Modified ceramic structures and methods of making the same
Assignee: Lanxide Technology Co LP
•
Filing: 1986-09-17
•
Granted: 1989-02-21
•
Expires: 2006-09-17
Abstract
Abstract A method of producing self-supporting ceramic structures comprising (i) a polycrystalline oxidation reaction product formed upon oxidation of a body of molten parent metal with an oxidant, and (ii) interconnected porosity at least partially accessible from one or more surfaces of said ceramic body. A second polycrystalline ceramic material is incorporated into the porosity of said ceramic body to modify or contribute to its properties.
Inventors
- 👤 Ratnesh K. Dwivedi
- 👤 Christopher R. Kennedy
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 11:39
CPC Classifications
C; C04; C04B; C04B35/00; C04B41/00; C04B41/009; C04B35/622; C04B35/64; C04B35/65; C04B35/652; C04B41/45; C04B41/50; C04B41/5025; C04B41/80; C04B41/81; C04B41/85; C04B41/87
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
162 words
A method of producing a self-supporting ceramic composite product comprising the steps of: (a) forming a self-supporting ceramic composite body comprising a ceramic matrix of an oxidation reaction product embedding at least one filler material, said self-supporting ceramic composite body exhibiting at least some interconnected porosity and being formed by melting a parent metal and reacting the molten parent metal with an oxidant to form oxidation reaction product and progressively drawing molten metal through the oxidation reaction product toward the oxidant and said at least one filler material so that oxidation reaction product continues to form within said mass of filler material at an interface between the oxidant and previously formed oxidation reaction product and continuing said reaction for a time sufficient to infiltrate at least a portion of said mass of filler material; and (b) disposing a second polycrystalline ceramic component in at least a portion of said porosity to form a ceramic composite product containing said second polycrystalline ceramic component.
Claim 2
Independent Claim
162 words
A method of producing a self-supporting ceramic composite product comprising the steps of: (a) forming a self-supporting ceramic composite body comprising a ceramic matrix of an oxidation reaction product embedding at least one filler material, said self-supporting ceramic composite body exhibiting at least some interconnected porosity and being formed by melting a parent metal and reacting the molten parent metal with an oxidant to form oxidation reaction product and progressively drawing molten metal through the oxidation reaction product toward the oxidant and said at least one filler material so that oxidation reaction product continues to form within said mass of filler material at an interface between the oxidant and previously formed oxidation reaction product and continuing said reaction for a time sufficient to infiltrate at least a portion of said mass of filler material; and (b) disposing a second polycrystalline ceramic component in at least a portion of said porosity to form a ceramic composite product containing said second polycrystalline ceramic component.
Claim 3
Independent Claim
210 words
A method of producing a self-supporting ceramic composite product comprising the steps of: (a) forming a self-supporting ceramic composite body comprising a ceramic matrix of an oxidation reaction product embedding at least one filler material, said self-supporting ceramic composite body exhibiting at least some interconnected porosity and being formed by melting a parent metal and reacting the molten parent metal with an oxidant to form oxidation reaction product and progressively drawing molten metal through the oxidation reaction product toward the oxidant and said at least one filer material so that oxidation reaction product continues to form within said mass of filler material at an interface between the oxidant and previously formed oxidation reaction product and continuing said reaction for a time sufficient to infiltrate at least a portion of said mass of filler material; (b) disposing a precursor material which is capable of forming a second polycrystalline ceramic component into at least a portion of said porosity by contacting said precursor material with said porosity, said precursor material being capable of infiltrating at least a portion of said interconnected porosity; and (c) infiltrating at least a portion of said interconnected porosity with said precursor material and effecting formation of said second polycrystalline ceramic component to form a ceramic composite product.
Claim 4
Independent Claim
210 words
A method of producing a self-supporting ceramic composite product comprising the steps of: (a) forming a self-supporting ceramic composite body comprising a ceramic matrix of an oxidation reaction product embedding at least one filler material, said self-supporting ceramic composite body exhibiting at least some interconnected porosity and being formed by melting a parent metal and reacting the molten parent metal with an oxidant to form oxidation reaction product and progressively drawing molten metal through the oxidation reaction product toward the oxidant and said at least one filer material so that oxidation reaction product continues to form within said mass of filler material at an interface between the oxidant and previously formed oxidation reaction product and continuing said reaction for a time sufficient to infiltrate at least a portion of said mass of filler material; (b) disposing a precursor material which is capable of forming a second polycrystalline ceramic component into at least a portion of said porosity by contacting said precursor material with said porosity, said precursor material being capable of infiltrating at least a portion of said interconnected porosity; and (c) infiltrating at least a portion of said interconnected porosity with said precursor material and effecting formation of said second polycrystalline ceramic component to form a ceramic composite product.
