Assignee: Sermatech International Inc
•
Filing: 1987-04-15
•
Granted: 1989-02-28
•
Expires: 2007-04-15
Abstract
Abstract The worn tip of a turbine blade is restored by applying a metallurgically bonded wear resistant surface at the tip. The wear resistant surface is applied using a transferred plasma arc and powdered metal particles.
Inventors
- 👤 Timothy A. Wertz
- 👤 Gilbert A. Saltzman
- 👤 Ira L. Friedman
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 05:58
CPC Classifications
B; B23; B23P; B23P6/00; B23P6/002; B23P6/007; F; F01; F01D; F01D5/00; F01D5/005; F01D5/12; F01D5/14; F01D5/20; Y; Y02; Y02T; Y02T50/00; Y02T50/60; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49316; Y10T29/49318; Y10T29/49718; Y10T29/49732; Y10T29/49742
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
35 words
A turbine engine blade comprising a blade root; a blade extending from said blade root to a blade tip; and a metallurgically bonded wear resistant surface entirely made from powdered metal on said blade tip.
Claim 2
Dependent Claim
35 words
A turbine engine blade comprising a blade root; a blade extending from said blade root to a blade tip; and a metallurgically bonded wear resistant surface entirely made from powdered metal on said blade tip.
Claim 3
Dependent Claim
34 words
A turbine blade as set forth in claim 1 wherein said wear resistant surface is a composite of a metal alloy defining a matrix and abrasive particles of hard material distributed throughout said matrix.
Claim 4
Dependent Claim
27 words
A turbine blade as set forth in claim 2 wherein said particles are selected from the group consisting of ceramics and refractory metal carbides, nitrides and borides.
Claim 5
Dependent Claim
19 words
A turbine blade as set forth in claim 1 wherein said blade is formed of a single crystal structure.
Claim 6
Dependent Claim
24 words
A turbine blade as set forth in claim 1 wherein said wear surface is of a thickness of from 0.010 inches to 0.120 inches.
Claim 7
Dependent Claim
25 words
A turbine blade as set forth in claim 5 wherein said particles are in a range of size of about 0.001 inches to 0.030 inches.
Claim 8
Dependent Claim
20 words
A turbine blade as set forth in claim 1 wherein said blade is formed of a directionally solidified crystal structure.
Claim 9
Dependent Claim
49 words
A restored turbine engine blade comprising a blade root; a curved blade extending from said blade root to a blade tip; and a metallurgically bonded wear resistant surface entirely made from powdered metal on said tip of a thickness in a range of from 0.010 inches to 0.120 inches.
Claim 10
Dependent Claim
49 words
A restored turbine engine blade comprising a blade root; a curved blade extending from said blade root to a blade tip; and a metallurgically bonded wear resistant surface entirely made from powdered metal on said tip of a thickness in a range of from 0.010 inches to 0.120 inches.
Claim 11
Dependent Claim
29 words
A restored turbine blade as set forth in claim 8 wherein said wear resistant surface is of a thickness in a range of from 0.010 inches to 0.100 inches.
Claim 12
Dependent Claim
32 words
A restored turbine blade as set forth in claim 8 wherein said blade is made of a nickel-base alloy and said wear resistant surface is characterized in being a cast metal alloy.
Claim 13
Dependent Claim
34 words
A restored turbine blade as set forth in claim 10 wherein said wear resistant surface has abrasive particles therein in a ratio of from 10% to 80% by weight of said cast metal alloy.
Claim 14
Independent Claim
79 words
A method of rebuilding a blade tip of a turbine engine blade said method comprising the steps of creating a transferred plasma arc between an electrode and a worn tip of the turbine blade at an amperage of from 1 amp to 15 amps; and feeding powdered metal particles into the arc for depositing a series of overlapping weld deposits on the blade tip to form a wear resistant layer thereon, said layer being metallurgically bonded to the tip.
Claim 15
Independent Claim
79 words
A method of rebuilding a blade tip of a turbine engine blade said method comprising the steps of creating a transferred plasma arc between an electrode and a worn tip of the turbine blade at an amperage of from 1 amp to 15 amps; and feeding powdered metal particles into the arc for depositing a series of overlapping weld deposits on the blade tip to form a wear resistant layer thereon, said layer being metallurgically bonded to the tip.
Claim 16
Dependent Claim
23 words
A method as set forth in claim 12 wherein the wear resistant layer is of a thickness of from 0.010 to 0.120 inches.
References Cited (Backward Citations)
US3199836A
Cited
SU507428A1
Cited
US4033792A
Cited
US4028788A
Cited
US4050133A
Cited
US4214355A
Cited
US4176433A
Cited
US4227703A
Cited
US4326833A
Cited
US4390320A
Cited
US4386112A
Cited
US4671735A
Cited
EP0166676A2
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-02-28 | 1992-08-29 | 1993-02-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-02-28 | 1996-08-29 | 1997-02-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-02-28 | 2000-08-29 | 2001-02-28 | $7700.00 | Window Closed / Lapsed |