Method for the production of shaped synthetic members
Assignee: Individual
•
Filing: 1987-04-06
•
Granted: 1988-11-08
•
Expires: 2007-04-06
Abstract
Abstract The invention relates to a method for the production of shaped synthetic members, in which (a) Synthetic granulated particles are mixed and coated with a conducting powder; (b) An electric current is passed through the mixture of granulated particles and conducting powder the surfaces of the granulated particles becoming plasticized; (c) The mixture of granulated particles and conducting powder is sintered to form a preform under the action of pressure; (d) The preform is extruded into a moulding cavity thus forming the shaped synthetic member.
Inventors
- 👤 Karl Gohring
- 👤 Hermann Kress
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 00:57
CPC Classifications
B; B29; B29C; B29C35/00; B29C35/02; B29B; B29B11/00; B29B11/06; B29B11/12; B29C43/00; B29C43/006; B29C45/00; B29C45/02; B29K; B29K2105/00; B29K2105/25; B29K2105/251; B29K2707/00; B29K2707/04
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
92 words
A method for the production of a shaped synthetic member which comprises (a) coating synthetic granulated particles with a mixture of a conducting powder and a synthetic powder, (b) passing an electric current through the coating of said coated granulated particles in a first zone whereby the surfaces of the granulated particles are plastified. (c) sintering the coated granulated particles to a preform in said first zone under the action of pressure; and (d) extruding the preform from said first zone into a moulding cavity to thus form a shaped synthetic member.
Claim 2
Independent Claim
92 words
A method for the production of a shaped synthetic member which comprises (a) coating synthetic granulated particles with a mixture of a conducting powder and a synthetic powder, (b) passing an electric current through the coating of said coated granulated particles in a first zone whereby the surfaces of the granulated particles are plastified. (c) sintering the coated granulated particles to a preform in said first zone under the action of pressure; and (d) extruding the preform from said first zone into a moulding cavity to thus form a shaped synthetic member.
Claim 3
Dependent Claim
20 words
The method according to claim 1 wherein said synthetic powder consists of the same material as the synthetic granulated particles.
Claim 4
Dependent Claim
31 words
The method according to claim 1 wherein the conducting powder and the synthetic powder are first mixed with each other and thereafter this mixture is mixed with the synthetic granulated particles.
Claim 5
Dependent Claim
30 words
The method according to claim 1 wherein approximately 10 to 40% by weight of the conducting powder is mixed with approximately 60 to 90% by weight of the synthetic powder.
Claim 6
Dependent Claim
26 words
The method according to claim 4 wherein approximately 20% by weight of the conducting powder is mixed with approximately 80% by weight of the synthetic powder.
Claim 7
Dependent Claim
36 words
The method according to claim 3 wherein approximately 3 to 40% by weight of the mixture of conducting powder and synthetic powder is mixed with approximately 60 to 97% by weight of the synthetic granulated particles.
Claim 8
Dependent Claim
32 words
The method according to claim 6 wherein approximately 20% by weight of the mixture of conducting powder and synthetic powder is mixed with approximately 80% by weight of the synthetic granulated particles.
Claim 9
Dependent Claim
35 words
The method according to claim 1 wherein during sintering the current flowing through the preform in the course of formation is measured and sintering is terminated when the current has dropped to a certain value.
Claim 10
Dependent Claim
14 words
The method according to claim 1 wherein the conducting powder is a graphite powder.
Claim 11
Dependent Claim
16 words
The method according to claim 1 wherein the synthetic material is an ultra high molecular polyethylene.
Claim 12
Dependent Claim
83 words
The method according to claim 1 wherein in passing from said first zone to said moulding cavity the material of the preform is extruded through a narrow passageway that has a cross section dimension less than the dimensions of the individual granulated particles so that in passing through said narrow passageway the synthetic granulated particles are deformed mechanically and the moulding cavity is gradually filled by material that consists of superficially plasticized, mechanically deformed synthetic granulated particles, sintered synthetic powder and conducting powder.
Claim 13
Dependent Claim
17 words
A method according to claim 11 wherein said narrow passageway remains closed until the preform is completed.
References Cited (Backward Citations)
US2439966A
Cited
US3254143A
Cited
US3284372A
Cited
US3268633A
Cited
US3733385A
Cited
US4065519A
Cited
US4193956A
Cited
US4491553A
Cited
US4518704A
Cited
US4518552A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-11-08 | 1992-05-09 | 1992-11-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-11-08 | 1996-05-09 | 1996-11-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-11-08 | 2000-05-09 | 2000-11-08 | $7700.00 | Window Closed / Lapsed |