Method of making high strength polyethylene fiber
Assignee: Raychem Corp
•
Filing: 1987-04-27
•
Granted: 1988-10-18
•
Expires: 2007-04-27
Abstract
Abstract High strength fibers of a polymeric material and having outstanding tensile strength, Young's modulus values, and creep resistance are prepared by treating a fiber from a polymeric material, which may contain a crosslinking promoter, by (a) crosslinking the polymeric material; (b) heating the fiber to a temperature, T 1 , which (i) in the event the polymer is amorphous, is above the glass transition temperature (Tg) of the polymer and, (ii) in the event the polymer is crystalline, is above the second order transition temperature, T.sub.α.sbsb.c, and below the crystalline melting temperature (Tm) of the polymer; (c) drawing the fiber to a draw ratio of at least about 2 at a rate of at least about 200% per minute and (d) cooling the fiber.
Inventors
- 👤 Joseph K. Kiang
- 👤 Patrick K. C. Tsou
- 👤 Christine E. Vogdes
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 13:00
CPC Classifications
B; B29; B29C; B29C35/00; B29C35/02; B29C35/08; B29C35/10; D; D06; D06M; D06M13/00; D06M13/322; D06M13/35; D06M13/355; D06M13/358; D01; D01D; D01D10/00; D01D5/00; D01D5/12; D01F; D01F6/00; D01F6/02; D01F6/04; D06M10/00; D06M10/001; D06M10/008
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
173 words
A method of making a high strength, high creep recovery polyethylene fiber, comprising the steps of: (a) providing a fiber of polyethylene having a molecular weight distribution Mw/Mn in the range of about 2 to about 10, wherein Mw is the weight average molecular weight and Mn is the number average molecular weight; (b) cross-linking the polyethylene; (c) thereafter heating the fiber to a temperature T 1 , which is above the second order transition temperature T.sub.α.sbsb.c and below the crystalline melting temperature T m of the polyethylene; (d) drawing the heated fiber to a draw ratio of at least about two at a rate of at least about 200% per minute; and (e) cooling the drawn fiber; whereby a fiber is obtained which has a tensile strength of at least about 70,000 psi and which, when subjected to a stress of 15,000 psi at 25° C. for at least 1 hour, thereby causing the fiber to deform, is capable of substantially complete recovery to its undeformed configuration when the stress is removed.
Claim 2
Independent Claim
173 words
A method of making a high strength, high creep recovery polyethylene fiber, comprising the steps of: (a) providing a fiber of polyethylene having a molecular weight distribution Mw/Mn in the range of about 2 to about 10, wherein Mw is the weight average molecular weight and Mn is the number average molecular weight; (b) cross-linking the polyethylene; (c) thereafter heating the fiber to a temperature T 1 , which is above the second order transition temperature T.sub.α.sbsb.c and below the crystalline melting temperature T m of the polyethylene; (d) drawing the heated fiber to a draw ratio of at least about two at a rate of at least about 200% per minute; and (e) cooling the drawn fiber; whereby a fiber is obtained which has a tensile strength of at least about 70,000 psi and which, when subjected to a stress of 15,000 psi at 25° C. for at least 1 hour, thereby causing the fiber to deform, is capable of substantially complete recovery to its undeformed configuration when the stress is removed.
Claim 3
Dependent Claim
13 words
A method according to claim 1, wherein Mw is at least about 50,000.
Claim 4
Dependent Claim
27 words
A method according to claim 1, wherein the fiber is heated in step (c) to a temperature within the range of about 80° to about 130° C.
Claim 5
Dependent Claim
27 words
A method according to claim 1, wherein the fiber is heated in step (c) to a temperature within the range of about 100° to about 130° C.
Claim 6
Dependent Claim
13 words
A method according to claim 1, wherein the polyethylene is crosslinked by irradiation.
Claim 7
Dependent Claim
27 words
A method according to claim 5, wherein the polyethylene is crosslinked by subjecting it to a radiation dose from an electron beam of 2 to 35 Mrads.
Claim 8
Dependent Claim
13 words
A method according to claim 6, wherein the polyethylene contains a crosslinking promoter.
Claim 9
Dependent Claim
12 words
A method according to claim 7, wherein the crosslinking promoter is triallyisocyanurate.
Claim 10
Dependent Claim
18 words
A method according to claim 1, wherein the fiber is drawn at least 8 times its initial length.
Claim 11
Dependent Claim
18 words
A method according to claim 1, wherein the fiber is drawn at least 10 times its initial length.
Claim 12
Dependent Claim
20 words
A method according to claim 1, wherein a fiber having a tensile strength of at least 100,000 psi is obtained.
Claim 13
Dependent Claim
21 words
A method according to claim 1, wherein the fiber is drawn at a rate of at least about 2,000% per minute.
Claim 14
Dependent Claim
21 words
A method according to claim 1, wherein the fiber is drawn at a rate of at least about 15,000% per minute.
Claim 15
Dependent Claim
17 words
A method according to claim 1, wherein the polyethylene is crosslinked by subjecting it to ultra-violet radiation.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-10-18 | 1992-04-18 | 1992-10-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-10-18 | 1996-04-18 | 1996-10-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-10-18 | 2000-04-18 | 2000-10-18 | $7700.00 | Window Closed / Lapsed |