Material based on a caoutchouc-type mixture for producing hard rubber, method of using such material for producing engine components, and engine components manufactured from such material
Assignee: Semperit AG Holding
•
Filing: 1985-09-09
•
Granted: 1988-12-06
•
Expires: 2005-09-09
Abstract
Abstract Into a material based on a caoutchouc-type or caoutchouc-containing mixture for producing hard rubber, there is incorporated a pre-mix containing high-strength organic fibers and a liquid hardenable plastic material. The high-strength and temperature resistant material thus obtained is particularly suitable for the attenuation of noise in combustion engines when heavy-weight fillers are also added to such material. Engine components like, for example, valve covers, timing gear covers and oil pans can be manufactured from this material.
Inventors
- 👤 Josef Affenzeller
- 👤 Wolf-Dieter Jost
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 13:40
CPC Classifications
F; F02; F02F; F02F7/00; F02F7/006; C; C08; C08J; C08J3/00; C08J3/20; C08J3/22; C08J5/00; C08J5/24; C08J5/245; C08J5/249; C08K; C08K3/00; C08K3/02; C08K3/08; C08K7/00; C08K7/02; C08K9/00; C08K9/04; C08L; C08L21/00; C08L61/00; C08L61/04; C08L9/00; C08L9/02; C08J2321/00; C08L63/00; C08L65/00; C08L65/02; C08L67/00; C08L77/00; C08L77/10; F01; F01M; F01M11/00; F01M11/0004; F05; F05C; F05C2225/00; F05C2225/02
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
194 words
A material based on a rubber mixture for producing hard rubber and comprising: a rubber mixture comprising a preselected synthetic nitrile rubber, another synthetic diene rubber or natural rubber conjointly with vulcanizing adjuvants and a pre-mix; said pre-mix containing a mixture of high-strength organic fibers and a liquid hardenable plastic material; said high-strength organic fibers being selected from high-strength organic fibers which withstand, to a large extent, the shearing stresses occurring during the rubber mixing operations; said high-strength organic fibers being present in an amount resulting in a proportion in the range of about 10 to about 100 parts per 100 parts of said preselected rubber in said rubber mixture; said liquid hardenable plastic material containing a cross-linking agent for hardening said liquid hardenable plastic material; said liquid hardenable plastic material being selected from the group consisting of liquid phenolic resin, liquid polyester resin, liquid epoxide resin and a mixture of at least two of the aforementioned resins; and said liquid hardenable plastic resin being present in an amount resulting in a proportion in the range of about 20 to about 200 parts per 100 parts of said preselected rubber in said rubber mixture.
Claim 2
Dependent Claim
194 words
A material based on a rubber mixture for producing hard rubber and comprising: a rubber mixture comprising a preselected synthetic nitrile rubber, another synthetic diene rubber or natural rubber conjointly with vulcanizing adjuvants and a pre-mix; said pre-mix containing a mixture of high-strength organic fibers and a liquid hardenable plastic material; said high-strength organic fibers being selected from high-strength organic fibers which withstand, to a large extent, the shearing stresses occurring during the rubber mixing operations; said high-strength organic fibers being present in an amount resulting in a proportion in the range of about 10 to about 100 parts per 100 parts of said preselected rubber in said rubber mixture; said liquid hardenable plastic material containing a cross-linking agent for hardening said liquid hardenable plastic material; said liquid hardenable plastic material being selected from the group consisting of liquid phenolic resin, liquid polyester resin, liquid epoxide resin and a mixture of at least two of the aforementioned resins; and said liquid hardenable plastic resin being present in an amount resulting in a proportion in the range of about 20 to about 200 parts per 100 parts of said preselected rubber in said rubber mixture.
Claim 3
Dependent Claim
17 words
The material as defined in claim 1, wherein: said high-strength organic fibers are pre-impregnated with liquid rubber.
Claim 4
Dependent Claim
19 words
The material as defined in claim 1, wherein: said high-strength organic fibers incorporated into said pre-mix, constitute aramid fibers.
Claim 5
Dependent Claim
19 words
The material as defined in claim 1, wherein: said high-strength organic fibers incorporated into said pre-mix, constitute polyester fibers.
Claim 6
Dependent Claim
19 words
The material as defined in claim 1, wherein: said high-strength organic fibers incorporated into said pre-mix, constitute poly-acrylonitrile fibers.
Claim 7
Dependent Claim
19 words
The material as defined in claim 2, wherein: said high-strength organic fibers incorporated into said pre-mix, constitute aramid fibers.
