US4776992A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for production of molded composites
Assignee: Novartis Corp
•
Filing: 1986-07-25
•
Granted: 1988-10-11
•
Expires: 2006-07-25
Abstract
Abstract Coated, reinforced composites are prepared by a process in which (i) a liquid composition comprising a photocurable residue and a residue having at least one epoxide group or phenolic hydroxyl group is applied to the surface of a mould, (ii) the composition is exposed to actinic radiation until it solidifies, (iii) reinforcement and a thermosettable composition are applied to the solidified layer, this composition containing an epoxide resin or a phenolic resin, (iv) the assembly is heated to form a cured moulding, and (v) the moulding is removed from the mould. The composition used in the first stage may be a mixture of a photocurable resin and an epoxide or phenolic resin, or a dual-functional resin having, in the same molecule, at least one photocurable group and at least one epoxide or phenolic hydroxyl group, which resin photocures in stage (ii) to produce a thermosettable resin, or it may be an epoxide resin or a phenolic resin together with a curing agent that is activated by heat and one that is activated by actinic radiation.
Inventors
- 👤 Edward Irving
- 👤 Terence J. Smith
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 17:37
CPC Classifications
B; B29; B29C; B29C37/00; B29C37/0025; B29C37/0028; B29C37/0032; C; C08; C08G; C08G18/00; C08G18/06; C08G18/28; C08G59/00; C08G59/14; C08G59/1433; C08G59/1438; C08G59/1455; C08G59/1461; C08G8/00; C08G8/28; C08J; C08J5/00; C08J5/04; C08J5/24; C08J5/241; C08J5/244; C08J5/249; C08L; C08L61/00; C08L61/04; C08L61/06; B29C35/00; B29C35/02; B29C35/08; B29C35/0805; B29C2035/0833; B29C2037/0035; Y; Y10; Y10S; Y10S430/00; Y10S430/148; Y10S522/00; Y10S522/913
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
127 words
A process for the production of a coated, reinforced epoxide or phenolic moulding which comprises (i) applying to the surface of a mould a layer of a liquid composition comprising a photocurable residue and a residue having at least one epoxide group or phenolic hydroxyl group, (ii) exposing the said layer to actinic radiation until solidification occurs, thereby forming on said surface a solidified layer having a thermosettable residue which is an epoxide or phenolic resin, (iii) applying to the solidified layer, in either order or simultaneously, at least one layer of reinforcement and at least one layer of a thermosettable resin that is an epoxide or phenolic resin, (iv) heating the assembly to form a cured moulding and (v) removing the cured moulding from the mould.
Claim 2
Dependent Claim
127 words
A process for the production of a coated, reinforced epoxide or phenolic moulding which comprises (i) applying to the surface of a mould a layer of a liquid composition comprising a photocurable residue and a residue having at least one epoxide group or phenolic hydroxyl group, (ii) exposing the said layer to actinic radiation until solidification occurs, thereby forming on said surface a solidified layer having a thermosettable residue which is an epoxide or phenolic resin, (iii) applying to the solidified layer, in either order or simultaneously, at least one layer of reinforcement and at least one layer of a thermosettable resin that is an epoxide or phenolic resin, (iv) heating the assembly to form a cured moulding and (v) removing the cured moulding from the mould.
Claim 3
Dependent Claim
122 words
A process according to claim 1, in which the composition comprises a solely photocurable resin with a solely thermosettable epoxide or phenolic resin; a dual-functional resin having, in the same molecule, at least one photocurable group and at least one epoxide or phenolic hydroxyl group, which resin photocures in stage (ii) to produce a thermosettable resin; a mixture of a said dual-functional resin and a solely photocurable resin or a solely thermosettable epoxide or phenolic resin; a mixture of a said dual-functional resin, a solely photocurable resin and a solely thermosettable epoxide or phenolic resin; or an epoxide resin or phenolic resin together with a curing agent which is activated by heat and a curing agent which is activated by actinic radiation.
Claim 4
Dependent Claim
32 words
A process according to claim 1, in which the resin used in stage (iii) is of the same type as the thermosettable resin used in stage (i) or produced in stage (ii).
