Fluoroaluminosilicate glass powder for dental glass ionomer cement
Assignee: GC Corp
•
Filing: 1986-08-21
•
Granted: 1988-10-04
•
Expires: 2006-08-21
Abstract
Abstract A fluoroaluminosilicate glass powder for dental glass ionomer cement, a surface of which is treated with a fluoride in an amount of from 0.01 to 5 parts by weight based on 100 parts by weight of the glass powder, is disclosed. The fluoroaluminosilicate glass powder of the invention is improved in not only physical properties such as crushing strength but also mixing workability without impairing the inherent characteristics thereof for the dental use.
Inventors
- 👤 Shoji Akahane
- 👤 Kazuo Hirota
- 👤 Kentaro Tomioka
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 22:03
CPC Classifications
C; C03; C03C; C03C3/00; C03C3/04; C03C3/062; A; A61; A61K; A61K6/00; A61K6/20; A61K6/30; A61K6/80; A61K6/884; A61K6/887; A61K6/889; C03C17/00; C03C17/22; C03C3/076; C03C3/11; C03C3/112; C03C2217/00; C03C2217/20; C03C2217/28; C03C2217/284; C03C2217/285; C03C2218/00; C03C2218/10; C03C2218/11; C03C2218/111; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2982; Y10T428/2991; Y10T428/2993; Y10T428/2996
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
186 words
A fluoroaluminosilicate glass powder suitable as a dental glass ionomer cement, which is produced by treating the surface of a fluoroaluminosilicate glass powder with a metal fluoride or fluorocomplex salt in an amount of from about 0.01 to 5 parts by weight of said metal fluoride or fluorocomplex salt based on 100 parts by weight of the glass powder; and wherein said fluoroaluminosilicate glass powder comprises 25 to 50 weight percent of silica, 15 to 40 weight percent of alumina, 10 to 40 weight percent of fluoride and 0 to 20% of a phosphate; and wherein said metal fluoride is selected from the group consisting of a fluoride of zinc, aluminum, tin, zirconium acidic sodium; and said fluorocomplex salt is selected from the group consisting of potassium tetrafluoroberyllate, ammonium tetrafluoroberyllate, sodium hexafluorozirconate, potassium hexafluorozirconate, potassium heptafluoroniobate, potassium heptafluorotantalate, sodium hexafluorosilicate, potassium heptafluorosilicate, lithium hexafluorosilicate, ammonium hexafluorosilicate, iron hexafluorosilicate, nickel hexafluorosilicate, zinc hexafluorosilicate, tin hexafluorosilicate, magnesium hexafluorosilicate, sodium hexafluorotitanate, potassium hexafluorotitanate, ammonium hexafluorotitanate, nickel hexafluorotitanate, potassium tetrafluoroborate, ammonium tetrafluoroborate, manganese tetrafluoroborate, iron tetrafluoroborate, nickel tetrafluoroborate, tin tetrafluoroborate, indium tetrafluoroborate, zinc tetrafluoroborate, antimony tetrafluoroborate, and boron trifluoride-acetate complex.
Claim 2
Dependent Claim
186 words
A fluoroaluminosilicate glass powder suitable as a dental glass ionomer cement, which is produced by treating the surface of a fluoroaluminosilicate glass powder with a metal fluoride or fluorocomplex salt in an amount of from about 0.01 to 5 parts by weight of said metal fluoride or fluorocomplex salt based on 100 parts by weight of the glass powder; and wherein said fluoroaluminosilicate glass powder comprises 25 to 50 weight percent of silica, 15 to 40 weight percent of alumina, 10 to 40 weight percent of fluoride and 0 to 20% of a phosphate; and wherein said metal fluoride is selected from the group consisting of a fluoride of zinc, aluminum, tin, zirconium acidic sodium; and said fluorocomplex salt is selected from the group consisting of potassium tetrafluoroberyllate, ammonium tetrafluoroberyllate, sodium hexafluorozirconate, potassium hexafluorozirconate, potassium heptafluoroniobate, potassium heptafluorotantalate, sodium hexafluorosilicate, potassium heptafluorosilicate, lithium hexafluorosilicate, ammonium hexafluorosilicate, iron hexafluorosilicate, nickel hexafluorosilicate, zinc hexafluorosilicate, tin hexafluorosilicate, magnesium hexafluorosilicate, sodium hexafluorotitanate, potassium hexafluorotitanate, ammonium hexafluorotitanate, nickel hexafluorotitanate, potassium tetrafluoroborate, ammonium tetrafluoroborate, manganese tetrafluoroborate, iron tetrafluoroborate, nickel tetrafluoroborate, tin tetrafluoroborate, indium tetrafluoroborate, zinc tetrafluoroborate, antimony tetrafluoroborate, and boron trifluoride-acetate complex.
Claim 3
Dependent Claim
22 words
The fluoroaluminosilicate glass powder as claimed in claim 1, wherein said glass powder is capable of passing through a number 80 sieve.
Claim 4
Dependent Claim
22 words
The fluoroaluminosilicate glass powder as claimed in claim 2, wherein said glass powder is capable of passing through a number 150 sieve.
Claim 5
Dependent Claim
81 words
The fluoroaluminosilicate glass powder of claim 1, wherein said fluoroaluminosilicate glass having the surface thereof treated with a metal fluoride or fluorocomplex salt is prepared by melting a composition containing from 25 to 50 weight percent of said silica, from 15 to 40 weight percent of said alumina, from 10 to 40 weight percent of said fluoride, and from 0 to 20 percent by weight of said phosphate at a temperature of 1,000° C. or higher, followed by cooling and grinding.
Claim 6
Dependent Claim
23 words
The fluoroaluminosilicate glass powder as claimed in claim 1, wherein said phosphate is an orthophosphate, a pyrophosphate, or a monobasic or dibasic phosphate.
Claim 7
Dependent Claim
35 words
The fluoroaluminosilicate glass powder as claimed in claim 1, wherein said phosphate is selected from the group consisting of a phosphate of an alkali metal, an alkaline earth metal, zinc, aluminum, yttrium, lanthanum and zirconium.
Claim 8
Dependent Claim
26 words
The fluoroaluminosilicate glass powder as claimed in claim 1, wherein said glass powder consists essentially of particles having a maximum diameter of 25 μm or less.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-10-04 | 1992-04-04 | 1992-10-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-10-04 | 1996-04-04 | 1996-10-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-10-04 | 2000-04-04 | 2000-10-04 | $7700.00 | Window Closed / Lapsed |