Transparent coatings by reactive sputtering
Assignee: Messer LLC
•
Filing: 1987-02-02
•
Granted: 1988-09-06
•
Expires: 2007-02-02
Abstract
Abstract A method for depositing a protective coating by cathode sputtering of an alloy of aluminum and silicon in a reactive gas is disclosed. The sputtering target contains sufficient silicon to produce an amorphous coating; 6 to 18 percent silicon is preferred. Targets of approximately 88% aluminum and 12% silicon are especially preferred. Oxygen, nitrogen, compounds of oxygen and compounds of nitrogen are preferred reactive gases. A range of combinations of oxygen and nitrogen are particularly preferred. The method provides durable transparent coatings which may be used as an overcoating for a metal or dielectric coating to provide increased resistance to abrasion and corrosion. In particular, the protected coating may be a metal, dielectric or dielectric-metal-dielectric coating as used in double-glazed window units for buildings or vehicles.
Inventors
- 👤 Abraham I. Belkind
- 👤 Erik Bjornard
- 👤 James J. Hofmann
- 👤 Donald V. Jacobson
- 👤 Steven J. Nadel
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 11:06
CPC Classifications
C; C23; C23C; C23C14/00; C23C14/22; C23C14/34; C03; C03C; C03C17/00; C03C17/34; C03C17/36; C03C17/3602; C03C17/3644; C03C17/22; C03C17/225; C03C17/23; C03C17/245; C03C17/3411; C03C17/3417; C03C17/3429; C03C17/3435; C23C14/06; C23C14/08; C23C14/10; C23C14/14; C03C2217/00; C03C2217/20; C03C2217/21; C03C2217/23; C03C2217/28; C03C2217/281; C03C2217/29; C03C2217/70; C03C2217/78; C03C2218/00; C03C2218/10; C03C2218/15; C03C2218/154; C03C2218/155; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12493; Y10T428/12535; Y10T428/12597; Y10T428/12611; Y10T428/12674; Y10T428/12736; Y10T428/12771; Y10T428/12785; Y10T428/12792; Y10T428/12861; Y10T428/12896
Claims Analysis
Total Claims: 29
Claim 1
Independent Claim
82 words
A method for depositing a coating and a protective overcoating on a substrate comprising: depositing a coating on the substrate; preparing a sputtering target of an alloy comprising aluminum and sufficient silicon to produce an amorphous overcoating; placing the target and the coated substrate in an evacuated chamber; and sputtering the target in an atmosphere comprising a gas having components which react with aluminum and silicon so as to form a transparent amorphous dielectric overcoating containing reaction products of aluminum and silicon.
Claim 2
Independent Claim
82 words
A method for depositing a coating and a protective overcoating on a substrate comprising: depositing a coating on the substrate; preparing a sputtering target of an alloy comprising aluminum and sufficient silicon to produce an amorphous overcoating; placing the target and the coated substrate in an evacuated chamber; and sputtering the target in an atmosphere comprising a gas having components which react with aluminum and silicon so as to form a transparent amorphous dielectric overcoating containing reaction products of aluminum and silicon.
Claim 3
Dependent Claim
21 words
The method according to claim 1, wherein the alloy comprises greater than about 6 percent and less than about 95% silicon.
Claim 4
Dependent Claim
26 words
The method according to claim 2, wherein the reactive gas is selected from the group consisting of oxygen nitrogen, compounds of oxygen, and compounds of nitrogen.
Claim 5
Dependent Claim
25 words
The method according to claim 3, wherein the substrate is transparent and the step of depositing a coating comprises depositing a dielectric-metal-dielectric coating by sputtering.
Claim 6
Independent Claim
68 words
A method for depositing a transparent coating on a substrate comprising: preparing a sputtering target of an alloy comprising aluminum and 6 to 18 percent silicon; placing the target and the substrate in an evacuated chamber; sputtering the target in an atmosphere comprising a gas having components which react with aluminum and silicon so as to form an amorphous dielectric coating containing reaction products of aluminum and silicon.
Claim 7
Independent Claim
68 words
A method for depositing a transparent coating on a substrate comprising: preparing a sputtering target of an alloy comprising aluminum and 6 to 18 percent silicon; placing the target and the substrate in an evacuated chamber; sputtering the target in an atmosphere comprising a gas having components which react with aluminum and silicon so as to form an amorphous dielectric coating containing reaction products of aluminum and silicon.
Claim 8
Dependent Claim
26 words
The method according to claim 5, wherein the reactive gas is selected from the group consisting of nitrogen, oxygen, compounds of oxygen, and compounds of nitrogen.
