Oxidation resistant ferrous base foil and method therefor
Assignee: Armco Inc
•
Filing: 1985-06-04
•
Granted: 1987-08-11
•
Expires: 2005-06-04
Abstract
Abstract Aluminum coated ferritic base metal foil formed by cold reduction of hot dip aluminum coated ferritic steel strip containing from 10% to about 35% chormium, up to 3% aluminum, and up to 1% silicon, the foil having a ratio of aluminum coating thickness on both sides to base metal foil thickness of at least 1:10, which at least 4% by weight total aluminum. The method of production includes heating the foil in an oxidizing atmosphere within specified temperature and time limitations to provide a porous surface having a thin layer of aluminum oxide. The foil is adapted for fabrication into monolithic support structures for catalytic converters for internal combustion engine exhaust systems.
Inventors
- 👤 Farrell M. Kilbane
- 👤 F. Curtiss Dunbar
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 13:06
CPC Classifications
C; C23; C23C; C23C2/00; C23C2/04; C23C2/12; C23C2/26; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12493; Y10T428/12535; Y10T428/12542; Y10T428/12549; Y10T428/12583; Y10T428/1259; Y10T428/12736; Y10T428/1275; Y10T428/12757
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
122 words
Aluminum coated ferrous base metal foil having a thickness not greater than 0.13 mm formed by cold reduction of a hot dip aluminum coated ferritic base metal strip containing from 10% to about 35% by weight chromium, up to 3% aluminum, up to 1% silicon, and balance essentially iron, said ferritic base metal strip having a thickness of at least 0.25 mm and an aluminum coating thickness ranging from 0.013 to 0.13 mm on each side, said coated foil having a ratio of total aluminum coating thickness to base metal foil thickness of at least 1:10, with at least 4% by weight total aluminum in said coated foil, said coated foil exhibiting improved high temperature oxidation resistance and improved wet corrosion resistance.
Claim 2
Dependent Claim
122 words
Aluminum coated ferrous base metal foil having a thickness not greater than 0.13 mm formed by cold reduction of a hot dip aluminum coated ferritic base metal strip containing from 10% to about 35% by weight chromium, up to 3% aluminum, up to 1% silicon, and balance essentially iron, said ferritic base metal strip having a thickness of at least 0.25 mm and an aluminum coating thickness ranging from 0.013 to 0.13 mm on each side, said coated foil having a ratio of total aluminum coating thickness to base metal foil thickness of at least 1:10, with at least 4% by weight total aluminum in said coated foil, said coated foil exhibiting improved high temperature oxidation resistance and improved wet corrosion resistance.
Claim 3
Dependent Claim
46 words
The coated foil claimed in claim 1, including an aluminum oxide layer ranging in thickness from about 500 to about 10,000 angstroms on each surface of said foil, said layer being adapted to bond securely to a wash coat of a heat resistant catalyst support material.
Claim 4
Dependent Claim
55 words
The coated foil claimed in claim 1, wherein said strip has a thickness of about 0.4 to about 1.0 mm, said aluminum coating has a thickness of about 0.04 to about 0.10 mm on each side before said cold reduction, and wherein said coated foil has a thickness of about 0.04 to about 0.10 mm.
Claim 5
Dependent Claim
27 words
The coated foil claimed in claim 1, wherein said ferritic base metal strip contains from about 10.0% to about 14.5% chromium and about 0.1% to 0.1% silicon.
Claim 6
Dependent Claim
21 words
The coated foil claimed in claim 4, wherein said ferritic base metal strip contains from about 0.5% to about 1.0% aluminum.
Claim 7
Dependent Claim
37 words
The coated foil claimed in claim 1, wherein said ferritic base metal strip contains residual amounts of aluminum, and wherein from 4% to about 30% by weight total aluminum is at the surfaces of said coated foil.
Claim 8
Dependent Claim
37 words
The coated foil claimed in claim 2, wherein said ferritic base metal strip contains residual amounts of aluminum, and wherein from 4% to about 30% by weight total aluminum is at the surfaces of said coated foil.
Claim 9
Dependent Claim
31 words
The coated foil claimed in claim 2, wherein said heat resistant catalyst support material is at least one of gamma aluminum oxide, alkaline earth metal oxides, scandium oxide, and yttrium oxide.
Claim 10
Dependent Claim
40 words
The coated foil claimed in claim 4, wherein the composition of said ferritic base metal strip is based on the intended operating temperature of said foil in accordance with the formula: Operating temperature (° C.)=15 [% Cr+1.5×% Si+3×% Al]+800° C.
References Cited (Backward Citations)
US2170361A
Cited
US3059326A
Cited
US3214820A
Cited
US3867313A
Cited
JPS499982A
Cited
US4188309A
Cited
US4414023A
Cited
US4624895A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-08-10 | 1991-02-09 | 1991-08-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-08-10 | 1995-02-09 | 1995-08-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-08-10 | 1999-02-09 | 1999-08-11 | $7700.00 | Window Closed / Lapsed |