Method of making multilayer composite hollow fibers
Assignee: Mitsubishi Chemical Corp
•
Filing: 1987-09-01
•
Granted: 1989-02-07
•
Expires: 2007-09-01
Abstract
Abstract Disclosed are a multilayer composite hollow fiber comprising at least one nonporous separating membrane layer (A) performing a separating function and two or more porous layers (B) performing a reinforcing function, the layer (A) and the layers (B) being alternately laminated so as to give a structure having internal and external surfaces formed by the porous layers (B), as well as a method of making such a hollow fiber. In this multilayer composite hollow fiber, the separating membrane can be formed as an ultrathin, homogeneous membrane. Moreover, the separating membrane is not liable to get damaged owing to the unique structure of the hollow fiber. Furthermore, such hollow fibers can be readily and stably produced on an industrial scale.
Inventors
- 👤 Tohru Takemura
- 👤 Hajime Itoh
- 👤 Jun Kamo
- 👤 Haruhiko Yoshida
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 04:19
CPC Classifications
D; D01; D01D; D01D5/00; D01D5/24; B; B01; B01D; B01D67/00; B01D67/0002; B01D67/0023; B01D67/0025; B01D67/0027; B01D69/00; B01D69/08; B01D69/12; B01D69/1213; B01D69/1216; B01D2323/00; B01D2323/08; B01D2323/081; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2913; Y10T428/2929; Y10T428/2933; Y10T428/2935; Y10T428/2973; Y10T428/2975
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
182 words
A method of making a multilayer composite hollow fiber comprising (A) at least one nonporous separating membrane layer which performs a separating function and (B) at least two porous layers which perform a reinforcing function, said layer (A) and said layers (B) being alternately laminated together so as to give a structure having inner and outer surfaces formed by said layers (B), comprising the steps of: (i) co-spinning a polymer (A') selected from the group consisting of (a) a non-crystalline polymer, (b) a crystalline polymer having a lower melting point than polymer (B'), (C) a crystalline polymer having a melt index greater than the melt index of polymer (B') and (d) a crystalline polymer containing a solvent or plasticizer which forms said separating membrane layer and a crystalline polymer (B') which forms said porous layers through a spinning nozzle of multiple tubular construction which sandwiches the spun polymer (A') between two layers of the spun polymer (B'), thereby forming a composite hollow fiber; and (ii) stretching the resulting hollow fiber thereby imparting porosity to said layers (B) while leaving layer (A) non-porous.
Claim 2
Independent Claim
182 words
A method of making a multilayer composite hollow fiber comprising (A) at least one nonporous separating membrane layer which performs a separating function and (B) at least two porous layers which perform a reinforcing function, said layer (A) and said layers (B) being alternately laminated together so as to give a structure having inner and outer surfaces formed by said layers (B), comprising the steps of: (i) co-spinning a polymer (A') selected from the group consisting of (a) a non-crystalline polymer, (b) a crystalline polymer having a lower melting point than polymer (B'), (C) a crystalline polymer having a melt index greater than the melt index of polymer (B') and (d) a crystalline polymer containing a solvent or plasticizer which forms said separating membrane layer and a crystalline polymer (B') which forms said porous layers through a spinning nozzle of multiple tubular construction which sandwiches the spun polymer (A') between two layers of the spun polymer (B'), thereby forming a composite hollow fiber; and (ii) stretching the resulting hollow fiber thereby imparting porosity to said layers (B) while leaving layer (A) non-porous.
Claim 3
Dependent Claim
29 words
The method of claim 1, wherein the spinning temperature ranges from the melting point of the polymer (B') to a temperature about 80° C. higher than said melting point.
Claim 4
Dependent Claim
15 words
The method of claim 1, wherein the spinning draw ratio is not less than 30.
Claim 5
Dependent Claim
31 words
The method of claim 1, wherein the hollow fiber of step (i) is annealed at a temperature ranging from the glass transition point to the melting point of the polymer (B').
Claim 6
Dependent Claim
106 words
The method of claim 1, wherein the stretching of said composite hollow fiber of step (i) is carried out in two steps of: (1) cold-stretching the composite hollow fiber of step (i) at a stretching ratio of about 5 to 150% at a temperature ranging from 0° C. to a temperature of 50° C. lower than the melting point of the polymer (B') so as to create microcrazes in the layers (B) consisting of the polymer (B'), and (2) hot-stretching the hollow fiber through at least one stage at a temperature higher than the cold-stretching temperature and lower than the melting point of the polymer (B').
References Cited (Backward Citations)
US4267047A
Cited
US4230463A
Cited
US4214020A
Cited
US4317729A
Cited
US4243701A
Cited
US4470831A
Cited
US4405688A
Cited
US4421529A
Cited
US4666469A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-02-07 | 1992-08-08 | 1993-02-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-02-07 | 1996-08-08 | 1997-02-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-02-07 | 2000-08-08 | 2001-02-07 | $7700.00 | Window Closed / Lapsed |