Claim 5
Dependent Claim
39 words
The method of claim 1 or claim 2, wherein the interconnected porosity is formed by substantially completely exhausting said molten parent metal, thus creating interconnected porosity in at least part of the ceramic composite body formed in step "a".
Claim 6
Dependent Claim
31 words
The method of claim 3, wherein said interconnected porosity is formed by substantially completely exhausting said molten parent metal, thus creating interconnected porosity throughout substantially all of said ceramic composite body.
Claim 7
Dependent Claim
43 words
The method of claim 1 or claim 2, wherein said interconnected porosity is formed by contacting said ceramic composite body formed in step "a" with a leachant to dissolve or disperse out interconnected metal, prior to disposing said second polycrystalline ceramic component therein.
Claim 8
Dependent Claim
43 words
The method of claim 5, wherein said ceramic composite body formed in step "a" is contacted with said leachant for a time sufficient to dissolve or disperse out interconnected metal in a substantially uniform outer zone while retaining an unaffected central core zone.
Claim 9
Dependent Claim
44 words
The method of claim 5, wherein said ceramic composite body formed in step "a" is contacted with said leachant in such a way so as to cause said interconnected metal to be dissolved or dispersed out of a portion of said ceramic composite body.
Claim 10
Dependent Claim
28 words
The method of claim 1 or claim 2, wherein the parent metal comprises a metal selected from the group consisting of aluminum, silicon, titanium, tin, zirconium, and hafnium.
Claim 11
Dependent Claim
23 words
The method of claim 1 or claim 2, wherein the parent metal comprises aluminum and the polycrystalline oxidation reaction product is primarily alumina.
Claim 12
Dependent Claim
35 words
The method of claim 1 or claim 2, wherein the interconnected porosity is between about 5 to 45 percent by volume of the ceramic body before the ceramic is impregnated with said second ceramic component.
Claim 13
Dependent Claim
17 words
The method of claim 1 or claim 2, wherein said second ceramic component comprises chromia or silica.
Claim 14
Independent Claim
185 words
A method of producing a self-supporting ceramic composite body comprising the steps of: (a) forming a self-supporting ceramic composite body comprising a ceramic matrix of an oxidation reaction product embedding at least one filler material, said self-supporting ceramic composite body exhibiting at least some interconnected porosity and being formed by melting a parent metal and reacting the molten parent metal with an oxidant to form oxidation reaction product and progressively drawing molten metal through the oxidation reaction product toward the oxidant and said at least one filler material so that oxidation reaction product continues to form within said mass of filler material at an interface between the oxidant and previously formed oxidation reaction product and continuing said reaction for a time sufficient to infiltrate at least a portion of said mass of filler material; (b) contacting said ceramic composite body formed in step "a" with a leachant to remove at least some interconnected metal therefrom; and (c) infiltrating at least a portion of said interconnected porosity with said precursor material and effecting formation of said second polycrystalline ceramic component to form a ceramic composite body.
Claim 15
Independent Claim
185 words
A method of producing a self-supporting ceramic composite body comprising the steps of: (a) forming a self-supporting ceramic composite body comprising a ceramic matrix of an oxidation reaction product embedding at least one filler material, said self-supporting ceramic composite body exhibiting at least some interconnected porosity and being formed by melting a parent metal and reacting the molten parent metal with an oxidant to form oxidation reaction product and progressively drawing molten metal through the oxidation reaction product toward the oxidant and said at least one filler material so that oxidation reaction product continues to form within said mass of filler material at an interface between the oxidant and previously formed oxidation reaction product and continuing said reaction for a time sufficient to infiltrate at least a portion of said mass of filler material; (b) contacting said ceramic composite body formed in step "a" with a leachant to remove at least some interconnected metal therefrom; and (c) infiltrating at least a portion of said interconnected porosity with said precursor material and effecting formation of said second polycrystalline ceramic component to form a ceramic composite body.
References Cited (Backward Citations)
US2741822A
Cited
US3255027A
Cited
US3298842A
Cited
US3296002A
Cited
US3419404A
Cited
US3473987A
Cited
US3421863A
Cited
US3437468A
Cited
US3789096A
Cited
US3473938A
Cited
US3538231A
Cited
US3864154A
Cited
US3973977A
Cited
EP0116809A1
Cited
EP0169067A2
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-02-21 | 1992-08-22 | 1993-02-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-02-21 | 1996-08-22 | 1997-02-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-02-21 | 2000-08-22 | 2001-02-21 | $7700.00 | Window Closed / Lapsed |