Process for the production of carbon fibres which are vapor-deposited from methane
Assignee: Mersen SA
•
Filing: 1985-05-09
•
Granted: 1988-09-13
•
Expires: 2005-05-09
Abstract
Abstract PCT No. PCT/FR85/00110 Sec. 371 Date Jan. 9, 1986 Sec. 102(e) Date Jan. 9, 1986 PCT Filed May 9, 1985 PCT Pub. No. WO85/05383 PCT Pub. Date Dec. 5, 1985.The invention concerns a process for the production of vapor-deposited carbon fibres wherein a gaseous or vaporized hydrocarbon which is entrained by a carrier gas is pyrolyzed on a substrate in a flow reactor at a temperature of between 950 DEG and 1300 DEG C. in two successive stages, a germination stage and a growth stage. The process comprises the following steps: preparing a gaseous mixture comprising from 50 to 90% and preferably from 85 to 65% by volume of hydrogen and/or helium and from 10 to 40% and preferably from 15 to 35% by volume of methane; circulating the mixture in the reactor over a substrate comprising from 10-8 to 10-4 g/cm2 of a catalyst selected from iron, nickel, cobalt and alloys thereof; initiating germination and growth of the carbon fibres in respect of length at a temperature t1 which is stabilized at between 950 DEG and 1050 DEG C., with a substantially constant velocity of the gaseous mixture of between 10 and 50 centimeters per minute for a period of between 10 and 90 minutes; causing growth of the carbon fibres in respect of diameter at a temperature t2 which is higher than 1050 DEG C. and which can attain approximately 1300 DEG C., with a progressively increasing velocity of the gaseous mixture; and cooling the reactor under an inert gas before extracting the carbon fibres.
Inventors
- 👤 Michel Coulon
- 👤 Najib Kandani
- 👤 Lucien Bonnetain
- 👤 Jacques Maire
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 18:35
CPC Classifications
D; D01; D01F; D01F9/00; D01F9/08; D01F9/12; D01F9/127; D01F9/1271; D01F9/1272; B; B82; B82Y; B82Y30/00
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
267 words
A process for the production of vapor-deposited carbon fibers wherein a gaseous or vaporised hydrocarbon which is entrained by a carrier gas is pyrolysed on a substrate in a flow reactor at a temperature of between 950° and 1300° C. in two successive stages, a germination stage and a growth stage, said process comprising the steps of: (a) preparing a gaseous mixture comprising from 50 to 90% by volume of a gas selected from the group consisting of hydrogen, helium and mixtures thereof, and from 10 and 40% by volume of methane; (b) circulating the mixture in the reactor over a substrate comprising from 10 -8 to 10 -4 g/cm 2 of a catalyst selected from the group consisting of iron, nickel, cobalt and alloys thereof; (c) initiating germination and growth of the carbon fibers in respect of length by heating the reactor to a temperature t1 which is stabilised at between 950° and 1050° C., and maintaining a substantially constant velocity of the gaseous mixture of between 10 and 50 centimeters per minute, for a period of between 10 and 90 minutes; (d) causing growth of the carbon fibers in respect of diameter at a temperature t2 which is higher than 1050° C. and which can attain approximately 1300° C., by progressively increasing the velocity of the gaseous mixture and progressively increasing the temperature of the reactor from the germination temperature t1 to the growth temperature t2 at a rate of rise in temperature of between 0.5 and 5° C. per minute; and (e) cooling the reactor under an inert gas before extracting the carbon fibers.
Claim 2
Dependent Claim
267 words
A process for the production of vapor-deposited carbon fibers wherein a gaseous or vaporised hydrocarbon which is entrained by a carrier gas is pyrolysed on a substrate in a flow reactor at a temperature of between 950° and 1300° C. in two successive stages, a germination stage and a growth stage, said process comprising the steps of: (a) preparing a gaseous mixture comprising from 50 to 90% by volume of a gas selected from the group consisting of hydrogen, helium and mixtures thereof, and from 10 and 40% by volume of methane; (b) circulating the mixture in the reactor over a substrate comprising from 10 -8 to 10 -4 g/cm 2 of a catalyst selected from the group consisting of iron, nickel, cobalt and alloys thereof; (c) initiating germination and growth of the carbon fibers in respect of length by heating the reactor to a temperature t1 which is stabilised at between 950° and 1050° C., and maintaining a substantially constant velocity of the gaseous mixture of between 10 and 50 centimeters per minute, for a period of between 10 and 90 minutes; (d) causing growth of the carbon fibers in respect of diameter at a temperature t2 which is higher than 1050° C. and which can attain approximately 1300° C., by progressively increasing the velocity of the gaseous mixture and progressively increasing the temperature of the reactor from the germination temperature t1 to the growth temperature t2 at a rate of rise in temperature of between 0.5 and 5° C. per minute; and (e) cooling the reactor under an inert gas before extracting the carbon fibers.
Claim 3
Dependent Claim
51 words
A process according to claim 1 wherein the duration of the phase for germination and growth in respect of length of the fibers is between 30 and 90 minutes for a temperature of 950° to 1000° C. and between 10 and 30 minutes for a temperature of 950° to 1050° C.
Claim 4
Dependent Claim
53 words
A process according to claim 1 wherein the velocity of the gaseous mixture during the phase of growth of the fibers in respect of diameter is progressively increased from an initial value that is at least equal to 10 centimeters per minute to a final value which may attain 400 centimeters per minute.
Claim 5
Dependent Claim
45 words
A process according to claim 1 wherein the duration of the growth of the fibers in respect of diameter is between 30 and 120 minutes at a temperature of between 1050° and 1300° C., for a final fiber diameter of between 10 and 20 crometers.
Claim 6
Dependent Claim
27 words
A process according to claim 1 wherein, before reaching the substrate, the gaseous mixture is preheated to a temperature that is at least equal to 500° C.
Claim 7
Dependent Claim
21 words
A process according to claim 5 wherein the gaseous mixture is preheated in an auxiliary furnace disposed upstream of the reactor.
Claim 8
Dependent Claim
40 words
A process according to claim 5 wherein the gaseous mixture is preheated by passing over a heat exchanger which is disposed at the intake of the reactor and which is formed for example by a graphite or carbon felt plug.
Claim 9
Dependent Claim
19 words
A process according to claim 1 wherein the substrate is formed by a sheet of graphite such as "PAPYEX".
Claim 10
Dependent Claim
41 words
A process according to claim 1 wherein the fibers, after the end of the growth stage, are graphitised at a temperature of between 2800° and 3200° C. under an inert atmosphere for a period of between 15 minutes and 1 hour.
Claim 11
Dependent Claim
30 words
A process according to claim 1 wherein the gaseous mixture comprises from 85 to 65% by volume of hydrogen and/or helium and from 15 to 35% by volume of methane.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-09-13 | 1992-03-14 | 1992-09-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-09-13 | 1996-03-14 | 1996-09-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-09-13 | 2000-03-14 | 2000-09-13 | $7700.00 | Window Closed / Lapsed |