Synthetic fiber
Assignee: Intera Technologies Inc
•
Filing: 1987-08-03
•
Granted: 1988-12-13
•
Expires: 2007-08-03
Abstract
Abstract The invention is related to a method of making paper or non-woven articles, comprising treating a substrate to render said substrate durably hydrophilic; and forming said durably hydrophilic fiber into a paper or non-woven article.
Inventors
- 👤 Ted A. Mallen
- 👤 Doyle B. Word
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 12:53
CPC Classifications
D; D21; D21H; D21H17/00; D21H17/03; D21H17/05; D21H17/18; D21H17/19; D21H17/06; D21H17/09; D21H21/00; D21H21/06; D21H21/08
Claims Analysis
Total Claims: 40
Claim 1
Independent Claim
129 words
A method of making paper or non-woven articles, comprising: (i) treating a fiber substrate to render said substrate durably hydrophilic, wherein said treating step comprises: (a) contacting said substrate with an aqueous mixture at a temperature between about 40° C. and about 100° C. containing an effective amount of a water-soluble cross-linking vinyl monomer and an effective amount of an organic hydrophobic carrier compound having a greater affinity for the substrate than the surrounding aqueous mixture, all non-aromatic carbon-carbon bonds of said carrier compound being saturated; and (b) thereafter initiating polymerization of said water-soluble cross-linking monomer to form a vinyl polymer on said substrate whereby the hydrophilic properties of said substrate are improved; and (ii) forming said durable hydrophilic substrate into a paper or non-woven article on papermaking equipment.
Claim 2
Independent Claim
129 words
A method of making paper or non-woven articles, comprising: (i) treating a fiber substrate to render said substrate durably hydrophilic, wherein said treating step comprises: (a) contacting said substrate with an aqueous mixture at a temperature between about 40° C. and about 100° C. containing an effective amount of a water-soluble cross-linking vinyl monomer and an effective amount of an organic hydrophobic carrier compound having a greater affinity for the substrate than the surrounding aqueous mixture, all non-aromatic carbon-carbon bonds of said carrier compound being saturated; and (b) thereafter initiating polymerization of said water-soluble cross-linking monomer to form a vinyl polymer on said substrate whereby the hydrophilic properties of said substrate are improved; and (ii) forming said durable hydrophilic substrate into a paper or non-woven article on papermaking equipment.
Claim 3
Dependent Claim
16 words
The method of claim 1, wherein said aqueous mixture is maintained under agitation in step (a).
Claim 4
Dependent Claim
28 words
The method of claim 1, wherein the aqueous mixture is a suitable aqueous emulsion containing a water-soluble cross-linking vinyl monomer, and a hydrophobic carrier compound which is emulsifiable.
Claim 5
Dependent Claim
19 words
The method of claim 3, wherein the temperature during polymerization is between about 80° C. and about 100° C.
Claim 6
Dependent Claim
19 words
The method of claim 4, wherein the temperature during polymerization is between about 90° C. and about 95° C.
Claim 7
Dependent Claim
118 words
The method of claim 3, wherein the carrier compound has the formula: ##STR10## wherein n is an integer from zero to ten; R 1 and R 2 are independently selected from the group consisting of hydrogen and alkyl, cycloalkyl, alkylaryl and halohydrocarbyl groups containing from 1 to 20 carbon atoms; each R 3 is independently hydrogen or alkyl; R 4 and R 4' are independently selected from the group consisting of hydrogen and hydrocarbyl groups containing from 1 to 20 carbon atoms; and R 5 and R 5' are independently selected from the group consisting of hydrogen, hydrocarbyl and halohydrocarbyl group containing from 1 to 30 carbon atoms, and acyl groups containing from 1 to 30 carbon atoms.
Claim 8
Dependent Claim
91 words
The method of claim 3, wherein the carrier compound has the formula: ##STR11## wherein n is an integer from zero to ten; R 4 and R 4' are independently selected from the group consisting of hydrogen and hydrocarbyl groups containing from 1 to 20 carbon atoms; and R 6 and R 6' are independently selected from the group consisting of (i) hydrogen, (ii) alkyl, cycloalkyl, alkylaryl and halohydrocarbyl groups containing from 1 to 20 carbon atoms, and (iii) alkanoyl, cycloalkanoyl, arylalkanoyl and halohydrocarbanoyl groups containing from 1 to 20 carbon atoms.
