Imidopolysiloxanes and method for making
Assignee: General Electric Co
•
Filing: 1988-03-07
•
Granted: 1988-10-25
•
Expires: 2008-03-07
Abstract
Abstract Imidopolysiloxane gums, resins and fluids are made by equilibrating imidocylclopolysiloxanes with organocyclopolysiloxanes, or cohydrolyzing imidosilanes and organosilanes. The resulting imidopolysiloxanes are useful as temperature and solvent resistant resin and fluids and can be converted to temperature and solvent resistant elastomers.
Inventors
- 👤 Jonathan D. Rich
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 18:21
CPC Classifications
C; C08; C08G; C08G77/00; C08G77/04; C08G77/22; C08G77/26; C07; C07F; C07F7/00; C07F7/02; C07F7/08; C07F7/0834; C07F7/0838; C07F7/21; C08G77/045; C08K; C08K5/00; C08K5/04; C08K5/14
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
94 words
Imidopolysiloxane having an imide to silicon ratio of at least 0.01 and comprising at least three chemically combined siloxy units of the formula, ##STR7## where R and R 1 are selected from the group consisting of C.sub.(1-14) monovalent hydrocarbon radicals and C.sub.(1-14) monovalent radicals selected from the class consisting of haloalkyl, cyanoalkyl, haloaryl, and nitroaryl, R 2 is selected from C.sub.(6-14) trivalent aromatic hydrocarbon radicals, a and b are whole numbers equal to 0 to 3 inclusive, and the sum of a+b has an average value of from about 1 to about 2.67, inclusive.
Claim 2
Dependent Claim
94 words
Imidopolysiloxane having an imide to silicon ratio of at least 0.01 and comprising at least three chemically combined siloxy units of the formula, ##STR7## where R and R 1 are selected from the group consisting of C.sub.(1-14) monovalent hydrocarbon radicals and C.sub.(1-14) monovalent radicals selected from the class consisting of haloalkyl, cyanoalkyl, haloaryl, and nitroaryl, R 2 is selected from C.sub.(6-14) trivalent aromatic hydrocarbon radicals, a and b are whole numbers equal to 0 to 3 inclusive, and the sum of a+b has an average value of from about 1 to about 2.67, inclusive.
Claim 3
Dependent Claim
11 words
The imidopolysiloxane of claim 1, wherein the imidopolysiloxane is a resin.
Claim 4
Dependent Claim
11 words
The imidopolysiloxane of claim 1, wherein the imidopolysiloxane is a fluid.
Claim 5
Dependent Claim
11 words
The imidopolysiloxane of claim 1, wherein the imidopolysiloxane is a gum.
Claim 6
Dependent Claim
56 words
Imidocyclopolysiloxane having the formula, ##STR8## where R and R 1 are selected from C.sub.(1-14) monovalent hydrocarbon radicals and C.sub.(1-14) monovalent radicals selected from the class consisting of haloalkyl, cyanoalkyl, haloaryl and nitroaryl, R 2 is selected from C.sub.(6-14) trivalent aromatic hydrocarbon radicals, and n is an integer having a value of from 3 to 16, inclusive.
Claim 7
Dependent Claim
56 words
Imidocyclopolysiloxane having the formula, ##STR8## where R and R 1 are selected from C.sub.(1-14) monovalent hydrocarbon radicals and C.sub.(1-14) monovalent radicals selected from the class consisting of haloalkyl, cyanoalkyl, haloaryl and nitroaryl, R 2 is selected from C.sub.(6-14) trivalent aromatic hydrocarbon radicals, and n is an integer having a value of from 3 to 16, inclusive.
Claim 8
Dependent Claim
135 words
A heat curable silicone composition comprising by weight, (1) 100 parts of a silicone imidopolysioxane gum having an imide to silicon ratio of at least 0.01, and consisting essentially of chemically combined units of the formula, ##STR9## (2) 50 to 500 parts of filler, and (3) an effective amount of a peroxide curing catalyst, where R and R 1 are selected from the group consisting of C.sub.(1-14) monovalent hydrocarbon radicals and C.sub.(1-14) monovalent radicals selected from the class consisting of haloalkyl, cyanoalkyl, haloaryl, and nitroaryl, R 2 is selected from the group consisting of C.sub.(6-14) trivalent aromatic hydrocarbon radicals, f has a value of from 0 to 3 inclusive, g has a value of from 0 to 3 inclusive, and the sum of f and g has a value of about 1.95 to 2.01, inclusive.
Claim 9
Dependent Claim
135 words
A heat curable silicone composition comprising by weight, (1) 100 parts of a silicone imidopolysioxane gum having an imide to silicon ratio of at least 0.01, and consisting essentially of chemically combined units of the formula, ##STR9## (2) 50 to 500 parts of filler, and (3) an effective amount of a peroxide curing catalyst, where R and R 1 are selected from the group consisting of C.sub.(1-14) monovalent hydrocarbon radicals and C.sub.(1-14) monovalent radicals selected from the class consisting of haloalkyl, cyanoalkyl, haloaryl, and nitroaryl, R 2 is selected from the group consisting of C.sub.(6-14) trivalent aromatic hydrocarbon radicals, f has a value of from 0 to 3 inclusive, g has a value of from 0 to 3 inclusive, and the sum of f and g has a value of about 1.95 to 2.01, inclusive.
Claim 10
Dependent Claim
28 words
A heat curable silicone composition in accordance with claim 6, where the silicone imidopolysiloxane gum is an imidopolydimethylsiloxane having at least 0.01 mole of vinyl, per silicon atom.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-10-25 | 1992-04-25 | 1992-10-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-10-25 | 1996-04-25 | 1996-10-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-10-25 | 2000-04-25 | 2000-10-25 | $7700.00 | Window Closed / Lapsed |