Production process for manufacturing low molecular weight water soluble acrylic polymers as drilling fluid additives
Assignee: Amcol International Corp
•
Filing: 1987-11-30
•
Granted: 1988-12-27
•
Expires: 2007-11-30
Abstract
Abstract Disclosed is a process for preparing relatively low molecular weight, water absorbing, acrylic polymers for use as drilling fluid additives by aqueous polymerization of (A) an acrylic monomer, such as acrylic acid neutralized 0 to 100 mole percent with, for example, ammonia, and/or an alkali such as Na 2 O 3 , and/or an amine; with (B) acrylamide in a mole ratio of 70 to 100 mole percent (A) to 30:0 mole percent (B). The molecular weight is limited to 1,000 to 50,000, such as by adding a chain transfer agent to the polymerization mixture, to achieve excellent results as a drilling fluid additive. The monomer, such as partially neutralized acrylic acid, is polymerized in aqueous solution in the presence of a polymerization initiator without external heating while allowing water to evaporate off. A substantially dry water soluble polymer (less than 15 weight percent water) is achieved when polymerization is completed by utilizing the exothermic heat of polymerization and crosslinking to drive off water without the need for additional heating to obtain a dry solid.
Inventors
- 👤 William Alexander
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 04:43
CPC Classifications
C; C08; C08F; C08F20/00; C08F20/02; C08F20/04; C08F20/06; C09; C09K; C09K8/00; C09K8/02; C09K8/04; C09K8/14; C09K8/18; C09K8/22; C09K8/24; Y; Y10; Y10S; Y10S524/00; Y10S524/916
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
149 words
A process for preparing a solid, essentially uncrosslinked water-soluble resin comprising mixing with water a monomer solution of an acrylic monomer and 0-30 mole percent acrylamide, said acrylic monomer neutralized 0-100 mole percent; and limiting the degree of polymerization of the monomer to a weight average molecular weight of about 1,000 to about 50,000 to form a mixed monomer solution, wherein the monomers of the mixed monomer solution consist essentially of the acrylic monomer and optionally acrylamide, and water is present in the mixed monomer solution in an amount of 1 to 40% by weight of the mixed monomer solution, and initiating polymerization of the acrylic monomer such that during polymerization, the exothermic heat of reaction is substantially the only heat energy used to accomplish polymerization, and to drive off sufficient water to obtain a solid, water-soluble resin having a water content of 13 percent by weight or less.
Claim 2
Dependent Claim
149 words
A process for preparing a solid, essentially uncrosslinked water-soluble resin comprising mixing with water a monomer solution of an acrylic monomer and 0-30 mole percent acrylamide, said acrylic monomer neutralized 0-100 mole percent; and limiting the degree of polymerization of the monomer to a weight average molecular weight of about 1,000 to about 50,000 to form a mixed monomer solution, wherein the monomers of the mixed monomer solution consist essentially of the acrylic monomer and optionally acrylamide, and water is present in the mixed monomer solution in an amount of 1 to 40% by weight of the mixed monomer solution, and initiating polymerization of the acrylic monomer such that during polymerization, the exothermic heat of reaction is substantially the only heat energy used to accomplish polymerization, and to drive off sufficient water to obtain a solid, water-soluble resin having a water content of 13 percent by weight or less.
Claim 3
Dependent Claim
23 words
A process as defined in claim 1 wherein the mixed monomer solution has a temperature of ambient to 85° C. prior to polymerization.
Claim 4
Dependent Claim
24 words
A process as defined in claim 1 wherein the molecular weight is limited by including a chain transfer agent in the mixed monomer solution.
Claim 5
Dependent Claim
13 words
The process of claim 3 wherein the chain transfer agent is a mercaptan.
Claim 6
Dependent Claim
29 words
A process as defined in claim 1 wherein the mixed monomer solution contains 1 to 10 wt. % of an organic solvent based on the weight of the monomer(s).
Claim 7
Dependent Claim
26 words
A process as defined in claim 1 wherein the mixed monomer solution further contains an organic solvent having a boiling point of 40° to 150° C.
Claim 8
Dependent Claim
157 words
A process for preparing a solid, essentially uncrosslinked water-soluble polymer comprising: combining a monomer mixture of (A) an acrylic monomer; and (B) 0 to 30 mole percent acrylamide, with water in an amount of at least 5.0 weight percent of (A) plus (B) based on the total weight of (A) plus (B) plus water to form a monomer solution wherein the monomers of the monomer mixture consist essentially of (A) and (B) and the water content of the monomer solution is 40% by weight or less; adding a polymerization initiator to said monomer mixture capable of initiating, and in an amount sufficient to initiate, polymerization of said monomer(s) in said monomer solution; polymerizing said monomer solution while utilizing the exothermic heat of reaction as substantially the only non-ambient energy source to drive water away from said monomer solution to form said water-soluble polymer having a water content sufficiently low to be powdered without an intermediate drying step.
