US4797316A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Etched glass and process of manufacturing same
Assignee: AGC Glass Europe SA
•
Filing: 1987-12-04
•
Granted: 1989-01-10
•
Expires: 2007-12-04
Abstract
Abstract The invention relates to an article comprising a glass sheet and having an etched pattern, and to a process of manufacturing an article comprising a glass sheet and having an etched pattern. The glass sheet 11 is a chemically tempered glass sheet, and the pattern comprises one or more grooves 10 etched into the article using fluorine ions to a depth of less than 2 μm. The etched grooves 10 constituting the pattern may be formed in a layer 12 of inorganic material such as SiO 2 . They may have a width of less than 10 μm and the spacing (p) between two adjacent grooves may also be less than 10 μm. The etching may be performed by applying a layer of radiation-sensitive material to at least one face of that sheet and exposing it to radiation to form a latent image of a desired groove pattern, whereafter the radiation-sensitive material is developed to form a resist and the sheet is exposed, through the resist, to the action of fluorine ions in an etching medium to etch the desired groove pattern to a depth of less than 2 μm. The invention is particularly useful for forming storage discs for recording data and also for forming panels of high optical transmittance.
Inventors
- 👤 Andre Hecq
- 👤 Rene Ledroit
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 15:24
CPC Classifications
G; G03; G03F; G03F7/00; G03F7/0005; C; C03; C03C; C03C15/00; G11; G11B; G11B7/00; G11B7/24; G11B7/241; G11B7/252; G11B7/253; G11B7/26; G11B7/261; G11B11/00; G11B11/10; G11B11/105; G11B11/10582; G11B11/10584; Y; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/24479; Y10T428/2457; Y10T428/24595
Claims Analysis
Total Claims: 61
Claim 1
Independent Claim
46 words
An article comprising a glass sheet and having an etched pattern, characterised in that said glass sheet is a chemically tempered glass sheet, and the pattern comprises one or more grooves etched into the article using fluorine ions to a depth of less than 2 μm.
Claim 2
Dependent Claim
46 words
An article comprising a glass sheet and having an etched pattern, characterised in that said glass sheet is a chemically tempered glass sheet, and the pattern comprises one or more grooves etched into the article using fluorine ions to a depth of less than 2 μm.
Claim 3
Dependent Claim
36 words
An article according to claim 1, wherein the pattern comprises closely spaced groove portions which have a width of less than 10 μm, and the spacing between two adjacent groove portions is less than 10 μm.
Claim 4
Dependent Claim
41 words
An article according to claim 2, wherein the etched groove portions have a width of less than 1.5 μm and a depth greater than 50 nm, and in that the interval between two adjacent groove portions is less than 2 μm.
Claim 5
Dependent Claim
20 words
An article according to claim 1 wherein the pattern is etched into a surface layer of the tempered glass sheet.
Claim 6
Dependent Claim
42 words
An article according to claim 1 wherein the etched groove portions are etched into a layer of inorganic material deposited on the tempered glass, which material has a hardness which is substantially equal to or greater than the hardness of the glass.
Claim 7
Dependent Claim
16 words
An article according to claim 5, wherein such inorganic layer comprises substantially a single constituent. tuent.
Claim 8
Dependent Claim
17 words
An article according to claim 6 wherein such inorganic layer is a layer of SiO 2 .
Claim 9
Dependent Claim
24 words
An article according to claim 5 wherein the depth of the etched groove portions is substantially equal to the thickness of the inorganic layer.
Claim 10
Dependent Claim
12 words
An article according to claim 1 wherein it comprises an anti-reflecting layer.
Claim 11
Dependent Claim
15 words
An article according to claim 1 wherein said glass sheet is a float glass sheet..
Claim 12
Dependent Claim
16 words
An article according to claim 1 wherein said glass sheet has a thickness below 2 mm.
Claim 13
Dependent Claim
56 words
An article according to claim 1 wherein the pattern is etched on a face of the article with grooves disposed mesh-wise to form a grid pattern, the dimension of the mesh being less than 0.5 μm, and wherein the total optical reflectance of that face within the visible region of the spectrum is less than 4%.
Claim 14
Dependent Claim
18 words
An article according to claim 12, wherein the depth of the etched grooves is greater than 0.1 μm.
