Abstract The present invention relates to a novel crystalline massive aluminosilicate with an expanded structure and to its process of manufacture. The particular structure is a closed cell structure containing nitrogen. It is obtained by: grinding industrial glass; adding aluminum based nitride in the proportion of 0.1 to 20% by weight with respect to the weight of the ground industrial glass; mixing the ground glass and so-added nitride; oxidizing the nitride within said mixture by heating to a temperature of 800 DEG to 1000 DEG C. for about 1 hour, and cooling and recovering the expanded crystalline aluminosilicate. The material has multiple applications in the building industry and in the construction of furnaces, in the manufacture of fireproof walls and doors, and in naval construction, with various advantages over prior art materials.
A massive partially crystalline aluminosilicate material comprising a plurality of expanded closed cell structures containing nitrogen gas.
Claim 2
Dependent Claim
17 words
A massive partially crystalline aluminosilicate material comprising a plurality of expanded closed cell structures containing nitrogen gas.
Claim 3
Dependent Claim
20 words
A massive aluminosilicate according to claim 1, the apparent density whereof is comprised between 200 and 700 kg/m 3 .
Claim 4
Dependent Claim
18 words
A massive aluminosilicate according to claim 1 whose coefficient of thermal insulation γ is approximately 0.07 W/m C.
Claim 5
Dependent Claim
17 words
A massive aluminosilicate according to claim 1, whose thermal diffusivity is approximately 3×10 -3 cm 2 /S.
Claim 6
Dependent Claim
17 words
A massive aluminosilicate according to claim 1, whose compressive strength is higher than about 3×10 6 Pa.
Claim 7
Dependent Claim
27 words
A massive aluminosilicate according to claim 1, whose coefficient of thermal expansion measured between 20° and 500° C. is equal to about 7.4×10 -6 °K. -1 .