Process for producing ultrafine metal powder
Assignee: Mitsubishi Chemical Corp
•
Filing: 1988-04-21
•
Granted: 1989-02-28
•
Expires: 2008-04-21
Abstract
Abstract In a process for producing an ultrafine powder of a metal by subjecting a transition metal carbonyl compound to gas phase pyrolysis reaction, the improvement which comprises diluting said carbonyl compound with an inert gas or hydrogen to a concentration of 3 vol. % or less with optional addition of an oxygen-containing organic compound and/or a sulfur-containing organic compound in an amount of 0.0001 to 0.1 mol per mol of said carbonyl compound to prepare a gas mixture, and then carrying out gas phase pyrolysis reaction at 300° C. or higher by allowing said gas mixture to reside for 5 seconds or less in a reaction system to which a magnetic field of 100 gauss or higher is being applied, thereby obtaining the ultrafine powder of said metal having a length of 1 micron or less, a coercive force of 800 oersted or higher and a saturation magnetization of 120 emu/g or higher.
Inventors
- 👤 Yoshiteru Kageyama
- 👤 Yoshiaki Sawada
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 14:29
CPC Classifications
H; H01; H01F; H01F1/00; H01F1/01; H01F1/03; H01F1/032; H01F1/04; H01F1/06; B; B22; B22F; B22F9/00; B22F9/16; B22F9/30; B22F9/305; C; C22; C22B; C22B5/00; C22B5/02; C22B5/20; G; G11; G11B; G11B5/00; G11B5/84; G11B5/8416; H01F41/00; H01F41/14; H01F41/22
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
153 words
In a process for producing an ultrafine powder of a metal by subjecting a transition metal carbonyl compound to gas phase pyrolysis reaction, the improvement which comprises diluting said carbonyl compound with an inert gas or hydrogen to a concentration of 3 vol. % or less with optional addition of an oxygen-containing organic compound and/or a sulfur-containing organic compound in an amount of 0.0001 to 0.1 mol per mol of said carbonyl compound to prepare a gas mixture, and then carrying out gas phase pyrolysis reaction at 300° C. or higher by allowing said gas mixture to reside for 5 seconds or less in a reaction system to which a magnetic field of 100 gauss or higher is being applied, thereby obtaining the ultrafine powder of said metal having a length of 1 micron or less, a coercive force of 800 oersted or higher and a saturation magnetization of 120 emu/g or higher.
Claim 2
Dependent Claim
153 words
In a process for producing an ultrafine powder of a metal by subjecting a transition metal carbonyl compound to gas phase pyrolysis reaction, the improvement which comprises diluting said carbonyl compound with an inert gas or hydrogen to a concentration of 3 vol. % or less with optional addition of an oxygen-containing organic compound and/or a sulfur-containing organic compound in an amount of 0.0001 to 0.1 mol per mol of said carbonyl compound to prepare a gas mixture, and then carrying out gas phase pyrolysis reaction at 300° C. or higher by allowing said gas mixture to reside for 5 seconds or less in a reaction system to which a magnetic field of 100 gauss or higher is being applied, thereby obtaining the ultrafine powder of said metal having a length of 1 micron or less, a coercive force of 800 oersted or higher and a saturation magnetization of 120 emu/g or higher.
Claim 3
Dependent Claim
19 words
The process according to claim 1, wherein the transition metal carbonyl compound is Fe(CO) 5 or Ni(CO) 4 .
Claim 4
Dependent Claim
33 words
The process according to claim 1, wherein the transition metal carbonyl compound is a mixture of a transition metal carbonyl compound haYing a high boiling point and Fe(CO) 5 or Ni(CO) 4 .
Claim 5
Dependent Claim
24 words
The process according to claim 1, wherein the oxygen-containing organic compound is selected from the group consisting of an alcohol, ester, ketone and ether.
Claim 6
Dependent Claim
20 words
The process according to claim 4, wherein the oxygen-containing organic compound is an alcohol having 1 to 8 carbon atoms.
Claim 7
Dependent Claim
31 words
The process according to claim 5, wherein the alcohol is selected from the group consisting of methyl alcohol, ethyl alcohol, propyl alcohol, butyl alcohol, octyl alcohol, trimethyl silanol and ethylene glycol.
Claim 8
Dependent Claim
16 words
The process according to claim 1, wherein the sulfur-containing organic compound is a mercaptan or thioether.
Claim 9
Dependent Claim
23 words
The process according to claim 7, wherein the mercaptan is selected from the group consisting of methanethiol, ethanethiol, n-propanethiol, n-butanethiol, n-pentanethiol, and n-hexanethiol.
Claim 10
Dependent Claim
24 words
The process according to claim 7, wherein the thioether is selected from the group consisting of methylthiomethane, ethylthiomethane, butylthiomethane, propylthiomethane, ethylthioethane, propylthioethane and butylthioethane.
Claim 11
Dependent Claim
31 words
The process according to claim 1, wherein the amount of the oxygen-containing organic compound and/or the sulfur-containing organic compound added is 0.001 to 0.05 mol per mol of said carbonyl compound.
Claim 12
Dependent Claim
28 words
The process according to claim 1, wherein the concentration of said carbonyl compound in the inert gas or hydrogen as a diluent is 0.01 to 3 vol. %.
Claim 13
Dependent Claim
22 words
The process according to claim 1, wherein the intensity of the magnetic field is in the range of 300 to 1,500 gauss.
Claim 14
Dependent Claim
21 words
The process according to claim 1, wherein the pyrolysis reaction is carried out at a temperature of 400° to 700° C.
Claim 15
Dependent Claim
29 words
The process according to claim 1, wherein the ultrafine powder obtained has a coercive force of 1300 to 2500 oersted and a saturation magnetization of 120 to 200 emu/g.
Claim 16
Dependent Claim
14 words
An ultrafine powder of a metal produced according to the process of claim 1.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-02-28 | 1992-08-29 | 1993-02-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-02-28 | 1996-08-29 | 1997-02-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-02-28 | 2000-08-29 | 2001-02-28 | $7700.00 | Window Closed / Lapsed |