US4774263A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for the production of elastic molded articles
Assignee: Bayer AG
•
Filing: 1982-11-22
•
Granted: 1988-09-27
•
Expires: 2002-11-22
Abstract
Abstract Elastic molded articles having a closed surface layer are made from polyurea elastomers by the reaction injection molding technique. These polyurea elastomers are prepared from a polyisocyanate in which all of the isocyanate groups are aromatically bound, a polyether and a diamine. The polyether has at least two isocyanate-reactive groups and a molecular weight from 1800 to 12,000. At least 50% of the isocyanate-reactive groups in the polyether are pjrimary and/or secondary amino groups. The diamine has a molecular weight from 108 to 400 and primary and/or secondary aromatically bound amino groups. Known auxiliary agents and additives may also be employed.
Inventors
- 👤 Christian Weber
- 👤 Hans Wirtz
- 👤 Klaus Seel
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 19:01
CPC Classifications
C; C08; C08G; C08G18/00; C08G18/06; C08G18/28; C08G18/65; C08G18/66; C08G18/6666; C08G18/667; C08G18/6681; C08G18/6685; C08G18/40; C08G18/48; C08G18/50; C08G18/5021; C08G18/5024; C08G2110/00; C08G2110/0033; C08G2110/0041; C08G2110/0066; C08G2120/00
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
100 words
A process for the production of elastic molded articles having a closed surface layer by reacting as a one-shot system a mixture comprising (a) a diisocyanate and/or polyisocyanate in which the isocyanate groups are aromatically bound, (b) a polyether having at least two isocyanate-reactive groups and a molecular weight from 1800 to 12,000 in which at least 50% of the isocyanate-reactive groups are primary and/or secondary amine groups, (c) a diamine having a molecular weight from 108 to 400 and primary and/or secondary aromatically bound amino groups and (d) an internal mold release agent by a reaction injection molding technique.
Claim 2
Dependent Claim
100 words
A process for the production of elastic molded articles having a closed surface layer by reacting as a one-shot system a mixture comprising (a) a diisocyanate and/or polyisocyanate in which the isocyanate groups are aromatically bound, (b) a polyether having at least two isocyanate-reactive groups and a molecular weight from 1800 to 12,000 in which at least 50% of the isocyanate-reactive groups are primary and/or secondary amine groups, (c) a diamine having a molecular weight from 108 to 400 and primary and/or secondary aromatically bound amino groups and (d) an internal mold release agent by a reaction injection molding technique.
Claim 3
Dependent Claim
22 words
The process of claim 1 wherein the internal mold release agent is a salt of oleic acid or tall oil fatty acid.
Claim 4
Independent Claim
109 words
A method for making a reaction injection molded elastomer which will release from its mold without the presence of an externally applied mold release agent comprising injecting exactly two streams via a RIM machine into a mold cavity of the desired configuration, a formulation comprising in the first stream primary or secondary amine terminated polyethers of from 1800 to 12,000 molecular weight having greater than 50% of their active hydrogens in the form of amine hydrogens, a diamine having a molecular weight of from 108 to 400 and primary and/or secondary aromatically bound amino groups and an internal mold release agent, and in the second stream an aromatic polyisocyanate.
Claim 5
Independent Claim
109 words
A method for making a reaction injection molded elastomer which will release from its mold without the presence of an externally applied mold release agent comprising injecting exactly two streams via a RIM machine into a mold cavity of the desired configuration, a formulation comprising in the first stream primary or secondary amine terminated polyethers of from 1800 to 12,000 molecular weight having greater than 50% of their active hydrogens in the form of amine hydrogens, a diamine having a molecular weight of from 108 to 400 and primary and/or secondary aromatically bound amino groups and an internal mold release agent, and in the second stream an aromatic polyisocyanate.
Claim 6
Dependent Claim
20 words
A method as in claim 3 wherein the amine terminated polyether has a molecular weight of from 2000 to 8,000.
Claim 7
Dependent Claim
102 words
A RIM elastomer which will release from its mold without the presence of an externally applied mold release agent made by injecting exactly two streams via a RIM machine into a mold cavity of the desired configuration, a formulation comprising in the first stream primary or secondary terminated polyethers of from 1800 to 12,000 molecular weight having greater than 50% of their active hydrogens in the form of amine hydrogens, a diamine having a molecular weight from 108 to 400 and primary and/or secondary aromatically bound amino groups and an internal mold release agent, and in the second stream an aromatic polyisocyanate.