Claim 9
Dependent Claim
21 words
The method according to claim 6, wherein the alloy comprises 82 to 90 percent aluminum and 10 to 14 percent silicon.
Claim 10
Dependent Claim
21 words
The method according to claim 7, wherein the alloy comprises approximately 88 percent aluminum and 12 percent silicon with incidental impurities.
Claim 11
Dependent Claim
33 words
The method according to claim 6, wherein the reactive gas comprises oxygen and nitrogen and the ratio of oxygen to the total of oxygen and nitrogen is in the range 0.1 to 0.3.
Claim 12
Dependent Claim
21 words
The method according to claim 9, wherein the alloy comprises 82 to 90 percent aluminum and 10 to 14 percent silicon.
Claim 13
Dependent Claim
21 words
The method according to claim 10, wherein the alloy comprises approximately 88 percent aluminum and 12 percent silicon with incidental impurities.
Claim 14
Dependent Claim
48 words
A coated article comprising a substrate, a coating on the substrate, and a protective overcoating on the coating where the overcoating comprises an amorphous dielectric layer of reaction products formed by sputtering a target in a reactive gas wherein the target is an alloy comprising aluminum and silicon.
Claim 15
Dependent Claim
48 words
A coated article comprising a substrate, a coating on the substrate, and a protective overcoating on the coating where the overcoating comprises an amorphous dielectric layer of reaction products formed by sputtering a target in a reactive gas wherein the target is an alloy comprising aluminum and silicon.
Claim 16
Dependent Claim
36 words
A coated article according to claim 12, wherein the alloy comprises 6 to 95 percent silicon and the reactive gas is selected from the group consisting of oxygen, nitrogen, compounds of oxygen, and compounds of nitrogen.
Claim 17
Dependent Claim
41 words
A coated article according to claim 13, wherein the substrate is transparent, the coating comprises a multilayer dielectric-metal-dielectric coating, and the materials of the dielectric layers are selected from the group consisting of oxides of bismuth, indium, tin, titanium and zinc.
Claim 18
Dependent Claim
14 words
The coated article according to claim 13, wherein the coating is a dielectric-metal-zinc oxide.
Claim 19
Dependent Claim
34 words
The coated article according to claim 15, wherein the reactive gas contains oxygen and nitrogen and the ratio of oxygen to the total of oxygen and nitrogen is in the range 0.1 to 0.3.
Claim 20
Dependent Claim
34 words
The coated article according to claim 13, wherein the reactive gas contains oxygen and nitrogen and the ratio of oxygen to the total of oxygen and nitrogen is in the range 0.1 to 0.3.
Claim 21
Dependent Claim
14 words
The coated article according to claim 17, wherein the coating is a dielectric-silver coating.
Claim 22
Dependent Claim
34 words
A coated article comprising a substrate and an amorphous dielectric coating of reaction products formed by sputtering a target comprising an alloy of aluminum and 6 to 18 percent silicon in a reactive gas.
Claim 23
Dependent Claim
34 words
A coated article comprising a substrate and an amorphous dielectric coating of reaction products formed by sputtering a target comprising an alloy of aluminum and 6 to 18 percent silicon in a reactive gas.
Claim 24
Dependent Claim
26 words
The article according to claim 19, wherein the reactive gas is selected from the group consisting of oxygen, nitrogen, compounds of oxygen, and compounds of nitrogen.
Claim 25
Dependent Claim
34 words
The coated article according to claim 20, wherein the reactive gas contains oxygen and nitrogen and the ratio of oxygen to the total of oxygen and nitrogen is in the range 0.1 to 0.3.
Claim 26
Dependent Claim
25 words
The coated article according to claim 21, wherein the substrate comprises a transparent base and a dielectric-metal coating over which the amorphous coating is deposited.
Claim 27
Dependent Claim
25 words
The article according to claim 21, wherein the substrate comprises a transparent base and a dielectric-metal-zinc oxide coating over which the amorphous coating is deposited.
Claim 28
Dependent Claim
22 words
The coated article according to claim 23, wherein the alloy contains approximately 88 percent aluminum and 12 percent silicon with incidental impurities.
Claim 29
Dependent Claim
31 words
The coated article of claim 24, further comprising a transparent sheet, and means for sealing the sheet and the base to form a double-glazed window unit with the amorphous coating inside.
References Cited (Backward Citations)
US4125446A
Cited
US4610771A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-09-06 | 1992-03-07 | 1992-09-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-09-06 | 1996-03-07 | 1996-09-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-09-06 | 2000-03-07 | 2000-09-06 | $7700.00 | Window Closed / Lapsed |