Process for coating fine powders with a nylon and products made therewith
Assignee: Rilsan Corp
•
Filing: 1976-04-05
•
Granted: 1977-12-27
•
Expires: 1996-04-05
Abstract
Abstract A method for coating powders with nylon by mixing the powder with the nylon and a solvent for the nylon, precipitating the nylon out of solution and coating the powder particles, and separating the coated powder substantially in the form of agglomerates of individually coated particles. The coated powder can then be readily compressed to form a shaped structure, such as, a molded article. A nylon coated powder especially suitable for conversion into shaped structures by melt processes, such as, injection molding or melt extrusion, is obtained by incorporating an organic polymer modifier into the nylon coated powder.
Inventors
- 👤 Robert B. Koch
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 01:50
CPC Classifications
C; C09; C09B; C09B67/00; C09B67/0001; C09B67/0004; C09B67/0008; C09B67/0013; B; B29; B29C; B29C45/00; B29C45/0001; B29C48/00; B29C48/03; B29C48/04; B29C48/25; B29C48/285; B29C48/288; B29C48/29; C09C; C09C3/00; C09C3/10; B29K; B29K2105/00; B29K2105/0005; C01; C01P; C01P2004/00; C01P2004/50; C01P2004/60; C01P2004/61; C01P2004/80; C01P2006/00; C01P2006/80; Y; Y10; Y10S; Y10S428/00; Y10S428/90; Y10T; Y10T428/00; Y10T428/29; Y10T428/2913; Y10T428/2933; Y10T428/2964; Y10T428/2967
Claims Analysis
Total Claims: 29
Claim 1
Independent Claim
233 words
A method of making a shaped structure composed of a nylon binder and a material in particle form, substantially each individual particle of the material being surrounded by the binder to form a coated powder, the shaped structure having substantially no particle to particle contact and having distribution of the nylon binder substantially uniform throughout, comprising: A. charging into a forming apparatus the coated powder of the material particles coated with the nylon, the nylon being one which adheres to the individual material particles and is capable of being drawn into a filament or fiber and being a polyamide wherein the recurring amide groups are separated from each other by an alkylene radical having from 3 to 12 contiguous carbon atoms, 1. the coated powder being substantially in the form of agglomerates of individually coated particles of the material, 2. the coated powder comprising individual particles of the material having a size from about 1 millimicron to about 500 microns and having a substantially uniform coating of nylon, the material particles being insoluble in solvents which dissolve the nylon, the nylon coating representing at least 2% based on the weight of the coated powder; B. compressing the coated powder in the forming apparatus at a pressure of about 200 - 100,000 psi to bind and form the coated particles into the shaped structure; and C. recovering the shaped structure from the forming apparatus.
Claim 2
Independent Claim
233 words
A method of making a shaped structure composed of a nylon binder and a material in particle form, substantially each individual particle of the material being surrounded by the binder to form a coated powder, the shaped structure having substantially no particle to particle contact and having distribution of the nylon binder substantially uniform throughout, comprising: A. charging into a forming apparatus the coated powder of the material particles coated with the nylon, the nylon being one which adheres to the individual material particles and is capable of being drawn into a filament or fiber and being a polyamide wherein the recurring amide groups are separated from each other by an alkylene radical having from 3 to 12 contiguous carbon atoms, 1. the coated powder being substantially in the form of agglomerates of individually coated particles of the material, 2. the coated powder comprising individual particles of the material having a size from about 1 millimicron to about 500 microns and having a substantially uniform coating of nylon, the material particles being insoluble in solvents which dissolve the nylon, the nylon coating representing at least 2% based on the weight of the coated powder; B. compressing the coated powder in the forming apparatus at a pressure of about 200 - 100,000 psi to bind and form the coated particles into the shaped structure; and C. recovering the shaped structure from the forming apparatus.
Claim 3
Dependent Claim
45 words
The method of claim 1 wherein the agglomerates described in step (A)(1) have a size less than about 500 microns and wherein step (B) is carried out at a temperature of about 32° to about 50° F below the thermal degradation temperature of the nylon.
Claim 4
Dependent Claim
18 words
The method of claim 1 wherein the coated powder of step (A) is cold pressed in step (B).
Claim 5
Dependent Claim
39 words
The method of claim 1 wherein the shaped structure recovered in step (C) is sintered at a temperature of about 75° F below the melting point of the nylon up to about the thermal degradation temperature of the nylon.
Claim 6
Dependent Claim
36 words
The method of claim 4 wherein the sintering is carried out at a temperature of about 50° F below the melting point of the nylon to about 75° F above the melting point of the nylon.
Claim 7
Dependent Claim
64 words
The method of claim 1 wherein the material particles in the coated powder of step (A) comprise a material capable of being magnetized and wherein the resulting shaped structure recovered in step (C) is sintered at a temperature of about 50° F below the melting point of the nylon to about 75° F above the melting point of the nylon and is thereafter magnetized.
Claim 8
Dependent Claim
35 words
The method of claim 1 wherein the material particles of the coated powder of step (A) comprises a bearing material and the shaped structure of step (C) is recovered in the form of a bearing.
Claim 9
Dependent Claim
18 words
The method of claim 1 wherein the coated powder of step (A) is hot pressed in step (B).
Claim 10
Dependent Claim
18 words
The method of claim 1 wherein the coated powder of step (A) is cold rolled in step (B).
Claim 11
Dependent Claim
18 words
The method of claim 1 wherein the coated powder of step (A) is hot rolled in step (B).
Claim 12
Dependent Claim
18 words
The method of claim 1 wherein the coated powder of step (A) is injection molded in step (B).
Claim 13
Dependent Claim
17 words
The method of claim 1 wherein the coated powder of step (A) is extruded in step (B).
