High-strength zirconia type sintered body and process for preparation thereof
Assignee: Tosoh Corp
•
Filing: 1985-02-21
•
Granted: 1988-09-27
•
Expires: 2005-02-21
Abstract
Abstract A zirconia type sintered body consisting essentially of 50 to 98% by weight of zirconia (ZrO 2 ) containing 1.5 to 5 mole % of yttria (Y 2 O 3 ) and 50 to 2% by weight of alumina (Al 2 O 3 ), spinal (MgAl 2 O 4 ) or mullite (3Al 2 O 3 .2SiO 2 ), and having a three-point bending strength of at least 1700 MPa is provided. This sintered body is prepared by a process wherein a powdery composition consisting essentially of 50 to 98% by weight of (a1) a powder of zirconia containing 1.5 to 5 mole % of yttria or (a2) a mixture comprising 1.5 to 5 mole % of yttria powder and 95 to 98.5 mole % of a zirconia powder and 2 to 50% by weight of (b) a powder of an alumina type oxide selected from alumina, and alumina-magnesia type oxide, an alumina-silica type oxide, a mixture of alumina and magnesia and a mixture of alumina and silica is subjected to a hot isotactic pressing treatment under a pressure of at least 50 MPa at temperature of 1300° C. to 1700° C. or a monoaxially compression-sintering treatment under a pressure of at least 20 MPa at a temperature of 1400° C. to 1700° C.
Inventors
- 👤 Koji Tsukuma
- 👤 Kuniyoshi Ueda
- 👤 Takaaki Tsukidate
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 22:46
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/01; C04B35/48; C04B35/622; C04B35/64; C04B35/645; C04B35/6455; C04B35/10; C04B35/44; C04B35/486; C04B35/488; C04B35/4885
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
207 words
A process for the preparation of a zirconia type sintered body having a three point bending strength of at least 1700 MPa, which comprises the steps of: molding a powdery composition consisting essentially of 50 to 98% by weight of (a1) a powder of zirconia containing 1.5 to 5 mole% of yttria, having an average primary particle size not larger than 0.1 μm, or (a2) a mixture comprising 1.5 to 5 mole% of a yttria powder having an average primary particle size not larger than 0.5 μm and 95 to 98.5 mole% of a zirconia powder having an average primary particle size not larger than 0.1 μm, and 2 to 50% by weight of (b) an α-alumina powder having a specific surface area smaller than 20 m 2 /g and an average primary particle size of 0.2 to 0.4 μm; preliminarily sintering the molded powdery mixture to obtain a preliminarily sintered product composed of grains having an average particle size not larger than 1.5 μm; and isostatically hot-pressing the preliminarily sintered product under pressure of at least 50 MPa at a temperature of 1300° C. to 1700° C., whereby said zirconia type sintered body having a three point bending strength of at least 1700 MPa is obtained.
Claim 2
Dependent Claim
207 words
A process for the preparation of a zirconia type sintered body having a three point bending strength of at least 1700 MPa, which comprises the steps of: molding a powdery composition consisting essentially of 50 to 98% by weight of (a1) a powder of zirconia containing 1.5 to 5 mole% of yttria, having an average primary particle size not larger than 0.1 μm, or (a2) a mixture comprising 1.5 to 5 mole% of a yttria powder having an average primary particle size not larger than 0.5 μm and 95 to 98.5 mole% of a zirconia powder having an average primary particle size not larger than 0.1 μm, and 2 to 50% by weight of (b) an α-alumina powder having a specific surface area smaller than 20 m 2 /g and an average primary particle size of 0.2 to 0.4 μm; preliminarily sintering the molded powdery mixture to obtain a preliminarily sintered product composed of grains having an average particle size not larger than 1.5 μm; and isostatically hot-pressing the preliminarily sintered product under pressure of at least 50 MPa at a temperature of 1300° C. to 1700° C., whereby said zirconia type sintered body having a three point bending strength of at least 1700 MPa is obtained.
Claim 3
Dependent Claim
24 words
A process according to claim 1, wherein the powdery mixture is filled in a capsule and then subjected to the hot isostatic pressing treatment.
Claim 4
Dependent Claim
23 words
A process according to claim 1, wherein the hot isotactic pressing treatment is carried out under pressure of 50 MPa to 500 MPa.
Claim 5
Dependent Claim
60 words
A process according to claim 1, wherein said powdery composition is prepared by adding ammonium carbonate to an aqueous solution containing (a) zirconium, (b) yttrium as a stabilizer and (c) aluminum, aluminum and magnesium, or aluminum and silicon, said elements being in the form of salts, organic metal compounds or oxides of said elements, and thermally decomposing the formed precipitate.
Claim 6
Dependent Claim
34 words
A process according to claim 4, wherein the ammonium carbonate is added at one time to the starting aqueous solution with violent stirring so that the pH value of the solution is about 9.
Claim 7
Dependent Claim
22 words
A process according to claim 4, wherein the precipitate is thermally decomposed in an air atmosphere at 900° C. to 1150° C.
Claim 8
Dependent Claim
23 words
A process according to claim 4, wherein the prepared powdery composition has an average primary particle size of not larger than 0.1 μm.
Claim 9
Dependent Claim
22 words
A process according to claim 4, wherein the molded powdery composition is preliminarily sintered at a temperature not higher than 1500° C.
Claim 10
Dependent Claim
24 words
A process according to claim 4, wherein the hot isostatic pressing treatment is carried out under a pressure of 50 MPa to 500 MPa.
References Cited (Backward Citations)
US4108652A
Cited
DE2810134A1
Cited
US4221650A
Cited
US4314827A
Cited
US4518397A
Cited
US4518398A
Cited
US4336339A
Cited
US4383957A
Cited
US4316964A
Cited
US4506024A
Cited
US4461843A
Cited
US4543341A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-09-27 | 1992-03-28 | 1992-09-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-09-27 | 1996-03-28 | 1996-09-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-09-27 | 2000-03-28 | 2000-09-27 | $7700.00 | Window Closed / Lapsed |