Claim 1

Independent Claim 97 words

A method for bonding two surfaces together without applying heat, the bond being formed via a metal matrix that is created when the two surfaces, having been prepared so that both surfaces have an outermost layer of aluminum, are brought into contact with each other in a manner so as to displace any aluminum oxide present, thus providing the contact of two virgin (non-oxidized) aluminum surfaces, wherein one of the surfaces to be bonded is prepared so that, at desired bonding points, aluminum coated particles protrude from the surface, providing discrete contact points with the other surface.

Claim 2

Independent Claim 97 words

A method for bonding two surfaces together without applying heat, the bond being formed via a metal matrix that is created when the two surfaces, having been prepared so that both surfaces have an outermost layer of aluminum, are brought into contact with each other in a manner so as to displace any aluminum oxide present, thus providing the contact of two virgin (non-oxidized) aluminum surfaces, wherein one of the surfaces to be bonded is prepared so that, at desired bonding points, aluminum coated particles protrude from the surface, providing discrete contact points with the other surface.

Claim 3

Dependent Claim 30 words

The method of claim 1 wherein: said particles pierce the surface of the aluminum and cause any oxide layer present to be displaced so that virgin aluminum surfaces are exposed.

Claim 4

Dependent Claim 12 words

The method of claim 2 wherein: said particles are industrial grade diamonds.

Claim 5

Dependent Claim 18 words

The method of claim 2 wherein: said particles are chosen from the class of alumina, quartz, and borosilicate.

Claim 6

Dependent Claim 36 words

The method of claim 2 wherein: the strength of the bond formed is variable and is controlled by the depth of piercing and size of said particle, and hence the surface area of virgin aluminum exposed.

Claim 7

Dependent Claim 27 words

The method of claim 2 wherein: the surfaces are prepared by applying various metal layers through photolithographic or metal addition processes, the outermost layer necessarily being aluminum.

Claim 8

Dependent Claim 39 words

The method of claim 6 wherein: a breakaway layer is provided on one of the surfaces, the breakaway layer being formed from a material chosen so as to have the lowest melting point of any of the metal layers.

Claim 9

Dependent Claim 34 words

The method of claim 2 wherein: the material for the particles may be chosen so as to be both electrically and thermally conductive, either electrically or thermally conductive, or both electrically and thermally insulative.

Claim 10

Independent Claim 93 words

A method for die/package interconnect bonding, the bond being a metal matrix formed between an outer layer of virgin aluminum on the die and an outer layer of virgin aluminum on a bond pad of the package, wherein the package is formed to include a plurality of metalized particles protruding from its surface at the desired bonding spots so that when the die and package are brought together, said particles first contact the bond pad and displace any aluminum oxide that may be present, thus providing the mating of two virgin aluminum surfaces.

Claim 11

Independent Claim 93 words

A method for die/package interconnect bonding, the bond being a metal matrix formed between an outer layer of virgin aluminum on the die and an outer layer of virgin aluminum on a bond pad of the package, wherein the package is formed to include a plurality of metalized particles protruding from its surface at the desired bonding spots so that when the die and package are brought together, said particles first contact the bond pad and displace any aluminum oxide that may be present, thus providing the mating of two virgin aluminum surfaces.

Claim 12

Dependent Claim 29 words

The method of claim 9 wherein: the material to be used for said particles is chosen so as to control the electrical and/or thermal conductivity of the interconnect bond.

Claim 13

Dependent Claim 30 words

The method of claim 9 wherein: the strength of the interconnect bond is controlled by the depth of piercing and size of the particles and choice of exterior metal layer.

Claim 14

Dependent Claim 49 words

The method of claim 9 wherein: a breakaway layer is provided on the die, the breakaway layer being a material with a melting point lower than that of the other materials present on the die, so that when heat is applied, the bond is broken at the breakaway layer.

Claim 15

Dependent Claim 24 words

The method of claim 9 wherein: the material for the particles is either industrial diamond or from the class of alumina, quartz, and borosilicate.

Claim 16

Independent Claim 147 words

A method for bonding together a first generally locally planar surface and a second generally locally planar surface, in steps comprising: A. coating the first surface with a first layer of aluminum; B. coating the second surface with a second layer of aluminum including a plurality of discrete particles embedded therein at selected bonding zones, said discrete particles being completely coated, on the exterior facing surfaces thereof, by said second layer of aluminum; and C. forcing the first surface against the second surface in a perpendicular manner such that said particles embedded in said second layer of aluminum pierce both said second layer and said first layer of aluminum, the force of such piercing exposing juxtaposed areas of virgin aluminum in both of said first and said second layers, such that adjacent exposed areas of virgin aluminum are caused to bond to each other by material affinity.

Claim 17

Independent Claim 147 words

A method for bonding together a first generally locally planar surface and a second generally locally planar surface, in steps comprising: A. coating the first surface with a first layer of aluminum; B. coating the second surface with a second layer of aluminum including a plurality of discrete particles embedded therein at selected bonding zones, said discrete particles being completely coated, on the exterior facing surfaces thereof, by said second layer of aluminum; and C. forcing the first surface against the second surface in a perpendicular manner such that said particles embedded in said second layer of aluminum pierce both said second layer and said first layer of aluminum, the force of such piercing exposing juxtaposed areas of virgin aluminum in both of said first and said second layers, such that adjacent exposed areas of virgin aluminum are caused to bond to each other by material affinity.

Claim 18

Dependent Claim 20 words

The method of claim 14 wherein said particles are selected to be multifaceted such that said piercing displaces maximal aluminum.

Claim 19

Dependent Claim 44 words

The method of claim 14 wherein a light amount of force is utilized in step C, such that the degree of said piercing is slight and disengagement of the bond may be accomplished with slight detriment to said first and said second aluminum layers.

Claim 20

Dependent Claim 57 words

The method of claim 16 and further including the following steps: D. inspecting/testing the juxtapositional alignment of the first and second surfaces to assure that desired alignment has been achieved; and E. repeating step C with a greater amount of force such that a greater degree of piercing is achieved and a more permanent bond is formed.

Claim 21

Dependent Claim 52 words

The method of claim 14 wherein: said particles are selected to be irregular solids having effective diameters less than the sum of the thicknesses of said first layer of aluminum and said second layer of aluminum, thus assuring said particles do not pierce the first and second surfaces and cause detriment thereto.

Annuity Stage	Window Opens	Payment Deadline	Surcharge Period Until	Estimated Fee	Status
3.5 Years (Year 4)	1992-02-14	1992-08-15	1993-02-14	$2000.00	Window Closed / Lapsed
7.5 Years (Year 8)	1996-02-14	1996-08-15	1997-02-14	$3760.00	Window Closed / Lapsed
11.5 Years (Year 12)	2000-02-14	2000-08-15	2001-02-14	$7700.00	Window Closed / Lapsed

Method for cold bonding