Production of microspheroidal particles of resole resins
Assignee: Unitika Ltd
•
Filing: 1986-10-03
•
Granted: 1988-10-18
•
Expires: 2006-10-03
Abstract
Abstract A resole resin in the form of microspherical particles whose surfaces are partly or entirely covered with a coating of a substantially water-insoluble inorganic salt and which are not larger than 500 μm in size, and a process for producing such resole resin. The resole resin comprises solid particles that are highly heat reactive and can be stored in a stable manner for a prolonged period. The resin particles can be used with good results in all fields of applications (e.g., moldings, laminations and binders) where conventional phenolic resins are used.
Inventors
- 👤 Yoshiaki Echigo
- 👤 Mutsunori Yamao
- 👤 Yoshiyuki Suematu
- 👤 Tadashi Ishikura
- 👤 Keiichi Asami
- 👤 Ritsuko Shidei
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 04:06
CPC Classifications
C; C08; C08J; C08J3/00; C08J3/12; C08J3/124; C08J3/14; C08K; C08K3/00; C08K3/16; C08J2361/00; C08J2361/04; C08J2361/06; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2982; Y10T428/2989
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
104 words
A process for producing a resole resin in the form of microspherical particles where the surfaces of the particles are partly or entirely covered with a coating of a substantially water-insoluble inorganic salt having a solubility in water not greater than about 0.2 g/1,000 ml at 25° C. and where the particles have a particle size not larger than about 500 μm, said process comprising reacting a phenol and an aldehyde in an aqueous medium in the presence of a basic catalyst and said substantially water-insoluble inorganic salt, said substantially water-insoluble inorganic salt being added for stabilization of an emulsion in the reaction system.
Claim 2
Dependent Claim
104 words
A process for producing a resole resin in the form of microspherical particles where the surfaces of the particles are partly or entirely covered with a coating of a substantially water-insoluble inorganic salt having a solubility in water not greater than about 0.2 g/1,000 ml at 25° C. and where the particles have a particle size not larger than about 500 μm, said process comprising reacting a phenol and an aldehyde in an aqueous medium in the presence of a basic catalyst and said substantially water-insoluble inorganic salt, said substantially water-insoluble inorganic salt being added for stabilization of an emulsion in the reaction system.
Claim 3
Dependent Claim
31 words
A process according to claim 1, wherein said substantially water-insoluble inorganic salt is at least one inorganic salt selected from the group consisting of calcium fluoride, magnesium fluoride and strontium fluoride.
Claim 4
Dependent Claim
101 words
A process for producing a resole resin in the form of microspherical particles where the surfaces of the particles are partly or entirely covered with a coating of a substantially water-insoluble inorganic salt having a solubility in water not greater than about 0.2 g/1,000 ml at 25° C. and a flame retardant and where the particles have a particle size not larger than about 500 μm in size, said process comprising reacting a phenol and an aldehyde in an aqueous medium in the presence of a basic catalyst, said substantially water-insoluble inorganic salt and said flame retardant in the reaction system.
Claim 5
Dependent Claim
101 words
A process for producing a resole resin in the form of microspherical particles where the surfaces of the particles are partly or entirely covered with a coating of a substantially water-insoluble inorganic salt having a solubility in water not greater than about 0.2 g/1,000 ml at 25° C. and a flame retardant and where the particles have a particle size not larger than about 500 μm in size, said process comprising reacting a phenol and an aldehyde in an aqueous medium in the presence of a basic catalyst, said substantially water-insoluble inorganic salt and said flame retardant in the reaction system.
Claim 6
Dependent Claim
39 words
A process according to claim 3, wherein said substantially water-insoluble inorganic salt is at least one inorganic salt selected from the group consisting of calcium fluoride, magnesium fluoride and strontium fluoride and wherein the flame retardant is red phosphorus.
Claim 7
Dependent Claim
35 words
A process according to claim 1 or 3, wherein the substantially water-insoluble inorganic salt is present in an amount ranging from about 0.2 to about 10 wt % based on the weight of the phenol.
Claim 8
Dependent Claim
32 words
A process according to claim 1 or 3, wherein the substantially water-insoluble inorganic salt is formed in the reaction system as a result of reaction between two or more water-soluble inorganic salts.
Claim 9
Dependent Claim
70 words
A process according to claim 6, wherein one of said two or more water-soluble inorganic salts is at least one inorganic salt selected from the group consisting of sodium fluoride, potassium fluoride and ammonium fluoride, and said at least one other water-soluble inorganic salt is selected from the group consisting of calcium chloride, calcium sulfate, calcium nitrate, magnesium chloride, magnesium sulfate, magnesium nitrate, strontium chloride, strontium sulfate and strontium nitrate.
Claim 10
Dependent Claim
31 words
A process according to claim 3, wherein the flame retardant is present in an amount ranging from about 0.1 to about 30 wt. % based on the weight of the phenol.
References Cited (Backward Citations)
US3371053A
Cited
US3660321A
Cited
US3755190A
Cited
US4239646A
Cited
US4070331A
Cited
US4454298A
Cited
US4542204A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-10-18 | 1992-04-18 | 1992-10-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-10-18 | 1996-04-18 | 1996-10-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-10-18 | 2000-04-18 | 2000-10-18 | $7700.00 | Window Closed / Lapsed |