Claim 5
Dependent Claim
43 words
A process according to claim 1, in which the photocurable resin has at least one unsaturated ester group of formula CH.sub.2 ═C(R.sup.1)COO-- I where R 1 represents a hydrogen, chlorine or bromine atom or an alkyl group of 1 to 4 carbon atoms.
Claim 6
Dependent Claim
18 words
A process according to claim 4, in which R 1 represents a hydrogen atom or a methyl group.
Claim 7
Dependent Claim
27 words
A process according to claim 4, in which the photocurable resin has at least two groups of formula I and a molecular weight of up to 10000.
Claim 8
Dependent Claim
59 words
A process according to claim 4, in which the photocurable resin is an acrylate or methacrylate of a monohydric alcohol or a full or partial ester of acrylic or methacrylic acid with a glycol or higher functional polyol, or a 2-hydroxypropyl ester formed by reaction of a compound containing one or more glycidyl groups with acrylic or methacrylic acid.
Claim 9
Dependent Claim
50 words
A process according to claim 1, in which the phenolic resin is a resole or novolak derived from phenol and formaldehyde; the epoxide resin is a diglycidyl ether of a dihydric phenol or alcohol, a polyglycidyl ether of a phenol-formaldehyde novolak or a bisphenol-formaldehyde novolak, or a N-glycidylated aromatic amine.
Claim 10
Dependent Claim
35 words
A process according to claim 1, in which the liquid composition contains a dual-functional resin having at least one 1,2-epoxide group or phenolic hydroxyl group and at least one substituted ester group of formula I.
Claim 11
Dependent Claim
31 words
A process according to claim 1, in which the liquid composition comprises an epoxide resin or a phenolic resin together with a curing agent therefor which is activated by actinic radiation.
Claim 12
Dependent Claim
24 words
A process according to claim 10, in which the curing agent is an aromatic iodonium, sulfonium, sulfoxonium or iodosyl salt or a ferrocenium salt.
Claim 13
Dependent Claim
34 words
A process according to claim 1, in which the liquid composition is irradiated in the presence of a catalyst which on irradiation gives an excited state which leads to the formation of free radicals.
Claim 14
Dependent Claim
46 words
A process according to claim 12, in which the catalyst is an alpha-halogen substituted acetophenone, a benzophenone, an O-alkoxycarbonyl derivative of an oxime of benzil or 1-phenylpropane-1,2-dione, a benzil ketal, a mixture of a phenothiazine dye or a quinoxaline with an electron donor, or a titanocene.
Claim 15
Dependent Claim
44 words
A process according to claim 1, in which a phenolic resole is used and cure is effected in the presence of an acidic curing agent, or in which a phenolic novolak is used and cure is effected in the presence of a formaldehyde donor.
Claim 16
Dependent Claim
50 words
A process according to claim 1, in which an epoxide resin is used together with a curing agent therefor which is an aromatic primary or secondary amine, an imidazole, an aromatic group-substituted urea, an amidine or a complex of boron trifluoride or trichloride with an aliphatic, cycloaliphatic, or heterocyclic amine.
Claim 17
Dependent Claim
14 words
A process according to claim 1, in which the reinforcement is in fibrous form.
Claim 18
Dependent Claim
24 words
A process according to claim 16, in which the fibrous reinforcement is in the form of loose fibres or a woven or nonwoven fabric.
Claim 19
Dependent Claim
16 words
A process according to claim 17, in which the reinforcement is pre-impregnated with the thermosettable resin.
Claim 20
Dependent Claim
19 words
A process according to claim 1, in which stage (ii) is effected with actinic radiation of wavelength 200-600 nm.
References Cited (Backward Citations)
US3848045A
Cited
US4097569A
Cited
US4367192A
Cited
US4242415A
Cited
US4350739A
Cited
US4338269A
Cited
DE3140316A1
Cited
US4414173A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-10-11 | 1992-04-11 | 1992-10-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-10-11 | 1996-04-11 | 1996-10-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-10-11 | 2000-04-11 | 2000-10-11 | $7700.00 | Window Closed / Lapsed |