Abstract Optical waveguide having a fused silica core and a fluorine doped silica cladding is made by heating a cylinder of silica in fluorine, the cylinder initially having an outer annular particulate or porous region which is dried by the fluorine and into which fluorine diffuses to lower the refractive index of the silica when fused. The cylinder is made by depositing particulate silica onto a mandrel, drying the silica in chlorine, and heating the silica to densify it. Further particulate silica is deposited and is then heated in a fluorine-containing gas to dry, fluorine diffuse, and sinter the porous outer part of the silica. The resulting tubular silica preform is heated to collapse the tubular preform into a rod from which optical waveguide is drawn, the waveguide having a fluorine doped silica cladding. In one alternative the silica cylinder is made by depositing onto a mandrel a first layer of relatively dense silica followed by a second layer of less dense particulate silica so that fluorine diffuses preferentially into the lower density material. In another alternative, the silica cylinder is made by depositing particulate silica directly onto a high purity fused silica rod without using a mandrel, the deposited silica then being dried and subjected to fluorine diffusion.
A method of manufacturing a preform for an optical waveguide comprising: depositing a thick layer of particulate silica onto a mandrel; drying the particulate silica; after the thick layer of particulate silica is deposited, densifying from the inside out an inner region of the thick layer of particulate silica to an extent that gaseous fluorine will not diffuse thereinto while leaving an outer region of the thick layer of particulate silica in a non-densified state so that gaseous fluorine will diffuse thereunto; after the inner region of the thick layer of particulate silica is densified, diffusing gaseous fluorine into the outer region of the thick layer of the particulate silica; removing the mandrel; and consolidating the particulate silica to produce a preform and collapsing the resulting tubular preform to a rod.
Claim 2
Independent Claim
131 words
A method of manufacturing a preform for an optical waveguide comprising: depositing a thick layer of particulate silica onto a mandrel; drying the particulate silica; after the thick layer of particulate silica is deposited, densifying from the inside out an inner region of the thick layer of particulate silica to an extent that gaseous fluorine will not diffuse thereinto while leaving an outer region of the thick layer of particulate silica in a non-densified state so that gaseous fluorine will diffuse thereunto; after the inner region of the thick layer of particulate silica is densified, diffusing gaseous fluorine into the outer region of the thick layer of the particulate silica; removing the mandrel; and consolidating the particulate silica to produce a preform and collapsing the resulting tubular preform to a rod.
Claim 3
Dependent Claim
48 words
A method as recited in claim 1 wherein said step of depositing a thick layer of particulate silica comprises depositing said thick layer of particualte silica onto a graphite mandrel, and said step of densifying said inner region comprises heating said inner region by heating said graphite mandrel.
Claim 4
Dependent Claim
33 words
A method as recited in claim 2 wherein said step of heating said mandrel comprises surrounding said particulate silica with an RF heating coil to cause said mandrel to act as a susceptor.
Claim 5
Dependent Claim
50 words
A method as recited in claim 1 wherein the step of densifying an inner region of the thick layer of particulate silica comprises heating said inner region of the thick layer of particulate by supplying heat from said mandril without heating said outer region by supplying heat from said mandril.