Claim 9
Dependent Claim
91 words
The method of claim 3, wherein the carrier compound has the formula: ##STR12## wherein n is an integer from zero to ten; R 4 and R 4' are independently selected from the group consisting of hydrogen and hydrocarbyl groups containing from 1 to 20 carbon atoms; and R 6 and R 6' are independently selected from the group consisting of (i) hydrogen, (ii) alkyl, cycloalkyl, alkylaryl and halohydrocarbyl groups containing from 1 to 20 carbon atoms, and (iii) alkanoyl, cycloalkanoyl, arylalkanoyl, and acylhalohydrocarbanoyl groups containing from 1 to 20 carbon atoms.
Claim 10
Dependent Claim
122 words
The method of claim 3, wherein the carrier compound has the formula: ##STR13## wherein n is an integer from zero to ten; R 4 and R 4' are independently selected from the group consisting of hydrogen and hydrocarbyl groups containing from 1 to 20 carbon atoms; R 6 and R 6' are independently selected from the group consisting of (i) hydrogen, (ii) alkyl, cycloalkyl, alkylaryl and halohydrocarbyl groups containing from 1 to 20 carbon atoms, and (iii) alkanoyl, cycloalkanoyl, arylalkanoyl and halohydrocarbanoyl groups containing from 1 to 20 carbon atoms; and R 7 is selected from the group consisting of alkylene, alkylalkylene, cycloalkylene, arylalkylene, haloalkylenyl and haloalkylalkylene groups containing from 1 to 20 carbon atoms, oxygen, sulfur, C═O and --SO 2 --.
Claim 11
Dependent Claim
47 words
The method of claim 3, wherein the carrier compound has the formula: ##STR14## wherein n is an integer from zero to ten; and R 4 and R 4' are independently selected from the group consisting of hydrogen and hydrocarbyl groups containing from 1 to 20 carbon atoms.
Claim 12
Dependent Claim
60 words
A process according to claim 3, wherein the carrier compound has the formula: ##STR15## wherein n is an integer from zero to ten; and R 7 is selected from the group consisting of (i) alkylene groups containing from 1 to 20 carbon atoms and (ii) alkyl-, cycloalkyl-, aryl-, aralkyl-, halo- and haloalkyl-substituted alkylene groups of from to 20 carbon atoms.
Claim 13
Dependent Claim
64 words
The method of claim 3, wherein the carrier compound is a member of the group consisting of ##STR16## wherein R 4 is selected from the group consisting of hydrogen and hydrocarbyl groups containing from 1 to 20 carbon atoms; and R 8 is selccted from the group consisting of hydrogen and alkyl, cycloalkyl, alkylaryl and halohydrocarbyl groups containing from 1 to 30 carbon atoms.
Claim 14
Dependent Claim
47 words
The method of claim 3, wherein the suitable emulsion contains an emulsifying agent of a composition which does not adversely interfere with the process and which is present in an amount sufficient to maintain said suitable aqueous emulsion but not enough to adversely interfere with said process.
Claim 15
Dependent Claim
64 words
The method of claim 13, wherein step (a) comprises the steps of: (i) immersing the substrate in water; (ii) adding the hydrophobic carrier compound and emulsifying agent to the water to form an aqueous emulsion of the hydrophobic carrier compound; (iii) agitating the system for a sufficient time for dispersal and contact of the components to occur; and (iv) adding water soluble vinyl monomer.
Claim 16
Dependent Claim
18 words
The method of claim 13, wherein the substrate is rinsed, after step (iii) to remove excess emulsifying agent.
Claim 17
Dependent Claim
20 words
The method of claim 11 in which the initiation of polymerization in step (b) is achieved by a chemical initiator.
Claim 18
Dependent Claim
25 words
The method of claim 11 in which the initiation of polymerization in step (b) is achieved by a physical impetus which starts and maintains polymerization.
Claim 19
Dependent Claim
37 words
The method of claim 11 wherein the suitable aqueous emulsion in step (a) is maintaine below the polymerization temperature and contains an initiator which is activated by raising the temperature above the polymerization temperature in step (b).
