Process for the production of molded polyurethane parts
Assignee: Bayer AG
•
Filing: 1988-01-11
•
Granted: 1988-09-20
•
Expires: 2008-01-11
Abstract
Abstract The present invention is directed to a process for the production of light-resistant, optionally foamed elastomeric molded polyurethanes by reacting (a) organic polyisocyanates which are either mixtures of isophorone diisocyanate with polyisocyanates containing isocyanurate groups and based on 1,6-diisocyanatohexane or mixtures of IPDI with polyisocyanates containing isocyanurate groups and based on 1,6-diisocyanato-hexane and IPDI with organic compounds containing isocyanate-reactive groups in the presence of catalysts, wherein the components are reacted together inside closed molds in an isocyanate index of about 70 to 130. The present invention is additionally directed to the elastomeric polyurethanes prepared by this process.
Inventors
- 👤 Friedhelm Pilger
- 👤 Ulrich Knipp
- 👤 Reinhard Halpaap
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 11:02
CPC Classifications
C; C08; C08G; C08G18/00; C08G18/06; C08G18/70; C08G18/72; C08G18/74; C08G18/75; C08G18/751; C08G18/752; C08G18/753; C08G18/755; C08G18/28; C08G18/65; C08G18/66; C08G18/6666; C08G18/667; C08G18/6681; C08G18/6688; C08G18/721; C08G18/725; C08G18/77; C08G18/78; C08G18/79; C08G18/791; C08G18/792; C08G2120/00
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
233 words
A process for the production of a light-resistant, optionally foamed elastomeric molded polyurethane which comprises reacting (a) an organic polyisocyanate component comprising (1) a mixture of (i) 1-isocyanato-3,3,5-trimethyl-5-isocyanatomethyl-cyclohexane (IPDI) and (ii) a polyisocyanate containing isocyanurate groups and at most 0.5% by weight of unreacted diisocyanate, having an isocyanate content of about 15 to 25% by weight and prepared by the trimerization of a portion of the isocyanate groups of 1,6-diisocyanatohexane in proportions by weight of (i):(ii) of about 0.1:1 to 2.5:1 or (2) a mixture comprising (i) IPDI and (iii) a polyisocyanate containing isocyanurate groups and at most 0.5% by weight of unreacted diisocyanate, having an isocyanate content of about 14 to 24% by weight and prepared by the trimerization of a portion of the isocyanate groups of a mixture of 1,6-diisocyanatohexane and IPDI in which the weight ratio of IPDI to HDI is up to 4:1, the quantity of component (i) being calculated so that the mixture (a2) contains about 10 to 70% by weight of IPDI, including any IPDI still present in component (iii) with (b) an organic compound which contains isocyanate reactive hydrogen atoms and is at least difunctional in isocyanate addition reactions in the presence of (c) a catalyst which accelerates the isocyanate addition reaction, the reactants being reacted together inside a closed mold in proportions which are suitable to provide an isocyanate index of about 70 to 130.
Claim 2
Dependent Claim
233 words
A process for the production of a light-resistant, optionally foamed elastomeric molded polyurethane which comprises reacting (a) an organic polyisocyanate component comprising (1) a mixture of (i) 1-isocyanato-3,3,5-trimethyl-5-isocyanatomethyl-cyclohexane (IPDI) and (ii) a polyisocyanate containing isocyanurate groups and at most 0.5% by weight of unreacted diisocyanate, having an isocyanate content of about 15 to 25% by weight and prepared by the trimerization of a portion of the isocyanate groups of 1,6-diisocyanatohexane in proportions by weight of (i):(ii) of about 0.1:1 to 2.5:1 or (2) a mixture comprising (i) IPDI and (iii) a polyisocyanate containing isocyanurate groups and at most 0.5% by weight of unreacted diisocyanate, having an isocyanate content of about 14 to 24% by weight and prepared by the trimerization of a portion of the isocyanate groups of a mixture of 1,6-diisocyanatohexane and IPDI in which the weight ratio of IPDI to HDI is up to 4:1, the quantity of component (i) being calculated so that the mixture (a2) contains about 10 to 70% by weight of IPDI, including any IPDI still present in component (iii) with (b) an organic compound which contains isocyanate reactive hydrogen atoms and is at least difunctional in isocyanate addition reactions in the presence of (c) a catalyst which accelerates the isocyanate addition reaction, the reactants being reacted together inside a closed mold in proportions which are suitable to provide an isocyanate index of about 70 to 130.
