Oxidation resistant ferrous base foil
Assignee: Armco Inc
•
Filing: 1987-05-08
•
Granted: 1989-01-10
•
Expires: 2007-05-08
Abstract
Abstract Aluminum coated ferritic base metal foil formed by cold reduction of hot dip aluminum coated ferritic steel strip containing from 10% to about 35% chromium, up to 3% aluminum, and up to 1% silicon, the foil having a ratio of aluminum coating thickness on both sides to base metal foil thickness of at least 1:10, with at least 4% by weight total aluminum. The method of production includes heating the foil in an oxidizing atmosphere within specified temperature and time limitations to provide a porous surface having a thin layer of aluminum oxide. The foil is adapted for fabrication into monolithic support structures for catalytic converters for internal combustion engine exhaust systems.
Inventors
- 👤 Farrell M. Kilbane
- 👤 F. Curtiss Dunbar
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 12:50
CPC Classifications
C; C23; C23C; C23C2/00; C23C2/04; C23C2/12; C23C2/26; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12493; Y10T428/12535; Y10T428/12542; Y10T428/12549; Y10T428/12583; Y10T428/1259; Y10T428/12736; Y10T428/1275; Y10T428/12757
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
160 words
A monolithic support structure for catalytic converters for internal combustion engine exhaust systems, comprising an aluminum coated ferrous base metal foil having a thickness not greater than 0.13 mm formed by cold reduction of a hot dip substantially pure aluminum coated ferritic base metal strip containing from 10% to about 35% by weight chromium, up to 3% aluminum, up to 1% silicon, and balance essentially iron, said ferritic base metal strip having a thickness of at least 0.25 mm and an aluminum coating thickness ranging from 0.013 to 0.13 mm on each side, said coated foil having a ratio of total aluminum coating thickness to base metal foil thickness of at least 1:10, with at least 4% by weight total aluminum in said coated foil, said coated foil being further provided with an aluminum oxide layer on each side ranging in thickness from about 500 to about 10,000 angstroms, and a washcoat of a heat resistant, ceramic catalyst support material.
Claim 2
Dependent Claim
160 words
A monolithic support structure for catalytic converters for internal combustion engine exhaust systems, comprising an aluminum coated ferrous base metal foil having a thickness not greater than 0.13 mm formed by cold reduction of a hot dip substantially pure aluminum coated ferritic base metal strip containing from 10% to about 35% by weight chromium, up to 3% aluminum, up to 1% silicon, and balance essentially iron, said ferritic base metal strip having a thickness of at least 0.25 mm and an aluminum coating thickness ranging from 0.013 to 0.13 mm on each side, said coated foil having a ratio of total aluminum coating thickness to base metal foil thickness of at least 1:10, with at least 4% by weight total aluminum in said coated foil, said coated foil being further provided with an aluminum oxide layer on each side ranging in thickness from about 500 to about 10,000 angstroms, and a washcoat of a heat resistant, ceramic catalyst support material.
Claim 3
Dependent Claim
28 words
A support structure as claimed in claim 1, wherein said ferritic base metal strip contains from about 10.0% to about 14.5% chromium and about 0.1% to 1.0% silicon.
Claim 4
Dependent Claim
34 words
A support structure as claimed in claim 1, wherein said heat resistant catalyst support material is chosen from the group consisting of gamma aluminum oxide, alkaline earth metal oxides, scandium oxide, and yttrium oxide.
Claim 5
Dependent Claim
26 words
A support structure as claimed in claim 3, including a catalyst on said washcoat chosen from the group consisting of platinum, rhodium, palladium and mixtures thereof.
References Cited (Backward Citations)
US2170361A
Cited
US3059326A
Cited
US3214820A
Cited
US3867313A
Cited
JPS4999982A
Cited
US4188309A
Cited
US4414023A
Cited
US4601999A
Cited
US4624895A
Cited
US4686155A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-01-10 | 1992-07-11 | 1993-01-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-01-10 | 1996-07-11 | 1997-01-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-01-10 | 2000-07-11 | 2001-01-10 | $7700.00 | Window Closed / Lapsed |