Metallized polymer compositions, processes for their preparation and their uses
Assignee: Akzo NV
•
Filing: 1986-05-08
•
Granted: 1989-01-03
•
Expires: 2006-05-08
Abstract
Abstract Metallized polymer compositions are disclosed, the surface of which comprises an intermetallic compound of a metal element A (Sn, As, Sb or Bi) and a metal element B (Fe, Co, Ni, Cu, Zn, Ga, Ru, Rh, Pd, Ag, Cd or In), preferably an intermetallic compound of antimony and a metal element B. Processes for producing such metallized polymer compositions involve either the reduction of a metal element A compound in the presence of metallic metal element B and the polymer or the compression of a laminate of metal element A and metal element B layers onto the polymer. The metallized polymers are useful in the production of printing circuit boards, electromagnetic interference shielding devices, membrane switches, capacitors, conductive fibers, magnetic tapes and disc, antistatic mats, barrier polymers and optical storage devices.
Inventors
- 👤 Boyd Cooray
- 👤 Peter Hope
- 👤 Jan Vleggaar
- 👤 Kees Helle
- 👤 Arie Roos
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 15:44
CPC Classifications
H; H05; H05K; H05K3/00; H05K3/38; H05K3/382; B; B44; B44C; B44C1/00; B44C1/10; B44C1/14; H05K1/00; H05K1/02; H05K1/09; H05K1/092; H05K1/095
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
99 words
A process for preparing a metallized polymer composition comprising reacting a compound or mixture of compounds containing a positive valent metal element A selected from the group consisting of tin, arsenic, antimony and bismuth with a metallic source of a metal element B selected from the group consisting of iron, cobalt, nickel, copper, zinc, gallium, ruthenium, rhodium, palladium, silver, cadmium, and indium at the surface of said polymer composition at a temperature and pressure appropriate for obtaining a surface layer on the polymer composition comprising an intermetallic combination containing both the metal element A and the metal element B.
Claim 2
Dependent Claim
99 words
A process for preparing a metallized polymer composition comprising reacting a compound or mixture of compounds containing a positive valent metal element A selected from the group consisting of tin, arsenic, antimony and bismuth with a metallic source of a metal element B selected from the group consisting of iron, cobalt, nickel, copper, zinc, gallium, ruthenium, rhodium, palladium, silver, cadmium, and indium at the surface of said polymer composition at a temperature and pressure appropriate for obtaining a surface layer on the polymer composition comprising an intermetallic combination containing both the metal element A and the metal element B.
Claim 3
Dependent Claim
17 words
The process of claim 1 wherein a support surface is provided which comprises said metal element B.
Claim 4
Dependent Claim
42 words
The process of claim 2, wherein said reaction is effected with said surface of said polymer composition being pressed onto said support surface with said compound or mixture of compounds being between said surface of said polymer composition and said support surface.
Claim 5
Dependent Claim
22 words
The process of claim 3, wherein said compound or mixture of compounds is first applied to said surface of said polymer composition.
Claim 6
Dependent Claim
19 words
The process of claim 3, wherein said compound or mixture of compounds is first applied to said support surface.
Claim 7
Dependent Claim
27 words
The process of claim 3, wherein said compound or mixture of compounds is first applied to both said surface of said polymer composition and said support surface.
Claim 8
Dependent Claim
47 words
The process of claim 2, wherein said support surface is of a shape that will determine the shape of the surface of the polymer composition to be metallized, said polymer composition being pressed onto said support surface to effect molding of said polymer composition during said reaction.
Claim 9
Dependent Claim
29 words
The process of claim 2, wherein said compound or mixture of compounds containing a positively valent metal element A is incorporated into said polymer composition prior to said reaction.
Claim 10
Dependent Claim
26 words
The process of claim 2, wherein said support surface comprises a mold on the surface of which a foil of the metal element B is placed.
Claim 11
Dependent Claim
27 words
The process claim 1 wherein said compound or mixture of compounds comprises a hydride, halide, sulfide, phosphide or carboxylate of the metal element A or its precursors.
Claim 12
Dependent Claim
21 words
The process of claim 1 wherein at least part of said surface layer is further plated by deposition of additional metal.
Claim 13
Dependent Claim
80 words
A process for preparing a metallized polymer composition comprising bringing into contact at least one layer of zero-valent antimony and at least one layer of a metal element B selected from the group consisting of iron, cobalt, nickel, copper, zinc, gallium, ruthenium, rhodium, palladium, silver, cadmium and indium with a polymer or prepolymer composition at a temperature and pressure appropriate for obtaining a polymer composition having a surface layer comprising an intermetallic compound of antimony and the metal element B.
Claim 14
Dependent Claim
80 words
A process for preparing a metallized polymer composition comprising bringing into contact at least one layer of zero-valent antimony and at least one layer of a metal element B selected from the group consisting of iron, cobalt, nickel, copper, zinc, gallium, ruthenium, rhodium, palladium, silver, cadmium and indium with a polymer or prepolymer composition at a temperature and pressure appropriate for obtaining a polymer composition having a surface layer comprising an intermetallic compound of antimony and the metal element B.
Claim 15
Dependent Claim
26 words
The process of claim 12 wherein said layer of metal element B constitutes the surface layer of a body consisting essentially of said metal element B.
Claim 16
Dependent Claim
21 words
The process of claim 12 wherein said layer of metal element B is a layer deposited upon an inert release substrate.
Claim 17
Dependent Claim
28 words
The process of claim 12 wherein said metallizing conditions include a pressure in the range of from about 100 kPa to about 10 MPa to effect said contact.
Claim 18
Dependent Claim
21 words
The process of claim 12 wherein said metallizing conditions include a temperature range of from ambient temperature to about 600° C.
Claim 19
Dependent Claim
20 words
The process of claim 16 wherein said metallizing conditions include a temperature of from about 125° to about 375° C.
Claim 20
Dependent Claim
21 words
A process of claim 12 wherein at least part of said surface layer is further plated by deposition of additional metal.
References Cited (Backward Citations)
US3620834A
Cited
GB1309320A
Cited
DE2022109A1
Cited
WO1983002784A1
Cited
US4459330A
Cited
EP0125617A2
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-01-03 | 1992-07-04 | 1993-01-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-01-03 | 1996-07-04 | 1997-01-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-01-03 | 2000-07-04 | 2001-01-03 | $7700.00 | Window Closed / Lapsed |