Claim 9
Dependent Claim
157 words
A process for preparing a solid, essentially uncrosslinked water-soluble polymer comprising: combining a monomer mixture of (A) an acrylic monomer; and (B) 0 to 30 mole percent acrylamide, with water in an amount of at least 5.0 weight percent of (A) plus (B) based on the total weight of (A) plus (B) plus water to form a monomer solution wherein the monomers of the monomer mixture consist essentially of (A) and (B) and the water content of the monomer solution is 40% by weight or less; adding a polymerization initiator to said monomer mixture capable of initiating, and in an amount sufficient to initiate, polymerization of said monomer(s) in said monomer solution; polymerizing said monomer solution while utilizing the exothermic heat of reaction as substantially the only non-ambient energy source to drive water away from said monomer solution to form said water-soluble polymer having a water content sufficiently low to be powdered without an intermediate drying step.
Claim 10
Dependent Claim
35 words
The process of claim 7 further including the step of adjusting the temperature of the monomer solution to a temperature of 25° to 85° C. prior to adding said polymerization initiator to said monomer mixture.
Claim 11
Dependent Claim
26 words
The process of claim 7 wherein said polymerization initiator is added in an amount of at least 0.5% by total weight of monomers (A) and (B).
Claim 12
Dependent Claim
32 words
The process of claim 7 wherein the water content of said water-soluble polymer is not greater than about 10% by weight as recovered from the polymerized mixture, without an additional drying step.
Claim 13
Dependent Claim
24 words
The process of claim 7 further including combining a non-aqueous solvent having a boiling point of 40°-150° C. with said monomers (A) and (B).
Claim 14
Dependent Claim
16 words
The process of claim 7 including the step of pulverizing said resin to form a powder.
Claim 15
Independent Claim
166 words
A method of manufacturing an essentially uncrosslinked water-soluble polymer comprising mixing a monomer solution of (A) an acrylic-monomer, neutralized 0 to 100 mole percent, and (B) acrylamide in a mole ratio of (A):(B) in the range of 70:30 to 100:0, and water to form a mixed monomer solution, wherein the monomers of the mixed monomer solution consist essentially of (A) and (B); and the monomer concentration in the mixture is 50-90% by weight of the monomer solution prior to polymerization initiation and the water concentration is 1% to 40% by weight of the monomer solution prior to polymerization initiation; and initiating polymerization of monomer (A) and terminating polymerization of monomer A at a weight average molecular weight of about 1,000 to about 50,000, such that during polymerization, the exothermic heat of reaction is substantially the only heat energy used to accomplish polymerization, and to drive off sufficient water to form a solid, water-soluble acrylic-containing polymer having a water content of 15 percent by weight or less.
Claim 16
Independent Claim
166 words
A method of manufacturing an essentially uncrosslinked water-soluble polymer comprising mixing a monomer solution of (A) an acrylic-monomer, neutralized 0 to 100 mole percent, and (B) acrylamide in a mole ratio of (A):(B) in the range of 70:30 to 100:0, and water to form a mixed monomer solution, wherein the monomers of the mixed monomer solution consist essentially of (A) and (B); and the monomer concentration in the mixture is 50-90% by weight of the monomer solution prior to polymerization initiation and the water concentration is 1% to 40% by weight of the monomer solution prior to polymerization initiation; and initiating polymerization of monomer (A) and terminating polymerization of monomer A at a weight average molecular weight of about 1,000 to about 50,000, such that during polymerization, the exothermic heat of reaction is substantially the only heat energy used to accomplish polymerization, and to drive off sufficient water to form a solid, water-soluble acrylic-containing polymer having a water content of 15 percent by weight or less.
Claim 17
Dependent Claim
35 words
The method of claim 13 wherein the water content of said water-soluble polymer is not greater than about 10% by weight as recovered from the mixed monomer solution after polymerization, without an additional drying step.
Claim 18
Dependent Claim
22 words
The method of claim 14 including depositing said monomer mixture including said initiator onto a support surface in layer form for polymerization.
References Cited (Backward Citations)
US3687846A
Cited
US3915927A
Cited
US4172066A
Cited
US4113688A
Cited
US4236545A
Cited
US4552938A
Cited
US4525527A
Cited
US4603154A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-12-27 | 1992-06-27 | 1992-12-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-12-27 | 1996-06-27 | 1996-12-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-12-27 | 2000-06-27 | 2000-12-27 | $7700.00 | Window Closed / Lapsed |