Method for producing silicone rubber moldings having a hard exterior layer
Assignee: DuPont Toray Specialty Materials KK
•
Filing: 1987-09-14
•
Granted: 1988-10-25
•
Expires: 2007-09-14
Abstract
Abstract The present invention provides a method for producing silicone rubber moldings composed of a uniform, smooth and hard exterior layer and a relatively soft interior portion. In accordance with this method the surfaces of the mold cavity are coated with an organohydrogenpolysiloxane containing at least two silicon-bonded hydrogen atoms before the curable organosiloxane used to form the interior portion of the molding is injected into the mold cavity and cured.
Inventors
- 👤 Keiji Yoshida
- 👤 Koji Shimizu
- 👤 Mitsuo Hamada
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 03:19
CPC Classifications
C; C08; C08J; C08J3/00; C08J3/24; C08J3/245; B; B29; B29C; B29C39/00; B29C39/02; B29C39/021; B29C39/025; B29K; B29K2083/00; B29K2083/005; C08J2383/00; C08J2383/04
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
130 words
A method for producing a unitary silicone rubber molding comprising a hard exterior layer and a relatively soft interior portion, said method comprising the sequential steps of (1) coating an organohydrogenpolysiloxane having at least 2 silicone-bonded hydrogen atoms in each molecule on the surface of a mold cavity, (2) filling said mold cavity with a liquid silicone rubber composition that cures in the presence of heat by a reaction selected from the group consisting of hydrosilation type addition reactions conducted in the presence of a platinum catalyst, free reactions initiated by an organoperoxide and condensation reactions involving silicon-bonded hydroxyl groups, and (3) thermally curing said organohydrogenpolysiloxane and said liquid silicone rubber composition by heating the contents of said mold cavity to a temperature of from 50 to 220 degrees C.
Claim 2
Independent Claim
130 words
A method for producing a unitary silicone rubber molding comprising a hard exterior layer and a relatively soft interior portion, said method comprising the sequential steps of (1) coating an organohydrogenpolysiloxane having at least 2 silicone-bonded hydrogen atoms in each molecule on the surface of a mold cavity, (2) filling said mold cavity with a liquid silicone rubber composition that cures in the presence of heat by a reaction selected from the group consisting of hydrosilation type addition reactions conducted in the presence of a platinum catalyst, free reactions initiated by an organoperoxide and condensation reactions involving silicon-bonded hydroxyl groups, and (3) thermally curing said organohydrogenpolysiloxane and said liquid silicone rubber composition by heating the contents of said mold cavity to a temperature of from 50 to 220 degrees C.
Claim 3
Dependent Claim
32 words
A method according to claim 1 where said liquid silicone rubber composition is curable by a platinum-catalyzed hydrosilation reaction or a free radical reaction conducted in the presence of an organic peroxide.
Claim 4
Dependent Claim
138 words
A method according to claim 2 where said liquid silicone rubber composition is curable by a platinum-catalyzed hydrosilation reaction and comprises (A) an organopolysiloxane containing at least 2 lower alkenyl radicals in each molecule, (B) an organohydrogenpolysiloxane having at least 2 silicon-bonded hydrogen atoms in each molecule, in an amount sufficient to provide from 0.1 to 1 mole of silicon-bonded hydrogen atoms for each mole of lower alkenyl radicals present in component (A), and (C) a platinum-type catalyst in an amount equivalent to from 0.1 to 1,000 parts by weight of platinum metal for each 1,000,000 weight parts of the total quantity of components (A) and (B), where the sum of the number of alkenyl radicals in each molecule of component (A) and the number of hydrogen atoms in each molecule of component (B) be at least 5.
Claim 5
Dependent Claim
48 words
A method according to claim 3 where the molar ratio of silicon-bonded hydrogen atoms to alkenyl radicals in said liquid silicone rubber composition is from 0.1 to 1, said alkenyl radicals are vinyl, and said composition is cured at a temperature of from 50 to 220 degrees C.
Claim 6
Dependent Claim
15 words
A method according to claim 1 where the molecular configuration of said organohydrogenpolysiloxane is branched.
Claim 7
Dependent Claim
12 words
A method according to claim 5 where said organohydrogenpolysiloxane is a methylhydrogenpolysiloxane.
Claim 8
Dependent Claim
55 words
A method according to claim 4 where said organopolysiloxane is a diorganopolysiloxane the silicon-bonded hydrocarbon radicals other than vinyl are methyl or a mixture of methyl and 3,3,3-trifluoropropyl, component B is a methylhydrogenpolysiloxane and the molar ratio of silicon-bonded hydrogen atoms to vinyl radicals in said liquid silicone rubber composition is from 0.4 to 0.6.
References Cited (Backward Citations)
US4517238A
Cited
JPS5930932A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-10-25 | 1992-04-25 | 1992-10-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-10-25 | 1996-04-25 | 1996-10-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-10-25 | 2000-04-25 | 2000-10-25 | $7700.00 | Window Closed / Lapsed |