US4770939A
Expired / Lapsed
US
⏱️ 0.0 years remaining
PVdF-based powder coatings
Assignee: TotalEnergies Onetech Belgium SA
•
Filing: 1987-08-27
•
Granted: 1988-09-13
•
Expires: 2007-08-27
Abstract
Abstract A pigmented PVdF-based powder coating product is disclosed, which comprises PVdF resin with a compatible thermoplastic resin, preferably PMMA, in a weight ratio of from 80:20 to 40:60, pigments, and optionally a small amount of flow promoter. Also disclosed is a process for coating a substrate, comprising the steps of (a) applying said powder coating product on a substrate, and (b) subjecting to a heat treatment.
Inventors
- 👤 Willem Sietses
- 👤 Tjalling M. Plantenga
- 👤 Jean-Paul Dekerk
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 04:27
CPC Classifications
B; B29; B29B; B29B13/00; B29B13/10; B05; B05D; B05D5/00; B05D5/08; B05D5/083; B29B9/00; B29B9/02; B29B9/06; C; C08; C08L; C08L27/00; C08L27/02; C08L27/12; C08L27/16; C09; C09D; C09D127/00; C09D127/02; C09D127/12; C09D127/16; C09D133/00; C09D133/04; C09D133/06; C09D133/10; C09D133/12; B05D2401/00; B05D2401/30; B05D2401/32; B05D2506/00; B05D2506/10; C08L33/00; C08L33/04; C08L33/06; C08L33/10; C08L33/12; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2982; Y10T428/2991; Y10T428/2998; Y10T428/31504; Y10T428/31511; Y10T428/3154
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
97 words
A process for preparing pigmented PVdF-based powder coating products, comprising the steps of: (i) mixing PVdF resin with at least one compatible thermoplastic PMMA resin, a minor amount of a low molecular weight acrylic polymer as a flow improver, and a minor amount of at least one pigment, wherein the weight ratio of PVdF-PMMA is from about 80-20 to 40-60; (ii) pelletizing the resulting mixture of (i); (iii) grinding, at a temperature below about -50° C., the resulting pellets of (ii) to form a particulate powder having an average particle size between about 0.03 and 0.05 mm.
Claim 2
Dependent Claim
97 words
A process for preparing pigmented PVdF-based powder coating products, comprising the steps of: (i) mixing PVdF resin with at least one compatible thermoplastic PMMA resin, a minor amount of a low molecular weight acrylic polymer as a flow improver, and a minor amount of at least one pigment, wherein the weight ratio of PVdF-PMMA is from about 80-20 to 40-60; (ii) pelletizing the resulting mixture of (i); (iii) grinding, at a temperature below about -50° C., the resulting pellets of (ii) to form a particulate powder having an average particle size between about 0.03 and 0.05 mm.
Claim 3
Dependent Claim
61 words
The process according to claim 1 wherein the PVdF resin has a molecular weight of about 10,000 to 70,000, the PMMA resin exhibits of visocity of about 7 to 70 P; and the acrylic resin has a molecular weight of about 20,000 and is present in the amount of about 1 weight % based on the total weight of the mixture.
Claim 4
Dependent Claim
14 words
A pigmented PVdF-based powder coating product prepared according to the process of claim 1.
Claim 5
Dependent Claim
19 words
The process according to claim 1 wherein the PVdF resin has a molecular weight of about 10,000 to 70,000.
Claim 6
Dependent Claim
19 words
The process according to claim 4 wherein the PVdF resin has a molecular weight of about 30,000 to 50,000.
Claim 7
Dependent Claim
40 words
The process according to claim 1 wherein the thermoplastic PMMA resin exhibits a viscosity of about 7 to 17 P in 40% solution in which the solvent is a 95:5 by weight mixture of toluene and ethylene glycol methyl ether.
Claim 8
Dependent Claim
17 words
The process according to claim 1 wherein the weight ratio of PVdF/PMMA is from 75:25 to 65:35.
Claim 9
Dependent Claim
37 words
The process according to claim 1 wherein said flow promoting agent admixed in said step (i) is an acrylic resin having a relatively low molecular weight and is present in a concentration of about 1 weight %.
Claim 10
Dependent Claim
24 words
The process according to claim 8 wherein said acrylic resin is made from ethylacrylate and 2-ethylhexylacrylate and has a molecular weight of about 20,000.
Claim 11
Dependent Claim
59 words
The process according to claim 1 wherein the grinding step of (iii) is conducted in a hammer mill in which a rotating shaft carries hammers that break the pellets into small particles on fixed shapes in the casing of the hammer mill and then hammer the small particles through a sieving lining at the bottom of the hammer mill.
Claim 12
Dependent Claim
17 words
The process according to claim 10 wherein the sieving lining has sieve openings of about 0.2 mm.
Claim 13
Dependent Claim
12 words
The process according to claim 1 wherein the pigment is titanium dioxide.
Claim 14
Dependent Claim
21 words
The process according to claim 12 wherein the titanium dioxide is in a concentration of at least about 35 weight %.
Claim 15
Dependent Claim
20 words
The process according to claim 1 wherein the pelletizing is conducted by melt extruding and granulating the mixture of (i).
Claim 16
Dependent Claim
75 words
A process for coating a substrate with a pigmented PVdF-based coating comprising the steps of: (a) applying on a substrate a powder which has been prepared according to the process of claim 1; (b) subjecting the applied powder of (a) to a heat treatment at a temperature between about 180° to 260° C. thereby melting the powder; and (c) cooling the melted powder of (b) to form a stable pigmented PVdF-based coating on said substrate.
Claim 17
Dependent Claim
22 words
The process according to claim 15 wherein the substrate of step (a) has been previously covered with an epoxy-type resin primer coating.
Claim 18
Dependent Claim
12 words
An article of manufacture produced according to the process of claim 16.
Claim 19
Dependent Claim
22 words
The process according to claim 15 wherein the heat treatment is carried out at a temperature of about 180° to 260° C.
References Cited (Backward Citations)
US3324069A
Cited
GB1293650A
Cited
US3944689A
Cited
GB1509404A
Cited
US4065438A
Cited
US4179542A
Cited
US4291112A
Cited
US4563393A
Cited
US4687801A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-09-13 | 1992-03-14 | 1992-09-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-09-13 | 1996-03-14 | 1996-09-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-09-13 | 2000-03-14 | 2000-09-13 | $7700.00 | Window Closed / Lapsed |