Pressure reaction injection molding process for making molded bodies of thermosets optionally containing filler and/or reinforcing material
Assignee: Novartis Corp
•
Filing: 1986-07-03
•
Granted: 1988-11-15
•
Expires: 2006-07-03
Abstract
Abstract Molded bodies of thermoset material are produced from monomers, oligomers or higher pre-polymers of reactive resins by pressure reaction injection molding. The molded bodies may contain filler and/or reinforcing material. The process is carried out in a mold consisting of a first, preferably upper half mold and a second, preferably lower half mold, and an inlet socket opening downwardly into the first half mold. The mold is equipped with heating coils adapted for applying separately a lower temperature to the first half mold and a higher temperature to the second one. During the introduction and hardening phase of the reactive mixture, the first half mold is maintained at a lower temperature than the second half mold, the temperature difference amounts to about 40 to 180, and preferably 60 to 120 centigrades.
Inventors
- 👤 Hermann Diethelm
- 👤 Wolfgang Dresen
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 14:44
CPC Classifications
B; B29; B29C; B29C37/00; B29C37/005; B29C33/00; B29C33/02; B29C33/04; B29C45/00; B29C45/17; B29C45/72; B29C45/73; B29C67/00; B29C67/24; B29C67/246; B29C2045/7343
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
164 words
In a pressure reaction injection molding process for manufacturing a molded body of thermoset material by introducing into a mold a reactive mixture of thermosetting pre-polymer material, hardening agent and from 0% by weight to an effective property enhancing amount of filler, heating the material in the mold to hardening temperature, and adding fresh material to the mass during the hardening phase thereof, the improvement comprising carrying out the aforesaid steps in a mold consisting essentially of an upper half and a lower half and an inlet opening downwardly through the upper half into the and, during the hardening phase, while introducing said fresh material under pressure into the mold through said inlet, maintaining the temperature of the upper half substantially below the hardening temperature of the reactive mixture and maintaining the temperature of the lower half at least at such hardening temperature, thereby compensating practically completely for any loss of volume in the molded body caused by shrinkage thereof during the hardening phase.
Claim 2
Dependent Claim
164 words
In a pressure reaction injection molding process for manufacturing a molded body of thermoset material by introducing into a mold a reactive mixture of thermosetting pre-polymer material, hardening agent and from 0% by weight to an effective property enhancing amount of filler, heating the material in the mold to hardening temperature, and adding fresh material to the mass during the hardening phase thereof, the improvement comprising carrying out the aforesaid steps in a mold consisting essentially of an upper half and a lower half and an inlet opening downwardly through the upper half into the and, during the hardening phase, while introducing said fresh material under pressure into the mold through said inlet, maintaining the temperature of the upper half substantially below the hardening temperature of the reactive mixture and maintaining the temperature of the lower half at least at such hardening temperature, thereby compensating practically completely for any loss of volume in the molded body caused by shrinkage thereof during the hardening phase.
Claim 3
Dependent Claim
24 words
The improvement of claim 1, wherein the temperature difference between the upper and lower mold halves amounts to from 40 to 180 degrees centigrade.
Claim 4
Dependent Claim
24 words
The improvement of claim 1, wherein the temperature difference between the upper and lower mold halves amounts to from 40 to 120 degrees centigrade.
Claim 5
Dependent Claim
19 words
The improvement of claim 1, wherein the thermosetting resin is an epoxy resin, polyurethane resin or unsaturated polyester resin.
Claim 6
Dependent Claim
40 words
The improvement of claim 1, wherein the thermosetting resin and the hardening agent are separately heated to a filling-in temperature of from about 50° to 150° C., are homogeneously mixed with each other and are then introduced into the inlet.
Claim 7
Dependent Claim
30 words
The improvement of claim 5, wherein the temperature to which the thermosetting resin and the hardening agent are separately heated, is in the range of from 50° to 60° C.
Claim 8
Dependent Claim
26 words
The improvement of claim 4, wherein filler in an effective amount up to 60% of the weight of the mixture is added to the reactive mixture.
Claim 9
Dependent Claim
11 words
The improvement of claim 5, wherein the reactive mixture is dearated.
Claim 10
Dependent Claim
18 words
The improvement of claim 8, wherein the dearation of the reactive mixture is carried out under high vacuum.
Claim 11
Dependent Claim
30 words
The improvement of claim 5, further comprising the step of introducing an effective strength enhancing amount of a reinforcing agent into the mold prior to introducing the reactive mixture thereinto.
Claim 12
Dependent Claim
29 words
The improvement of claim 10, wherein the amount of reinforcing agent is in the range of 60 to 70% of the combined weight of thermosetting resin and hardening agent.
Claim 13
Dependent Claim
44 words
The improvement of claim 1, wherein the injection pressure on the material being introduced is maintained and varied during the entire hardening phase in a manner such as to compensate for loss of volume occurring due to hardening of the mass in the mold.
Claim 14
Dependent Claim
36 words
The improvement of claim 12, wherein the internal pressure in the mold during the introduction of fresh material and prior to the gelling point, is maintained at a minimum value of about 10 to 60 bar.
Claim 15
Dependent Claim
20 words
The improvement of claim 13, wherein the internal pressure prior to the gelling point is maintained at about 25 bar.
References Cited (Backward Citations)
US2136423A
Cited
US3619449A
Cited
JPS49128098A
Cited
US4157931A
Cited
US4249882A
Cited
US4350739A
Cited
US4370122A
Cited
US4338068A
Cited
US4439386A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-11-15 | 1992-05-16 | 1992-11-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-11-15 | 1996-05-16 | 1996-11-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-11-15 | 2000-05-16 | 2000-11-15 | $7700.00 | Window Closed / Lapsed |