Thermally stable diamond abrasive compact body
Assignee: Individual
•
Filing: 1987-05-04
•
Granted: 1988-12-06
•
Expires: 2007-05-04
Abstract
Abstract The invention provides a composite diamond abrasive compact comprising a thermally stable diamond compact directly bonded to a cemented carbide substrate. The thermally stable diamond compact comprises bonded diamond forming a coherent, skeletal mass and a second phase which preferably consists of silicon and/or silicon carbide. A method of producing the composite diamond abrasive compact under controlled elevated temperature and pressure conditions is also provided.
Inventors
- 👤 Henry B. Dyer
- 👤 Cornelius Phaal
- 👤 Richard P. Brunand
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 17:20
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/515; C04B35/52; B; B01; B01J; B01J3/00; B01J3/06; B01J3/062; B22; B22F; B22F7/00; B22F7/06; B24; B24D; B24D3/00; B24D3/02; B24D3/04; B24D3/06; C04B35/622; C04B35/626; C04B35/63; C04B35/6303; C04B35/6316; C04B35/64; C04B35/645; C04B37/00; C04B37/02; C04B37/021; C04B37/023; C04B37/026; C22; C22C; C22C26/00; B01J2203/00; B01J2203/06; B01J2203/0605; B01J2203/062; B01J2203/065; B01J2203/0655; B01J2203/0675; B01J2203/0685; C04B2235/00; C04B2235/02; C04B2235/30; C04B2235/38; C04B2235/3817; C04B2235/3826; C04B2235/42; C04B2235/422; C04B2235/427; C04B2235/428; C04B2235/50; C04B2235/54; C04B2235/5418; C04B2235/5445; C04B2235/60; C04B2235/616; C04B2235/65; C04B2235/656; C04B2235/6567; C04B2235/70; C04B2235/80; C04B2237/00; C04B2237/02; C04B2237/04; C04B2237/08; C04B2237/083; C04B2237/09; C04B2237/30; C04B2237/32; C04B2237/36; C04B2237/363; C04B2237/40; C04B2237/401; C04B2237/50; C04B2237/61; C04B2237/64
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
172 words
A method of producing a composite diamond abrasive compact which includes a diamond compact directly bonded to a cemented carbide substrate, said diamond compact containing bonded diamond forming a coherent skeletal mass and a second phase consisting essentially of a refractory carbide forming metal, alone or in combination with another metal, each such metal being in the form of the metal, a carbide, and intermetallic compound or a combination of two or more thereof, comprising the steps of loading diamond particles and components(s) utilized to produce the second phase in a recess formed in a cemented carbide body such that the second phase components(s) lie(s) on the base of the recess and the diamond particles on top of the said component(s), providing means between the diamond and the side walls of the recess to prevent sideways infiltration of binder phase from the cemented carbide into the diamond mass, and subjecting the whole to controlled elevated temperature and pressure conditions to produce the diamond compact which is directly bonded to the carbide body.
Claim 2
Independent Claim
172 words
A method of producing a composite diamond abrasive compact which includes a diamond compact directly bonded to a cemented carbide substrate, said diamond compact containing bonded diamond forming a coherent skeletal mass and a second phase consisting essentially of a refractory carbide forming metal, alone or in combination with another metal, each such metal being in the form of the metal, a carbide, and intermetallic compound or a combination of two or more thereof, comprising the steps of loading diamond particles and components(s) utilized to produce the second phase in a recess formed in a cemented carbide body such that the second phase components(s) lie(s) on the base of the recess and the diamond particles on top of the said component(s), providing means between the diamond and the side walls of the recess to prevent sideways infiltration of binder phase from the cemented carbide into the diamond mass, and subjecting the whole to controlled elevated temperature and pressure conditions to produce the diamond compact which is directly bonded to the carbide body.
Claim 3
Dependent Claim
31 words
A method according to claim 1 which comprises placing the component(s) for the second phase directly on and in contact with the base of the recess formed in the carbide body.
Claim 4
Dependent Claim
40 words
A method according to claim 1 wherein a thin layer of no more than a few microns of a compatible particulate mass is placed between the second phase component(s) and the base of the recess formed in the carbide body.
Claim 5
Dependent Claim
22 words
A method according to claim 3 wherein the layer consists of powdered carbide containing a lower binder content than the carbide substrate.
Claim 6
Dependent Claim
32 words
A method according to claim 3 wherein the layer consists of powdered carbide containing a lower binder content than the carbide substrate and have a particle size of less than 1 micron.
Claim 7
Dependent Claim
20 words
A method to claim 4 wherein the layer consists of fine diamond particles of less than 1 micron particle size.
Claim 8
Dependent Claim
31 words
A method according to claim 3 wherein the layer consists of fine powdered carbide of particle size less than 1 micron having the same composition as that of the carbide substrate.
Claim 9
Dependent Claim
18 words
A method according to claim 3 wherein the layer consists of powdered carbide of a second phase metal.
Claim 10
Dependent Claim
17 words
A method according to claim 1 wherein the means is a layer of a high melting metal.
Claim 11
Dependent Claim
14 words
A method according to claim 1 wherein the means is a layer of tantalum.
Claim 12
Dependent Claim
48 words
A method according to claim 1 wherein the elevated conditions of temperature are in the range of 1400° to 1550° C., the elevated conditions of pressure are in the range 50 to 60 kilobars and these elevated conditions are maintained for a period of 10 to 20 minutes.
Claim 13
Dependent Claim
48 words
A method according to claim 1 wherein the cemented carbide is selected from the group consisting of cemented titanium carbide, cemented tungsten carbide and cemented tantalum carbide, each of which has a binder metal of nickel, iron, cobalt or a combination of two or more of said metals.
Claim 14
Dependent Claim
26 words
A method as defined in claim 1, wherein silicon is the component loaded into the recess so as to lie on the base of the recess.
References Cited (Backward Citations)
GB997352A
Cited
US3239321A
Cited
US3306720A
Cited
US3574580A
Cited
US3982911A
Cited
US3912500A
Cited
US3944398A
Cited
US3999962A
Cited
US4171339A
Cited
US4124401A
Cited
US4151686A
Cited
US4457765A
Cited
US4241135A
Cited
US4231195A
Cited
US4311490A
Cited
US4496372A
Cited
US4505721A
Cited
US4534773A
Cited
US4556403A
Cited
GB2158086A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-12-06 | 1992-06-06 | 1992-12-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-12-06 | 1996-06-06 | 1996-12-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-12-06 | 2000-06-06 | 2000-12-06 | $7700.00 | Window Closed / Lapsed |