Claim 3
Dependent Claim
30 words
The process of claim 1 wherein mixture (a1) is present and has an IPDI content of about 35 to 65% by weight, based on the total weight of component (a).
Claim 4
Dependent Claim
69 words
The process of claim 1 wherein component (b) comprises a mixture of (1) a polyether polyol having a molecular weight of 500 to 10,000 and a hydroxyl functionality of 2 or 3 or mixtures of such polyether polyols having an average hydroxyl functionality of 2 to 3 and (2) an organic compound having a molecular weight below 500 and a functionality in isocyanate addition reactions of 2 to 3.
Claim 5
Dependent Claim
69 words
The process of claim 2 wherein component (b) comprises a mixture of (1) a polyether polyol having a molecular weight of 500 to 10,000 and a hydroxyl functionality of 2 or 3 or mixtures of such polyether polyols having an average hydroxyl functionality of 2 to 3 and (2) an organic compound having a molecular weight below 500 and a functionality in isocyanate addition reactions of 2 to 3.
Claim 6
Dependent Claim
72 words
The process of claim 3 wherein component (b2) comprises a di- or tri-alkanolamine, and up to about 70% by weight, based on the total weight of component (b2), of a difunctional and/or trifunctional alkane diol and/or triol having a molecular weight of below 500 and optionally containing ether bridges, component (b2) being present in a quantity of about 3 to 50 parts by weight per 100 parts by weight of component (b1).
Claim 7
Dependent Claim
72 words
The process of claim 4 wherein component (b2) comprises a di- or tri-alkanolamine, and up to about 70% by weight, based on the total weight of component (b2), of a difunctional and/or trifunctional alkane diol and/or triol having a molecular weight of below 500 and optionally containing ether bridges, component (b2) being present in a quantity of about 3 to 50 parts by weight per 100 parts by weight of component (b1).
Claim 8
Dependent Claim
15 words
The process of claim 1 wherein component (c) comprises an organic tin and/or lead compound.
Claim 9
Dependent Claim
15 words
The process of claim 1 wherein component (c) comprises dimethyl tin dilaurate or lead octoate.
Claim 10
Dependent Claim
233 words
A light-resistant, optionally foamed elastomeric molded polyurethane which is prepared by a process which comprises reacting (a) an organic polyisocyanate component comprising (1) a mixture of (i) 1-isocyanato-3,3,5-trimethyl-5-isocyanatomethyl-cyclohexane (IPDI) and (ii) a polyisocyanate containing isocyanurate groups and at most 0.5% by weight of unreacted diisocyanate, having an isocyanate content of about 15 to 25% by weight and prepared by the trimerization of a portion of the isocyanate groups of 1,6-diisocyanatohexane in proportions by weight of (i):(ii) of about 0.1:1 to 2.5:1 or (2) a mixture comprising (i) IPDI and (iii) a polyisocyanate containing isocyanurate groups and at most 0.5% by weight of unreacted diisocyanate, having an isocyanate content of about 14 to 24% by weight and prepared by the trimerization of a portion of the isocyanate groups of a mixture of 1,6-diisocyanatohexane and IPDI in which the weight ratio of IPDI to HDI is up to 4:1, the quantity of component (i) being calculated so that the mixture (a2) contains from 10 to 70% by weight of IPDI, including any IPDI still present in component (iii) with (b) an organic compound which contains isocyanate reactive hydrogen atoms and is at least difunctional in isocyanate addition reactions in the presence of (c) a catalyst which accelerates the isocyanate addition reaction, the reactants being reacted together inside a closed mold in proportions which are suitable to provide an isocyanate index of about 70 to 130.