Claim 14
Dependent Claim
18 words
The method of claim 1 wherein the coated powder of step (A) is ram extruded in step (B).
Claim 15
Dependent Claim
29 words
The method of claim 1 wherein step (B) is carried out at a temperature of about 68° to about 50° F below the thermal degradation temperature of the nylon.
Claim 16
Dependent Claim
10 words
A shaped structure produced by the method of claim 1.
Claim 17
Independent Claim
137 words
A method of making a shaped structure composed of a nylon copolymer binder, a material in particle form, and an organic polymer modifier, substantially each individual particle of the material being surrounded by the nylon copolymer binder to form a coated powder, the shaped structure having substantially no particle to particle contact and having distribution of the nylon copolymer binder substantially uniform throughout, comprising: A. charging into a forming apparatus the coated powder with the organic polymer modifier to form a modified coated powder, the nylon copolymer being one which adheres to the material particles and being a polyamide of the type which is capable of being drawn into a filament or fiber and in which the recurring amide groups are separated from each other by an alkylene radical having from 3 to 12 contiguous carbon atoms;
Claim 18
Independent Claim
137 words
A method of making a shaped structure composed of a nylon copolymer binder, a material in particle form, and an organic polymer modifier, substantially each individual particle of the material being surrounded by the nylon copolymer binder to form a coated powder, the shaped structure having substantially no particle to particle contact and having distribution of the nylon copolymer binder substantially uniform throughout, comprising: A. charging into a forming apparatus the coated powder with the organic polymer modifier to form a modified coated powder, the nylon copolymer being one which adheres to the material particles and being a polyamide of the type which is capable of being drawn into a filament or fiber and in which the recurring amide groups are separated from each other by an alkylene radical having from 3 to 12 contiguous carbon atoms;
Claim 19
Dependent Claim
143 words
the modified coated powder being substantially in the form of agglomerates of individually coated particles of said material, 2. the coated powder comprising individual particles of the material having a size from about 1 millimicron to about 500 microns and having a substantially uniform coating of the nylon copolymer, the material particles being insoluble in solvents which dissolve the nylon copolymer, the nylon copolymer coating representing at least 2% based on the weight of the modified coated powder, B. compressing the modified coated powder in the forming apparatus at a pressure of about 200 - 100,000 psi at a temperature of about 32° to about 50° F below the thermal degradation temperature of the nylon copolymer and of the organic polymer modifier to bind and form the coated particles into the shaped structure; and C. recovering the shaped structure from the forming apparatus.
Claim 20
Dependent Claim
143 words
the modified coated powder being substantially in the form of agglomerates of individually coated particles of said material, 2. the coated powder comprising individual particles of the material having a size from about 1 millimicron to about 500 microns and having a substantially uniform coating of the nylon copolymer, the material particles being insoluble in solvents which dissolve the nylon copolymer, the nylon copolymer coating representing at least 2% based on the weight of the modified coated powder, B. compressing the modified coated powder in the forming apparatus at a pressure of about 200 - 100,000 psi at a temperature of about 32° to about 50° F below the thermal degradation temperature of the nylon copolymer and of the organic polymer modifier to bind and form the coated particles into the shaped structure; and C. recovering the shaped structure from the forming apparatus.
Claim 21
Dependent Claim
42 words
The method of claim 16 wherein the agglomerates of individually coated particles of step (A) have a size from about one micron up to about 5,000 microns and wherein the organic polymer modifier is present in the coated powder in particle form.
Claim 22
Dependent Claim
116 words
The method of claim 16 wherein the modified coated powder of step (A) is one in which the weight ratio of individual material particles to nylon copolymer coating is in the range of about 98:2 to 5:95, and the weight ratio of the organic polymer modifier to nylon copolymer is in the range of about 20:1 to 1:20, wherein the nylon copolymer is selected from the group consisting of nylon 6/11, nylon 6/12, nylon 6/6--6/6-10, nylon 6/6--6/6-10/6-12, nylon 6/6-9/6-12, nylon 6/6-9/6-10/6-12, nylon 6/11/12, and nylon 6/6-6/12 and the organic polymer modifier is a nylon homopolymer selected from the group consisting of nylon 6, nylon 11, nylon 12, nylon 6--6, nylon 6-9, nylon 6-10, and nylon 6-12.
Claim 23
Dependent Claim
19 words
The method of claim 16 wherein the modified coated powder of step (A) is injection molded in step (B).
Claim 24
Dependent Claim
18 words
The method of claim 16 wherein the modified coated powder of step (A) is extruded in step (B).
Claim 25
Dependent Claim
19 words
The method of claim 16 wherein the modified coated powder of step (A) is ram extruded in step (B).
Claim 26
Dependent Claim
19 words
The method of claim 16 wherein the modified coated powder of step (A) is hot rolled in step (B).
Claim 27
Dependent Claim
47 words
The method of claim 16 wherein the shaped structure recovered in step (C) is sintered at a temperature of about 75° F below the melting point of the nylon copolymer up to about the thermal degradation temperature of the nylon copolymer and of the organic polymer modifier.
Claim 28
Dependent Claim
38 words
The method of claim 23 wherein the sintering is carried out at a temperature of about 50° F below the melting point of the nylon copolymer to about 75° F above the melting point of the nylon copolymer.
Claim 29
Dependent Claim
10 words
A shaped structure produced by the method of claim 16.
References Cited (Backward Citations)
US3194859A
Cited
US3336244A
Cited
US3185589A
Cited
US3421931A
Cited
US3655850A
Cited
US3822177A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-12-26 | 1981-06-27 | 1981-12-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-12-26 | 1985-06-27 | 1985-12-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-12-26 | 1989-06-27 | 1989-12-27 | $7700.00 | Window Closed / Lapsed |