Claim 15
Dependent Claim
19 words
An article according to claim 12 wherein the dimension of the mesh of the grid is below 0.1 μm.
Claim 16
Dependent Claim
23 words
An article according to claim 1 wherein the etched groove portions form a spiral guide track whose pitch is less than 2 μm.
Claim 17
Dependent Claim
26 words
An article according to claim 1 wherein etched grooves form a guide track being a series of concentric circles whose pitch is less tha 2 μm.
Claim 18
Dependent Claim
10 words
An article according to claim 15, which is a disc.
Claim 19
Dependent Claim
25 words
An article according to claim 15 wherein the bottom of said guide track possesses a rugosity Ra below 10 nm an preferably below 5 nm.
Claim 20
Dependent Claim
29 words
an article according to claim 15 wherein the sides of said guide track posses a substantially symmetrical inclination relative to an axis perpendicular to the bottom of the track.
Claim 21
Dependent Claim
17 words
A disc according to claim 17 wherein such disc is adapted for the storage of recorded data.
Claim 22
Dependent Claim
13 words
A disc according to claim 20, wherein the etched pattern is address-wise modulated.
Claim 23
Dependent Claim
17 words
A disc according to claim 20 wherein the etched pattern i sover-coated with a data recording layer.
Claim 24
Dependent Claim
13 words
A disc according to claim 20 wherein the etched pattern is data-wise modulated.
Claim 25
Dependent Claim
99 words
A process of manufacturing an article comprising a glass sheet and having an etched pattern, characterised in that a glass sheet is chemically tempered, a layer of radiation-sensitive material is applied to at least one face of that sheet and is exposed to radiation to form a latent image of a desired groove pattern, in that the radiation-sensitive material is developed to form a resist and in that the sheet is exposed, through the resist, to the action of fluorine ions in an etching medium to etch the desired groove pattern to a depth of less than 2 μm.
Claim 26
Dependent Claim
99 words
A process of manufacturing an article comprising a glass sheet and having an etched pattern, characterised in that a glass sheet is chemically tempered, a layer of radiation-sensitive material is applied to at least one face of that sheet and is exposed to radiation to form a latent image of a desired groove pattern, in that the radiation-sensitive material is developed to form a resist and in that the sheet is exposed, through the resist, to the action of fluorine ions in an etching medium to etch the desired groove pattern to a depth of less than 2 μm.
Claim 27
Dependent Claim
15 words
A process according to claim 24, applied for the manufacture of a data storage disc.
Claim 28
Dependent Claim
23 words
A process according to claim 25, wherein the groove pattern is etched to form a spiral whose pitch is less than 2 μm.
Claim 29
Dependent Claim
26 words
A process according to claim 25, wherein the groove pattern is etched to form a series of concentric circles whose pitch is less than 2 μm.
Claim 30
Dependent Claim
25 words
A process according to claim 25 wherein the bottom of the groove pattern has a rugosity Ra below 10 nm and preferably below 5 nm.
Claim 31
Dependent Claim
34 words
A process according to claim 25 wherein the etching is performed so that the sides of the groove have a substantially symmetrical inclination relative to an axis perpendicular to the bottom of the groove.
Claim 32
Dependent Claim
14 words
A process according to claim 25 wherein the etched groove pattern is address-wise modulated.
Claim 33
Dependent Claim
18 words
A process according to claim 254 wherein the etched groove pattern is over-coated with a data reocrding layer.
Claim 34
Dependent Claim
14 words
A process according to claim 25 wherein the etched groove pattern is data-wise modulated.
Claim 35
Dependent Claim
13 words
A process according to claim 24 applied for the manufacture of matted glass.
Claim 36
Dependent Claim
51 words
A process according to claim 33, wherein the sheet is etched with grooves disposed mesh-wise to form a grid pattern, the dimension of the mesh being less than 0.5 μm, and wherein the total optical reflectance of the etched face within the visible region of the spectrum is less than 4%.
Claim 37
Dependent Claim
18 words
A process according to claim 33 wherein the grooves are etched to a depth greater tha 0.1 μm.
Claim 38
Dependent Claim
19 words
A process according to claim 33 wherein the dimension of the mesh of the grid is below 0.1 μm.