Claim 20
Dependent Claim
30 words
The method of claim 11 in which the water-soluble cross-linking vinyl monomer is present in a concentration of between about 0.002 to 10 weight percent on weight of the substrate.
Claim 21
Dependent Claim
34 words
The method of claim 11 in which the hydrophobic carrier compound is present in the suitable aqueous emulsion in a concentration of between about 0.02 to 2.0 weight percent on weight of the substrate.
Claim 22
Dependent Claim
30 words
The method of claim 11 in which the suitable aqueous emulsion is in contact with the substrate for at least about 30 seconds to 30 minutes prior to initiating polymerization.
Claim 23
Dependent Claim
23 words
The method of claim 11 in which polymerization is achieved within about 30 seconds to about 30 minutes after initiation in step (b).
Claim 24
Dependent Claim
38 words
The method of claim 11 wherein the carrier compound is selected from the group consisting of 5-hydroxy-3-oxapentyl terephthalate, diethoxylated Bisphenol A, triethoxylated Bisphenol A, hexaethoxylated Bisphenol A, isobutyric acid ester of ethoxylated Bisphenol A, and 1,4-butanediol diglycidyl ether.
Claim 25
Dependent Claim
26 words
The method of claim 11 wherein the carrier compound is an epoxy resin of the formula ##STR17## wherein n is an integer from zero to ten.
Claim 26
Dependent Claim
13 words
The method of claim 24 wherein the water-soluble cross-linking vinyl monomer is N,N'-methylenebisacrylamide.
Claim 27
Dependent Claim
34 words
The method of claim 11 in which the hydrophobic carrier compound is present in the suitable aqueous emulsion in a concentration of between about 0.02 to 2.0 weight percent on weight of the substrate.
Claim 28
Dependent Claim
91 words
The method of claim 11, in which the concentration of the water-soluble cross-linking vinyl monomer in the suitable substrate is between about 0.002 and about 10 weight percent on weight of the substrate, the concentration of the hydrophobic carrier compound is between about 0.02 and about 2.0 weight percent on weight of the substrate, the suitable aqueous emulsion is in contact with the substrate for about 30 seconds to about 30 minutes prior to initiating polymerization and the polymerization is achieved within about 30 seconds to about 30 minutes after initiation.
Claim 29
Dependent Claim
26 words
The method of claim 27 wherein the water-soluble cross-linking vinyl monomer is N,N'-methylenebisacrylamide and the hydrophobic carrier compound is isobutyric acid ester of ethoxylated Bisphenol A.
Claim 30
Dependent Claim
11 words
The method of claim 1, wherein said substrate is a fiber.
Claim 31
Dependent Claim
12 words
The method of claim 29, wherein said fiber is a staple fiber.
Claim 32
Dependent Claim
10 words
The method of claim 1, wherein the substrate is polyester.
Claim 33
Dependent Claim
11 words
The method of claim 1, wherein the substrate is a polyolefin.
Claim 34
Dependent Claim
10 words
The method of claim 32, wherein the polyolefin is polypropylene.
Claim 35
Dependent Claim
11 words
The method of claim 1, wherein the substrate is a polyamide.
Claim 36
Dependent Claim
20 words
The method of claim 34, wherein the poyamide is selected from the group consisting of nylon 6 and nylon 6,6.
Claim 37
Dependent Claim
14 words
The non-woven or paper article prepared in accordance with the process of claim 1.
Claim 38
Dependent Claim
15 words
The polyester non-woven or paper article prepared in accordance with the process of claim 31.
Claim 39
Dependent Claim
15 words
The polyolefin non-woven or paper article prepared in accordance with the process of claim 32.
Claim 40
Dependent Claim
15 words
The polyamide non-woven or paper article prepared in accordance with the process of claim 34.
References Cited (Backward Citations)
US2869435A
Cited
US3047355A
Cited
US3188165A
Cited
US3250664A
Cited
US3670048A
Cited
US3650669A
Cited
US3708555A
Cited
US3779881A
Cited
US4007250A
Cited
JPS5020010A
Cited
US4605612A
Cited
US4749328A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-12-13 | 1992-06-13 | 1992-12-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-12-13 | 1996-06-13 | 1996-12-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-12-13 | 2000-06-13 | 2000-12-13 | $7700.00 | Window Closed / Lapsed |