Method for making rare earth-containing magnets
Assignee: Union Oil Company of California
•
Filing: 1986-04-28
•
Granted: 1988-10-11
•
Expires: 2006-04-28
Abstract
Abstract Compositions for the production of rare earth-ferromagnetic-metal permanent magnets comprise mixtures of rare earth-ferromagnetic metal alloy powder and a lesser amount of a powdered second-phase sintering aid, wherein there is added up to about 2 percent by weight of a particulate refractory oxide, carbide, or nitride additive. Permanent magnets are prepared by mixing the components, aligning the mixture in a magnetic field, pressing and sintering. The refractory material inhibits grain growth in the second phase during sintering, improving the magnetic properties of the major phase.
Inventors
- 👤 Mohammad H. Ghandehari
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 15:35
CPC Classifications
H; H01; H01F; H01F1/00; H01F1/01; H01F1/03; H01F1/032; H01F1/04; H01F1/047; H01F1/053; H01F1/055; H01F1/0555; H01F1/0557
Claims Analysis
Total Claims: 24
Claim 1
Independent Claim
97 words
A method for producing rare earth-ferromagnetic metal alloy permanent magnets, comprising the steps of: (a) mixing a particulate additive material selected from the group consisting of refractory oxides, carbides, and nitrides, in an amount which provides about 0.1 percent to about 2 percent by weight additive material in the mixture, with a major amount of a particulate rare earth-ferromagnetic metal alloy and a minor amount of a particulate sintering aid alloy; (b) aligning magnetic domains of the mixture in a magnetic field; (c) compacting the aligned mixture to form a shape; and (d) sintering the compacted shape.
Claim 2
Independent Claim
97 words
A method for producing rare earth-ferromagnetic metal alloy permanent magnets, comprising the steps of: (a) mixing a particulate additive material selected from the group consisting of refractory oxides, carbides, and nitrides, in an amount which provides about 0.1 percent to about 2 percent by weight additive material in the mixture, with a major amount of a particulate rare earth-ferromagnetic metal alloy and a minor amount of a particulate sintering aid alloy; (b) aligning magnetic domains of the mixture in a magnetic field; (c) compacting the aligned mixture to form a shape; and (d) sintering the compacted shape.
Claim 3
Dependent Claim
23 words
The method defined in claim 1 wherein all components of the mixture have been reduced to particle sizes less than about 10 microns.
Claim 4
Dependent Claim
21 words
The method defined in claim 1 wherein the sintering aid comprises up to about 15 percent by weight of the mixture.
Claim 5
Dependent Claim
20 words
The method defined in claim 3 wherein the sintering aid comprises about 10 percent to about 15 percent by weight.
Claim 6
Dependent Claim
19 words
The method defined in claim 1 wherein, during sintering, at least a portion of the sintering aid is liquid.
Claim 7
Dependent Claim
32 words
The method defined in claim 1 wherein the rare earth-ferromagnetic metal alloy has an empirical formula corresponding approximately to RM 5 , wherein R is rare earth and M is ferromagnetic metal.
Claim 8
Dependent Claim
10 words
The method defined in claim 6 wherein R is praseodymium.
Claim 9
Dependent Claim
10 words
The method defined in claim 6 wherein M is cobalt.
Claim 10
Dependent Claim
32 words
The method defined in claim 1 wherein the rare earth-ferromagnetic metal alloy has an empirical formula corresponding approximately to RM 2 , wherein R is rare earth and M is ferromagnetic metal.
Claim 11
Dependent Claim
34 words
The method defined in claim 1 wherein the rare earth-ferromagnetic metal alloy has an empirical formula corresponding approximately to R 2 M 7 , wherein R is rare earth and M is ferromagnetic metal.
Claim 12
Dependent Claim
34 words
The method defined in claim 1 wherein the rare earth-ferromagnetic metal alloy has an empirical formula corresponding approximately to R 2 M 17 , wherein R is rare earth and M is ferromagnetic metal.
Claim 13
Dependent Claim
38 words
The method defined in claim 1 wherein the sintering aid is an alloy containing an excess of rare earth over the amount required to form RM 5 , wherein R is rare earth and M is ferromagnetic metal.
Claim 14
Dependent Claim
32 words
The method defined in claim 1 wherein the sintering aid is an alloy of a ferromagnetic metal and a rare earth selected from the group consisting of praseodymium, samarium, and mixtures thereof.
Claim 15
Dependent Claim
19 words
The method defined in claim 1 wherein the sintering aid is an alloy of rare earth metal and cobalt.
Claim 16
Dependent Claim
13 words
The method defined in claim 1 wherein the additive material is an oxide.
Claim 17
Dependent Claim
26 words
The method defined in claim 1 wherein the additive material is an oxide of a metal selected from the group consisting of chromium, aluminum, and magnesium.
Claim 18
Independent Claim
128 words
A method for producing praseodymium-cobalt based magnets, comprising the steps of: (a) mixing together the components: (i) a particulate praseodymium-cobalt alloy, having an empirical formula corresponding approximately to PrCo 5 ; (ii) a lesser amount of a particulate sintering aid alloy selected from the group consisting of praseodymium-cobalt alloys, samarium-cobalt alloys, praseodymium-samarium-cobalt alloys, and mixtures thereof; and (iii) a particulate additive selected from the group consisting of refractory oxides, carbides, and nitrides, in amounts to comprise about 0.1 to about 2 percent by weight of the mixture; (b) aligning magnetic domains of the mixture in a magnetic field; (c) compacting the aligned mixture to form a shape; and (d) sintering the compacted shape at temperatures which cause at least a portion of the sintering aid to become liquid.
Claim 19
Independent Claim
128 words
A method for producing praseodymium-cobalt based magnets, comprising the steps of: (a) mixing together the components: (i) a particulate praseodymium-cobalt alloy, having an empirical formula corresponding approximately to PrCo 5 ; (ii) a lesser amount of a particulate sintering aid alloy selected from the group consisting of praseodymium-cobalt alloys, samarium-cobalt alloys, praseodymium-samarium-cobalt alloys, and mixtures thereof; and (iii) a particulate additive selected from the group consisting of refractory oxides, carbides, and nitrides, in amounts to comprise about 0.1 to about 2 percent by weight of the mixture; (b) aligning magnetic domains of the mixture in a magnetic field; (c) compacting the aligned mixture to form a shape; and (d) sintering the compacted shape at temperatures which cause at least a portion of the sintering aid to become liquid.
Claim 20
Dependent Claim
20 words
The method defined in claim 17 wherein all components of step (a) have particle sizes less than about 10 microns.
Claim 21
Dependent Claim
25 words
The method defined in claim 17 wherein the sintering aid comprises about 10 to about 15 percent by weight of the mixture of step (a).
Claim 22
Dependent Claim
34 words
The method defined in claim 17 wherein the sintering aid alloy contains an excess of rare earth over an amount required to form RCo 5 , wherein R is praseodymium, samarium, or mixtures thereof.
Claim 23
Dependent Claim
12 words
The method defined in claim 17 wherein the additive is an oxide.
Claim 24
Dependent Claim
25 words
The method defined in claim 17 wherein the additive is an oxide of a metal selected from the group consisting of chromium, aluminum, and magnesium.
References Cited (Backward Citations)
US3701695A
Cited
US4081297A
Cited
US4135953A
Cited
US4043845A
Cited
US4211585A
Cited
US4497672A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-10-11 | 1992-04-11 | 1992-10-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-10-11 | 1996-04-11 | 1996-10-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-10-11 | 2000-04-11 | 2000-10-11 | $7700.00 | Window Closed / Lapsed |