Claim 8
Dependent Claim
102 words
A RIM elastomer which will release from its mold without the presence of an externally applied mold release agent made by injecting exactly two streams via a RIM machine into a mold cavity of the desired configuration, a formulation comprising in the first stream primary or secondary terminated polyethers of from 1800 to 12,000 molecular weight having greater than 50% of their active hydrogens in the form of amine hydrogens, a diamine having a molecular weight from 108 to 400 and primary and/or secondary aromatically bound amino groups and an internal mold release agent, and in the second stream an aromatic polyisocyanate.
Claim 9
Dependent Claim
20 words
A method as in claim 5 wherein the amine terminated polyether has a molecular weight of from 2,000 to 8,000.
Claim 10
Independent Claim
110 words
A method for making a RIM elastomer which will release from its mold without the presence of an externally applied mold release agent comprising injecting exactly two streams via a RIM machine into a mold cavity of the desired configuration, a formulation comprising in the first stream primary or secondary amine terminated polyethers having a molecular weight of from 1,800 to 12,000 and having greater than 50% of their active hydrogens in the form of amine hydrogens, a diamine having a molecular weight of from 108 to 400 and primary and/or secondary aromatically bound amino groups and an internal mold release agent, and in the second stream an aromatic polyisocyanate.
Claim 11
Independent Claim
110 words
A method for making a RIM elastomer which will release from its mold without the presence of an externally applied mold release agent comprising injecting exactly two streams via a RIM machine into a mold cavity of the desired configuration, a formulation comprising in the first stream primary or secondary amine terminated polyethers having a molecular weight of from 1,800 to 12,000 and having greater than 50% of their active hydrogens in the form of amine hydrogens, a diamine having a molecular weight of from 108 to 400 and primary and/or secondary aromatically bound amino groups and an internal mold release agent, and in the second stream an aromatic polyisocyanate.
Claim 12
Dependent Claim
107 words
A RIM elastomer which will release from its mold without the presence of an externally applied mold release agent made by injecting exactly two streams via a RIM machine into a mold cavity of the desired configuration, a formulation comprising in the first stream primary or secondary amine terminated polyethers having a molecular weight of from 1,800 to 12,000 and having greater than 50% of their active hydrogens in the form of amine hydrogens, a diamine having a molecular weight of from 108 and 400 and primary and/or secondary aromatically bound amino groups and an internal mold release agent, and in the second stream an aromatic polyisocyanate.
Claim 13
Dependent Claim
107 words
A RIM elastomer which will release from its mold without the presence of an externally applied mold release agent made by injecting exactly two streams via a RIM machine into a mold cavity of the desired configuration, a formulation comprising in the first stream primary or secondary amine terminated polyethers having a molecular weight of from 1,800 to 12,000 and having greater than 50% of their active hydrogens in the form of amine hydrogens, a diamine having a molecular weight of from 108 and 400 and primary and/or secondary aromatically bound amino groups and an internal mold release agent, and in the second stream an aromatic polyisocyanate.
Claim 14
Dependent Claim
17 words
A method as in claim 3 wherein the amine terminated polyether has a functionality of about 2-6.
Claim 15
Dependent Claim
17 words
A method as in claim 9 wherein the functionality of the amine terminated polyethers is about 2-3.
Claim 16
Dependent Claim
20 words
A method as in claim 3 where the internal mold release agent comprises a dimethyl siloxane with organic acid groups.
Claim 17
Dependent Claim
17 words
A method as in claim 5 wherein the amine terminated polyether has a functionality of about 2-6.
Claim 18
Dependent Claim
17 words
A method as in claim 12 wherein the amine terminated polyether has a functionality of about 2-3.
Claim 19
Dependent Claim
20 words
A method as in claim 5 where the internal mold release agent comprises a dimethyl siloxane with organic acid groups.
References Cited (Backward Citations)
GB1049644A
Cited
GB969114A
Cited
US3726952A
Cited
GB1326901A
Cited
GB1365215A
Cited
US4201847A
Cited
US3838076A
Cited
US3925527A
Cited
US4033912A
Cited
US4024090A
Cited
US4058492A
Cited
US3993606A
Cited
US4098731A
Cited
US4218543A
Cited
US4111861A
Cited
GB1520557A
Cited
US4076695A
Cited
US4246363A
Cited
US4269945A
Cited
EP0069286A1
Cited
US4396729A
Cited
US4433067A
Cited
US4444910A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-09-27 | 1992-03-28 | 1992-09-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-09-27 | 1996-03-28 | 1996-09-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-09-27 | 2000-03-28 | 2000-09-27 | $7700.00 | Window Closed / Lapsed |