Claim 39
Dependent Claim
21 words
A process according to claim 24 wherein the resist is eliminated from the substrate after the action of the etching medium.
Claim 40
Dependent Claim
41 words
A process according toe claim 24 wherein an inorganic layer is present on a face of the glass prior to the deposition of the radiation-sensitive material, and in that the material removed during etching comprises material originating from this inorganic layer.
Claim 41
Dependent Claim
26 words
A process according to claim 38, wherein the inorganic layer is deposited in a thickness substantially equal to the depth of the pattern to be eched.
Claim 42
Dependent Claim
32 words
A process according to claiam 39, wherein the action of the etching medium is stopped when the latter reaches the glass over substantially the entire area of the pattern to be etched.
Claim 43
Dependent Claim
32 words
A process according to claiam 39, wherein the action of the etching medium is stopped when the latter reaches the glass over substantially the entire area of the pattern to be etched.
Claim 44
Dependent Claim
20 words
A process according to claim 24 wherein the resist is constituted by the radiation-sensitive material after exposure to the radiation.
Claim 45
Dependent Claim
24 words
A process according to wherein the radiation-sensitive material is a photo-sensitive resin and in that the radiation comprises optical radiation and preferably ultraviolet radiation.
Claim 46
Dependent Claim
24 words
A process according to wherein the radiation-sensitive material is a photo-sensitive resin and in that the radiation comprises optical radiation and preferably ultraviolet radiation.
Claim 47
Dependent Claim
36 words
A process according to claim 42, wherein the face of the sheet opposite to that in which the pattern is to be etched is covered with an opaque layer prior to the exposure ot optical radiation.
Claim 48
Dependent Claim
27 words
A process according to claim 42 wherein the photo-sensitive resin is a resin which is transparent to optical radiation which becomes absorbent when exposed to this radiation.
Claim 49
Dependent Claim
23 words
A process according to claim 42 wherein a contrast-increasing layer is deposited on the photo-sensitive resin prior to exposure to the optical radiation.
Claim 50
Dependent Claim
40 words
A process according to claim 42 wherein the face to be etched is subjected to a lowenergy ion attack by means of an oxygen-based plasma before etching, so as substantially to expose that face over the pattern to be etched.
Claim 51
Dependent Claim
18 words
A process according to claim 24 wherein the radiation-sensitive material is exposed to said radiation through a mask.
Claim 52
Dependent Claim
48 words
A process according to claim 47 applied for the manufacture of matted glass, wherein said mask represents only a portion of the pattern to be etched, and in that various portions of the sensitive material are successively exposed through said mask in order to form said latent image.
Claim 53
Dependent Claim
18 words
A process according to claim 47 wherein the mask represents the entirety of the pattern to be etched.
Claim 54
Dependent Claim
19 words
A process according to any of claims 24 to 49 wherein the radiation is focused on the sensitive material.
Claim 55
Dependent Claim
13 words
A process according to claim 24 wherein the etching medium is a liquid.
Claim 56
Dependent Claim
16 words
A process according to claim 51, wherein the liquid etching medium also contains a polishing agent.
Claim 57
Dependent Claim
16 words
A process according to claim 24 wherein the etching medium is a plasma containing fluorine ions.
Claim 58
Dependent Claim
25 words
A process according to claim 53 wherein the energy induced into the plasma ions is less than 50 eV, and preferably less than 20 eV.
Claim 59
Dependent Claim
15 words
A process according to claim 24 wherein the glass which is tempered is float glass.
Claim 60
Dependent Claim
47 words
A process according to claim 55, wherein prior to tempering, the float glass is maintained at an elevated temperature not exceeding 550° C. to promote ionic migration within the glass and render the sodium ion population at the two faces of the float glass more nearly equal.
Claim 61
Dependent Claim
15 words
An article comprising tempered which has been etched by a process according to claim 24.
References Cited (Backward Citations)
US3817730A
Cited
US4106859A
Cited
US4046619A
Cited
US4544443A
Cited
US4655876A
Cited
US4726006A
Cited
EP0228814A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-01-10 | 1992-07-11 | 1993-01-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-01-10 | 1996-07-11 | 1997-01-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-01-10 | 2000-07-11 | 2001-01-10 | $7700.00 | Window Closed / Lapsed |