Process for manufacturing aggregate from ash residue

Claim 2

A process for manufacturing aggregate from ash residue, comprising the steps of: (a) comminuting the ash residue to create an average particle size and a particle size distribution approximating that which is desired for the final aggregate; (b) adding a heavy metal immobilizing agent and a volumetric stabilizing agent to the ash residue; (c) adding sufficient water for effectively mixing and reacting said heavy metal immobilizing agent and said volumetric stabilizing agent with the ash residue; (d) mixing said heavy metal immobilizing agent, said volumetric stabilizing agent and said water with the ash residue; (e) retaining the resulting mixture of said heavy metal immobilizing agent, said volumetric stabilizing agent, said water and the ash residue for sufficient time to allow the immobilizing and stabilizing reactions to occur and weak agglomerations to form; and (f) breaking up said weak agglomerations into individual particles before a solid mass is formed.

Claim 3

A process for manufacturing aggregate as recited in claim 1, wherein said heavy metal immobilizing agent is an alkaline material.

Claim 4

A process for manufacturing aggregate as recited in claim 1, wherein said heavy metal immobilizing agent is either Portland cement, lime, gypsum, caustic soda, magnesium oxide or sodium hydroxide.

Claim 5

A process for manufacturing aggregate as recited in claim 1, wherein said heavy metal immobilizing agent is Portland cement.

Claim 6

A process for manufacturing aggregate as recited in claim 4, wherein said Portland cement is added in amounts of approximately four percent to five percent by weight.

Claim 7

A process for manufacturing aggregate as recited in claim 1, wherein said volumetric stabilizing agent is a silicate bearing material.

Claim 8

A process for manufacturing aggregate as recited in claim 1, wherein said volumetric stabilizing agent is either Portland cement or sodium silicate.

Claim 9

A process for manufacturing aggregate as recited in claim 1, wherein said volumetric stabilizing material is Portland cement.

Claim 10

A process for manufacturing aggregate as recited in claim 8, wherein said Portland cement is added in amounts of at least approximately three percent by weight.

Claim 11

A process for manufacturing aggregate as recited in claim 1, wherein said heavy metal immobilizing agent and said volumetric stabilizing agent are both Portland cement.

Claim 12

A process for manufacturing aggregate as recited in claim 10, wherein said Portland cement is added in a total amount of approximately four percent to five percent by weight.

Claim 13

A process for manufacturing aggregate as recited in claim 11, wherein the resulting mixture of said Portland cement, said water and the ash residue is retained for approximately twelve hours to eighteen hours to allow the immobilizing and stabilizing reactions to occur and weak agglomerations to form.

Claim 14

A process for manufacturing aggregate from the bottom ash and fly ash residues resulting from incineration of municipal solid waste comprising the steps of: (a) quenching the bottom ash residue in water immediately following its discharge from an incinerator; (b) adding the fly ash residue discharged from a combustion gas cleaning means to the quenched bottom ash residue; (c) screening the bottom ash residue and the fly ash residue to remove oversized material; (d) mixing the bottom ash residue and the fly ash residue to form a combined ash residue; (e) magnetically removing ferrous metal from said combined ash residue; (f) comminuting said combined ash residue to create an average particle size and a particle size distribution approximating that which is desired for the final aggregate; (g) adding a heavy metal immobilizing agent and a volumetric stabilizing agent to said combined residue; (h) adding sufficient water for effectively mixing and reacting said heavy metal immobilizing agent and said volumetric stabilizing agent with said combined ash residue; (i) mixing said heavy metal immobilizing agent, said volumetric stabilizing agent and said water with said combined ash residue; (j) retaining the resulting mixture of said heavy metal immobilizing agent, said volumetric stabilizing agent, said water and said combined ash residue for sufficient time to allow the immobilizing and stabilizing reactions to occur and weak agglomerations to form; and (k) breaking up said weak agglomerations into individual particles before a solid mass is formed.

Claim 15

A process for manufacturing aggregate from the bottom ash and fly ash residues resulting from incineration of municipal solid waste comprising the steps of: (a) quenching the bottom ash residue in water immediately following its discharge from an incinerator; (b) adding the fly ash residue discharged from a combustion gas cleaning means to the quenched bottom ash residue; (c) screening the bottom ash residue and the fly ash residue to remove oversized material; (d) mixing the bottom ash residue and the fly ash residue to form a combined ash residue; (e) magnetically removing ferrous metal from said combined ash residue; (f) comminuting said combined ash residue to create an average particle size and a particle size distribution approximating that which is desired for the final aggregate; (g) adding a heavy metal immobilizing agent and a volumetric stabilizing agent to said combined residue; (h) adding sufficient water for effectively mixing and reacting said heavy metal immobilizing agent and said volumetric stabilizing agent with said combined ash residue; (i) mixing said heavy metal immobilizing agent, said volumetric stabilizing agent and said water with said combined ash residue; (j) retaining the resulting mixture of said heavy metal immobilizing agent, said volumetric stabilizing agent, said water and said combined ash residue for sufficient time to allow the immobilizing and stabilizing reactions to occur and weak agglomerations to form; and (k) breaking up said weak agglomerations into individual particles before a solid mass is formed.

Claim 16

A process for manufacturing aggregate as recited in claim 13, wherein said heavy metal immobilizing agent is an alkaline material.

Claim 17

A process for manufacturing aggregate as recited in claim 13, wherein said heavy metal immobilizing agent is either Portland cement, lime, gypsum, caustic soda, magnesium oxide or sodium hydroxide.

Claim 18

A process for manufacturing aggregate as recited in claim 13, wherein said heavy metal immobilizing agent is Portland cement.

Claim 19

A process for manufacturing aggregate as recited in claim 16, wherein said Portland cement is added in amounts of approximately four percent to five percent by weight.

Claim 20

A process for manufacturing aggregate as recited in claim 13, wherein said volumetric stabilizing agent is a silicate bearing material.

Claim 21

A process for manufacturing aggregate as recited in claim 13, wherein said volumetric stabilizing agent is either Portland cement or sodium silicate.

Claim 22

A process for manufacturing aggregate as recited in claim 13, wherein said volumetric stabilizing agent is Portland cement.

Claim 23

A process for manufacturing aggregate as recited in claim 20, wherein said Portland cement is added in amounts of at least approximately three percent by weight.

Claim 24

A process for manufacturing aggregate as recited in claim 13, wherein said heavy metal immobilizing agent and said volumetric stabilizing agent are both Portland cement.

Claim 25

A process for manufacturing aggregate as recited in claim 22, wherein said Portland cement is added in a total amount of approximately four percent to five percent by weight.

Claim 26

A process for manufacturing aggregate as recited in claim 23, wherein the resulting mixture of said Portland cement, said water and said combined ash residue is retained for approximately twelve hours to eighteen hours to allow the immobilizing and stabilizing reactions to occur and weak agglomerations to form.