Claim 11
Dependent Claim
233 words
A light-resistant, optionally foamed elastomeric molded polyurethane which is prepared by a process which comprises reacting (a) an organic polyisocyanate component comprising (1) a mixture of (i) 1-isocyanato-3,3,5-trimethyl-5-isocyanatomethyl-cyclohexane (IPDI) and (ii) a polyisocyanate containing isocyanurate groups and at most 0.5% by weight of unreacted diisocyanate, having an isocyanate content of about 15 to 25% by weight and prepared by the trimerization of a portion of the isocyanate groups of 1,6-diisocyanatohexane in proportions by weight of (i):(ii) of about 0.1:1 to 2.5:1 or (2) a mixture comprising (i) IPDI and (iii) a polyisocyanate containing isocyanurate groups and at most 0.5% by weight of unreacted diisocyanate, having an isocyanate content of about 14 to 24% by weight and prepared by the trimerization of a portion of the isocyanate groups of a mixture of 1,6-diisocyanatohexane and IPDI in which the weight ratio of IPDI to HDI is up to 4:1, the quantity of component (i) being calculated so that the mixture (a2) contains from 10 to 70% by weight of IPDI, including any IPDI still present in component (iii) with (b) an organic compound which contains isocyanate reactive hydrogen atoms and is at least difunctional in isocyanate addition reactions in the presence of (c) a catalyst which accelerates the isocyanate addition reaction, the reactants being reacted together inside a closed mold in proportions which are suitable to provide an isocyanate index of about 70 to 130.
Claim 12
Dependent Claim
30 words
The polyurethane of claim 9 wherein mixture (a1) is present and has an IPDI content of about 35 to 65% by weight, based on the total weight of component (a).
Claim 13
Dependent Claim
69 words
The polyurethane of claim 9 wherein component (b) comprises a mixture of (1) a polyether polyol having a molecular weight of 500 to 10,000 and a hydroxyl functionality of 2 or 3 or mixtures of such polyether polyols having an average hydroxyl functionality of 2 to 3 and (2) an organic compound having a molecular weight below 500 and a functionality in isocyanate addition reactions of 2 to 3.
Claim 14
Dependent Claim
69 words
The polyurethane of claim 10 wherein component (b) comprises a mixture of (1) a polyether polyol having a molecular weight of 500 to 10,000 and a hydroxyl functionality of 2 or 3 or mixtures of such polyether polyols having an average hydroxyl functionality of 2 to 3 and (2) an organic compound having a molecular weight below 500 and a functionality in isocyanate addition reactions of 2 to 3.
Claim 15
Dependent Claim
72 words
The polyurethane of claim 11 wherein component (b2) comprises a di- or tri-alkanolamine, and up to about 70% by weight, based on the total weight of component (b2), of a difunctional and/or trifunctional alkane diol and/or triol having a molecular weight of below 500 and optionally containing ether bridges, component (b2) being present in a quantity of about 3 to 50 parts by weight per 100 parts by weight of component (b1).
Claim 16
Dependent Claim
72 words
The polyurethane of claim 12 wherein component (b2) comprises a di- or tri-alkanolamine, and up to about 70% by weight, based on the total weight of component (b2), of a difunctional and/or trifunctional alkane diol and/or triol having a molecular weight of below 500 and optionally containing ether bridges, component (b2) being present in a quantity of about 3 to 50 parts by weight per 100 parts by weight of component (b1).
Claim 17
Dependent Claim
15 words
The polyurethane of claim 9 wherein component (c) comprises an organic tin and/or lead compound.
Claim 18
Dependent Claim
15 words
The polyurethane of claim 9 wherein component (c) comprises dimethyl tin dilaurate or lead octoate.
References Cited (Backward Citations)
US4025466A
Cited
US4150206A
Cited
US4256841A
Cited
US4263408A
Cited
US4324879A
Cited
US4292411A
Cited
US4419513A
Cited
DE3527863A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-09-20 | 1992-03-21 | 1992-09-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-09-20 | 1996-03-21 | 1996-09-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-09-20 | 2000-03-21 | 2000-09-20 | $7700.00 | Window Closed / Lapsed |