Claim 8
Dependent Claim
19 words
The material as defined in claim 2, wherein: said high-strength organic fibers incorporated into said pre-mix, constitute polyester fibers.
Claim 9
Dependent Claim
19 words
The material as defined in claim 2, wherein: said high-strength organic fibers incorporated into said pre-mix, constitute poly-acrylonitrile fibers.
Claim 10
Dependent Claim
26 words
The material as defined in claim 1, wherein: said high-strength organic fibers have a fiber length in the range of about 0.5 to about 70 mm.
Claim 11
Dependent Claim
26 words
The material as defined in claim 9, wherein: said high-strength organic fibers have a fiber length in the range of about 1 to about 60 mm.
Claim 12
Dependent Claim
42 words
The material as defined in claim 1, wherein: said high-strength organic fibers are contained in said rubber mixture in a proportion in the range of up to 60 parts per 100 parts by weight of said rubber in said preselected rubber mixture.
Claim 13
Dependent Claim
31 words
The material as defined in claim 1, wherein: said preselected rubber is selected from the group consisting of nitrile rubber, natural rubber and a mixture of nitrile rubber and natural rubber.
Claim 14
Dependent Claim
47 words
The material as defined in claim 1, further including: at least one filler; and said at least one filler is admixed to said rubber mixture in an amount in the range of about 200 to about 1,000 parts per 100 parts by weight of said pre-selected rubber.
Claim 15
Dependent Claim
27 words
The material as defined in claim 13, wherein: said at least one filler constitutes a heavy-weight filler selected from the group consisting of barytes and metal powder.
Claim 16
Dependent Claim
203 words
A material based on a rubber mixture for producing hard rubber and comprising: a rubber mixture comprising a preselected rubber conjointly with vulcanizing adjuvants and a premix; said preselected rubber being selected from the group consisting of nitrile rubber, natural rubber, and a mixture of nitrile rubber and natural rubber; said pre-mix containing a mixture of high-strength organic fibers and a liquid hardenable plastic material; said high-strength organic fibers being selected from the group consisting of aramid fibers, polyester fibers and poly-acrylonitrile fibers; said high-strength organic fibers being present in an amount resulting in a proportion in the range of about 10 to about 100 parts per 100 parts of said preselected rubber contained in said rubber mixture; said liquid hardenable plastic material containing a cross-linking agent for hardening said liquid hardenable plastic material; said liquid hardenable plastic material being selected from the group consisting of liquid phenolic resin, liquid polyester resin, liquid epoxide resin and a mixture of at least two of the aforementioned resins; and said liquid hardenable plastic resin being present in an amount resulting in a proportion in the range of about 20 to about 200 parts per 100 parts of said preselected rubber contained in said rubber mixture.
Claim 17
Dependent Claim
203 words
A material based on a rubber mixture for producing hard rubber and comprising: a rubber mixture comprising a preselected rubber conjointly with vulcanizing adjuvants and a premix; said preselected rubber being selected from the group consisting of nitrile rubber, natural rubber, and a mixture of nitrile rubber and natural rubber; said pre-mix containing a mixture of high-strength organic fibers and a liquid hardenable plastic material; said high-strength organic fibers being selected from the group consisting of aramid fibers, polyester fibers and poly-acrylonitrile fibers; said high-strength organic fibers being present in an amount resulting in a proportion in the range of about 10 to about 100 parts per 100 parts of said preselected rubber contained in said rubber mixture; said liquid hardenable plastic material containing a cross-linking agent for hardening said liquid hardenable plastic material; said liquid hardenable plastic material being selected from the group consisting of liquid phenolic resin, liquid polyester resin, liquid epoxide resin and a mixture of at least two of the aforementioned resins; and said liquid hardenable plastic resin being present in an amount resulting in a proportion in the range of about 20 to about 200 parts per 100 parts of said preselected rubber contained in said rubber mixture.
References Cited (Backward Citations)
GB1385478A
Cited
US3922422A
Cited
GB1462444A
Cited
GB1513049A
Cited
GB1477606A
Cited
US4029633A
Cited
FR2357736A1
Cited
US4285381A
Cited
GB2054626A
Cited
US4294732A
Cited
EP0070500A1
Cited
SU1027178A1
Cited
SU1073254A1
Cited
US4451595A
Cited
US4455399A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-12-06 | 1992-06-06 | 1992-12-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-12-06 | 1996-06-06 | 1996-12-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-12-06 | 2000-06-06 | 2000-12-06 | $7700.00 | Window Closed / Lapsed |