
Abstract A composite material in rod, tube, strip, sheet or plate shape with reversible thermomechanical properties is produced by joining of at least two parts consisting of a total of at least one shape memory alloy having a two-way effect, whereby each part has a memory effect by itself. In the case of at least two shape memory alloys (1, 2) with different transition temperatures but the same mode of movement, the joining of the individual parts can take place prior to the deformation in the low temperature range necessary to inducing the two-way effect. In the case of differing types and degrees of movement of the individual parts (25, 26), their joining can first be accomplished only after the individual deformations of each part for itself in the low temperature range are accomplished regardless of how many shape memory alloys with different transition temperatures are used in the structure of the composite material.
Inventors
- 👤 Joachim Albrecht
- 👤 Thomas Duerig
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 19:13
CPC Classifications
B; B32; B32B; B32B15/00; B32B15/01; G; G01; G01K; G01K5/00; G01K5/48; G01K5/483; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12014; Y10T428/12028; Y10T428/12063; Y10T428/1209; Y10T428/12493; Y10T428/125; Y10T428/12507; Y10T428/12514; Y10T428/12521; Y10T428/12771; Y10T428/12861; Y10T428/12903; Y10T428/1291
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
52 words
A process for the production of a composite material with reversible thermomechanical properties, comprising joining at least two parts having a memory effect and each of said parts being of at least one shape memory alloy having a two-way effect, by rolling, compression molding, extrusion, welding, soldering, diffusion joining or powder metallurgy.
Claim 2
Dependent Claim
52 words
A process for the production of a composite material with reversible thermomechanical properties, comprising joining at least two parts having a memory effect and each of said parts being of at least one shape memory alloy having a two-way effect, by rolling, compression molding, extrusion, welding, soldering, diffusion joining or powder metallurgy.
Claim 3
Dependent Claim
59 words
The process of claim 1, wherein the individual parts which possess different transition temperatures are joined first by rolling, welding, diffusion joining, soldering, or in a powder metallurgy manner into a composite material and the latter as a whole is subsequently subjected to thermal treatment and a mechanical deformation in the low temperature range to induce the two-way effect.
Claim 4
Dependent Claim
63 words
The process of claim 1, wherein the individual parts each are subjected to individual thermal treatment and individual mechanical deformation in the low temperature range to induce the two-way effect, so that the individual parts are exposed to different types of deformation or degrees of deformation and that the individual parts subsequently are joined by bonding or local fusing into a composite material.
Claim 5
Dependent Claim
131 words
A prismatic bending bar having reversible thermomechanical properties, comprising a first part, said first part comprising a shape memory alloy comprising 45.5 wt.% Ti, 10 wt.% Cu, and the remainder Ni, said first part having a width of 2.5 mm, a thickness of 1.2 mm and a length of 35 mm, joined to a second part, said second part comprising a shape memory alloy comprising 14.4 wt.% Al, 3.2 wt.% Ni, and the remainder Cu, said second part having the same width, thickness and length as said first part, to form said prismatic bending bar; wherein the transformation temperatures of said first part are A S =70° C. and A F =95° C., and the transition temperatures of said second part are A S =120° C. and A F =150° C.
Claim 6
Dependent Claim
131 words
A prismatic bending bar having reversible thermomechanical properties, comprising a first part, said first part comprising a shape memory alloy comprising 45.5 wt.% Ti, 10 wt.% Cu, and the remainder Ni, said first part having a width of 2.5 mm, a thickness of 1.2 mm and a length of 35 mm, joined to a second part, said second part comprising a shape memory alloy comprising 14.4 wt.% Al, 3.2 wt.% Ni, and the remainder Cu, said second part having the same width, thickness and length as said first part, to form said prismatic bending bar; wherein the transformation temperatures of said first part are A S =70° C. and A F =95° C., and the transition temperatures of said second part are A S =120° C. and A F =150° C.
Claim 7
Dependent Claim
170 words
A process for the production of a prismatic bending bar having reversible thermomechanical properties, said bending bar having two parts, said first part comprising a shape memory alloy comprising 45.5 wt.% Ti, 10 wt.% Cu, and the remainder Ni, and a second part comprising a shape memory comprising 14.4 wt.% Al, 3.2 wt.% Ni, and the remainder Cu, wherein the transformation temperatures of said first part are A S =70° C. and A F =95° C., and the transformation temperatures of said second part are A S =120° C. and A F =150° C., comprising the steps of: joining said first and second part by hot rolling to give a bending bar of 2.5 mm width, 2.4 mm height and 35 mm length; annealing said bending for 1/2 hour at 850° C. and then quenching said annealed bar in ice water; deforming said quenched bar by 7.5% in the low temperature martensitic range by bending; heating said bar for 1/2 hour at 300° C. and then cooling to room temperature.
Claim 8
Dependent Claim
170 words
A process for the production of a prismatic bending bar having reversible thermomechanical properties, said bending bar having two parts, said first part comprising a shape memory alloy comprising 45.5 wt.% Ti, 10 wt.% Cu, and the remainder Ni, and a second part comprising a shape memory comprising 14.4 wt.% Al, 3.2 wt.% Ni, and the remainder Cu, wherein the transformation temperatures of said first part are A S =70° C. and A F =95° C., and the transformation temperatures of said second part are A S =120° C. and A F =150° C., comprising the steps of: joining said first and second part by hot rolling to give a bending bar of 2.5 mm width, 2.4 mm height and 35 mm length; annealing said bending for 1/2 hour at 850° C. and then quenching said annealed bar in ice water; deforming said quenched bar by 7.5% in the low temperature martensitic range by bending; heating said bar for 1/2 hour at 300° C. and then cooling to room temperature.
Claim 9
Dependent Claim
38 words
A shaped part made of a composite material having shape memory properties, said shaped part comprising at least two sections, at least one of said sections having a two-way memory effect, and said sections being coupled metallurgically together.
Claim 10
Dependent Claim
38 words
A shaped part made of a composite material having shape memory properties, said shaped part comprising at least two sections, at least one of said sections having a two-way memory effect, and said sections being coupled metallurgically together.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-02-28 | 1992-08-29 | 1993-02-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-02-28 | 1996-08-29 | 1997-02-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-02-28 | 2000-08-29 | 2001-02-28 | $7700.00 | Window Closed / Lapsed |