Assignee: Societe Anonyme de Telecommunications SAT
•
Filing: 1987-05-01
•
Granted: 1989-01-31
•
Expires: 2007-05-01
Abstract
Abstract An HgCdTe avalanche photodiode for use at ambient temperature comprises an Hg1-xCdxTe crystal substrate in which x is chosen between substantially 0.35 and substantially 0.5, a PN junction is formed in the substrate with low concentrations in the vicinity of the junction, by impurity penetration from a polished and chemically etched surface and the P zone is illuminated. A guard band is provided around the PN junction. The dark current of the photodiode is less than 0.1 ANGSTROM /cm2 at ambient temperature and the excess noise factor is less than 0.4. The photodiode of the invention is used for detecting signals transmitted along fluorated glass optical fibers, for example.
Inventors
- 👤 Yves Carpentier
- 👤 Michel Royer
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 02:56
CPC Classifications
H; H10; H10F; H10F30/00; H10F30/20; H10F30/21; H10F30/22; H10F30/225; H10D; H10D64/00; H10D64/01; H10D64/011; H10F30/221; H10F30/2212; H10F77/00; H10F77/10; H10F77/12; H10F77/123; H10F77/1237; H10P; H10P30/00; H10P30/20; H10P30/202; H10P30/21; H10P30/22; H10P30/28; H10P32/00; H10P32/10; H10P32/12; H10P32/17; H10P50/00; H10P50/20; H10P52/00; H10P95/00; H10P95/70
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
140 words
A photodiode for use under avalanche operating conditions at ambient temperature comprising: a substrate formed of a Hg 1-x Cd x Te crystal, wherein a molar fraction x is between substantially 0.35 and substantially 0.5; an N conductivity zone formed in said substrate and having an N carrier concentration less than or equal to 2.10 15 /cm3; a P conductivity zone formed in said substrate and having a P carrier concentration less than or equal to 10 16 /cm3, said P conductivity zone receiving radiation to be detected; a PN junction formed at a boundary of said P and N conductivity zones, said PN junction being formed by penetration of impurities from a polished and chemically etched surface of said substrate; a guard band provided in said substrate and surrounding said PN junction and said photodiode exhibiting an avalanche phenomenon.
Claim 2
Dependent Claim
140 words
A photodiode for use under avalanche operating conditions at ambient temperature comprising: a substrate formed of a Hg 1-x Cd x Te crystal, wherein a molar fraction x is between substantially 0.35 and substantially 0.5; an N conductivity zone formed in said substrate and having an N carrier concentration less than or equal to 2.10 15 /cm3; a P conductivity zone formed in said substrate and having a P carrier concentration less than or equal to 10 16 /cm3, said P conductivity zone receiving radiation to be detected; a PN junction formed at a boundary of said P and N conductivity zones, said PN junction being formed by penetration of impurities from a polished and chemically etched surface of said substrate; a guard band provided in said substrate and surrounding said PN junction and said photodiode exhibiting an avalanche phenomenon.
Claim 3
Dependent Claim
40 words
The photodiode as claimed in claim 1, wherein: the N zone has an N carrier concentration greater than or equal to 5.10 14 /cm3, the P zone has a P carrier concentration greater than or equal to 10 15 /cm3.
Claim 4
Dependent Claim
62 words
The photodiode as claimed in claim 1, wherein said surface is subjected to the following polishing and chemical etching treatments: polishing with alumina of a grain size of 0.02 μm for one hour, mecano-chemical polishing with alumina having a grain size of 0.02 μm in a solution of 25 g/l of CrO 3 for an hour, and chemical etching with hydrochloric acid.
Claim 5
Dependent Claim
42 words
The photodiode as claimed in claim 1, including a stacked pair of masking and passivation layers on said substrate surface, each pair including a first layer of CdTe and a second layer of one of the materials ZnS and SiO 2 .
Claim 6
Dependent Claim
26 words
The photodiode as claimed in claim 1, wherein the Hg 1-x Cd x Te crystal is a solid crystal obtained by the Travelling Heater Method (THM).
Claim 7
Dependent Claim
31 words
The photodiode as claimed in claim 5, wherein said surface is subjected, before polishing and chemical etching, to prepolishing with alumina of a grain size of 0.3 μm for an hour.
Claim 8
Dependent Claim
29 words
The photodiode as claimed in claim 5, wherein the N zone is obtained by subjecting the crystal to a temperature of 300° C. under a saturating mercury vapor pressure.
Claim 9
Dependent Claim
26 words
The photodiode as claimed in claim 5, wherein the P zone is obtained by diffusion of gold under a saturating mercury vapor pressure at 300° C.
Claim 10
Dependent Claim
25 words
The photodiode as claimed in claim 1, wherein the Hg 1-x Cd x Te crystal is a crystal obtained by epitaxy from a semiconductor substrate.
Claim 11
Dependent Claim
20 words
The photodiode as claimed in claim 9, wherein the N zone is obtained by ionic implantation of Al 2+ ions.
References Cited (Backward Citations)
US4137544A
Cited
US4208003A
Cited
EP0045258A2
Cited
EP0045558A1
Cited
EP0060743A1
Cited
GB2138209A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-01-31 | 1992-08-01 | 1993-01-31 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-01-31 | 1996-08-01 | 1997-01-31 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-01-31 | 2000-08-01 | 2001-01-31 | $7700.00 | Window Closed / Lapsed |