Slide contacting member and production method therefor
Assignee: Mazda Motor Corp
•
Filing: 1987-04-13
•
Granted: 1988-09-27
•
Expires: 2007-04-13
Abstract
Abstract A slide contacting member which is subjected to slide contact with a counter member. The slide contacting member is made by applying a hard layer, e.g., chromium, onto a parent material, irradiating the hard layer with a high energy density laser beam onto the plating under conditions such that concavities having a softened layer are formed thereon, the concavities being used to keep oil during the contact with the other member. The hard layer is finished grinded after irradiation.
Inventors
- 👤 Kouji Tarumoto
- 👤 Junichi Yamamoto
- 👤 Yoshifumi Yamamoto
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 13:27
CPC Classifications
F; F16; F16J; F16J10/00; F16J10/02; F16J10/04; B; B23; B23K; B23K26/00; B23K26/14; B23K26/1435; B23K26/1436; B23K26/1462; B23K26/1464; B23K26/1476; B23K26/352; B23K26/355; B23K35/00; B23K35/22; B23K35/24; B23K35/30; B23K35/3053; B23K35/308; F02; F02B; F02B77/00; F02B77/02; F16J9/00; F16J9/26
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
129 words
A production method for a slide contacting member with improved abrasion resistance, comprising the following steps; applying a hard layer to a surface of a parent material by plating chromium thereon; irradiating a laser beam having a high energy density at points dispersed on said hard layer in a discrete manner while applying pressurized assist gas to each of said points to be irradiated, wherein irradiation conditions of said laser beam and the pressure of the assist gas are so chosen as to form concavities for keeping oil therein, each of which concavities has a softened layer on the concave surface thereof, said softened layer having hardness in a range from 500 to 900 of the Vickers hardness; and grinding said hard layer for finishing after said irradiating step.
Claim 2
Dependent Claim
129 words
A production method for a slide contacting member with improved abrasion resistance, comprising the following steps; applying a hard layer to a surface of a parent material by plating chromium thereon; irradiating a laser beam having a high energy density at points dispersed on said hard layer in a discrete manner while applying pressurized assist gas to each of said points to be irradiated, wherein irradiation conditions of said laser beam and the pressure of the assist gas are so chosen as to form concavities for keeping oil therein, each of which concavities has a softened layer on the concave surface thereof, said softened layer having hardness in a range from 500 to 900 of the Vickers hardness; and grinding said hard layer for finishing after said irradiating step.
Claim 3
Dependent Claim
136 words
A production method for a slide contacting member with improved abrasion resistance, comprising the following steps; applying a hard layer to a surface of a parent material by plating chromium alloy which includes a suitable amount of molybdenum; irradiating a laser beam having a high energy density at points dispersed on said hard layer in a discrete manner while applying pressurized assist gas to each of said points to be irradiated, wherein irradiation conditions of said laser beam and the pressure of the assist gas are so chosen as to form concavities for keeping oil therein, each of which concavities has a softened layer on the concave surface thereof, said soften layer having hardness in a range from 500 to 900 of the Vickers hardness; and grinding said hard layer for finishing after said irradiating step.
Claim 4
Dependent Claim
136 words
A production method for a slide contacting member with improved abrasion resistance, comprising the following steps; applying a hard layer to a surface of a parent material by plating chromium alloy which includes a suitable amount of molybdenum; irradiating a laser beam having a high energy density at points dispersed on said hard layer in a discrete manner while applying pressurized assist gas to each of said points to be irradiated, wherein irradiation conditions of said laser beam and the pressure of the assist gas are so chosen as to form concavities for keeping oil therein, each of which concavities has a softened layer on the concave surface thereof, said soften layer having hardness in a range from 500 to 900 of the Vickers hardness; and grinding said hard layer for finishing after said irradiating step.
Claim 5
Dependent Claim
165 words
A production method for a slide contacting member with improved abrasion resistance, comprising the following steps; applying a hard layer to a surface of a parent material by plating chromium thereon; irradiating a laser beam having a high energy density at points dispersed on said hard plated layer in a discrete manner while applying pressurized assist gas to each of said points to be irradiated, wherein irradiation conditions of said laser beam and the pressure of the assist gas are so chosen as to form concavities for keeping oil therein, each of which concavities has a softened layer on the concave surface thereof; said laser beams being controlled so as to form concavities, each having a diameter falling within a range from 100 to 150 μm, on the hard plated layer in cooperation with said pressurized assist gas, said softened layer having hardness in a range from 500 to 900 of the Vickers hardness; and grinding said hard layer for finishing after said irradiating step.
Claim 6
Dependent Claim
165 words
A production method for a slide contacting member with improved abrasion resistance, comprising the following steps; applying a hard layer to a surface of a parent material by plating chromium thereon; irradiating a laser beam having a high energy density at points dispersed on said hard plated layer in a discrete manner while applying pressurized assist gas to each of said points to be irradiated, wherein irradiation conditions of said laser beam and the pressure of the assist gas are so chosen as to form concavities for keeping oil therein, each of which concavities has a softened layer on the concave surface thereof; said laser beams being controlled so as to form concavities, each having a diameter falling within a range from 100 to 150 μm, on the hard plated layer in cooperation with said pressurized assist gas, said softened layer having hardness in a range from 500 to 900 of the Vickers hardness; and grinding said hard layer for finishing after said irradiating step.
Claim 7
Dependent Claim
194 words
A production method for a slide contacting member with improved abrasion resistance, comprising the following steps; applying a hard layer to a surface of a parent material by plating chromium alloy which includes a suitable amount of molybdenum thereon; irradiating a laser beam having a high energy density at points dispersed on said hard plated layer in a discrete manner while applying pressurized assist gas to each of said points to be irradiated, wherein irradiation conditions of said laser beam and the pressure of the assist gas are so chosen as to form concavities for keeping oil, each of which concavities has a softened layer on the concave surface thereof, said laser beams being controlled so as to form concavities each having a diameter falling within a range from 100 to 150 μm, on the hard plated layer in cooperation with said pressurized assist gas, said assist gas being the nitrogen gas pressurized at a pressure falling within a range from 1.0 to 3.0 kg/cm 2 , said softened layer having hardness in a range from 500 to 900 of the Vickers hardness; and grinding said hard plated layer for finishing after irradiating step.
Claim 8
Dependent Claim
194 words
A production method for a slide contacting member with improved abrasion resistance, comprising the following steps; applying a hard layer to a surface of a parent material by plating chromium alloy which includes a suitable amount of molybdenum thereon; irradiating a laser beam having a high energy density at points dispersed on said hard plated layer in a discrete manner while applying pressurized assist gas to each of said points to be irradiated, wherein irradiation conditions of said laser beam and the pressure of the assist gas are so chosen as to form concavities for keeping oil, each of which concavities has a softened layer on the concave surface thereof, said laser beams being controlled so as to form concavities each having a diameter falling within a range from 100 to 150 μm, on the hard plated layer in cooperation with said pressurized assist gas, said assist gas being the nitrogen gas pressurized at a pressure falling within a range from 1.0 to 3.0 kg/cm 2 , said softened layer having hardness in a range from 500 to 900 of the Vickers hardness; and grinding said hard plated layer for finishing after irradiating step.
References Cited (Backward Citations)
JPS5925841A
Cited
US4200382A
Cited
US4322600A
Cited
US4628179A
Cited
JPS603431A
Cited
US4686349A
Cited
DE3608286A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-09-27 | 1992-03-28 | 1992-09-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-09-27 | 1996-03-28 | 1996-09-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-09-27 | 2000-03-28 | 2000-09-27 | $7700.00 | Window Closed / Lapsed |