US4766033A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Highly heat-sensitive film for stencil
Assignee: Asahi Kasei Corp
•
Filing: 1986-07-14
•
Granted: 1988-08-23
•
Expires: 2006-07-14
Abstract
Abstract The present invention relates to a highly sensitive heat-sensitive film for stencil. This invention provides a highly heat-sensitive film for stencil, comprising a thermoplastic resin having a coefficient of temperature and melt viscosity (ΔT/Δ log VI) of not more than 100 and a thermal shrinkage (X%) at 100° C. and a thermal shrinkage stress (Y g/mm 2 ) at 100° C. falling respectively in the ranges of the formulas; 15≦X≦80 and 75≦Y≦500; and both falling in the range of the formula; -8X+400≦Y≦-10X+1000; having a thickness in the range of 0.5 to 15 μm, and excelling in low-energy perforation property. The film of this invention is superior in a low temperature perforation property, capable of being perforated with a low energy thermal head or with a low energy flash irradiation for making a plate; expansion of perforations is small when the film is perforated; and its change with time (dimensional change) is small and its sizes are stable.
Inventors
- 👤 Isao Yoshimura
- 👤 Takashi Nakao
- 👤 Mitsuo Kohno
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 16:15
CPC Classifications
B; B41; B41N; B41N1/00; B41N1/24; B41N1/245; Y; Y10; Y10S; Y10S428/00; Y10S428/91; Y10T; Y10T428/00; Y10T428/26; Y10T428/27; Y10T428/29; Y10T428/2913; Y10T428/31504; Y10T428/31507; Y10T428/31725; Y10T428/31739; Y10T428/31743; Y10T428/31746; Y10T428/31779; Y10T428/31783; Y10T428/31786; Y10T428/3179; Y10T428/31855; Y10T428/31909; Y10T428/31913; Y10T428/3192
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
84 words
A highly heat-sensitive film for stencil, comprising a thermoplastic resin having a coefficient of temperature and melt viscosity (ΔT/Δ log VI) of not more than 100 and a thermal shrinkage (X%) at 100° C. and a thermal shrinkage stress (Y g/mm 2 ) at 100° C. falling respectively in the ranges of the formulas; 15≦X≦80 and 75≦Y≦500; and both falling in the range of the formula; -8X+400≦Y≦-10X+1000; having a thickness in the range of 0.5 to 15 μm, and excelling in low-energy perforation property.
Claim 2
Dependent Claim
84 words
A highly heat-sensitive film for stencil, comprising a thermoplastic resin having a coefficient of temperature and melt viscosity (ΔT/Δ log VI) of not more than 100 and a thermal shrinkage (X%) at 100° C. and a thermal shrinkage stress (Y g/mm 2 ) at 100° C. falling respectively in the ranges of the formulas; 15≦X≦80 and 75≦Y≦500; and both falling in the range of the formula; -8X+400≦Y≦-10X+1000; having a thickness in the range of 0.5 to 15 μm, and excelling in low-energy perforation property.
Claim 3
Dependent Claim
25 words
A film according to claim 1, wherein the thermoplastic resin has a coefficient of temperature and melt viscosity in the range of 80 to 3.
Claim 4
Dependent Claim
22 words
A film according to claim 1, wherein said thermoplastic resin has a degree of crystallinity in the range of 0 to 30%.
Claim 5
Dependent Claim
23 words
A film according to claim 1, wherein said thermoplastic resin has a Vicat softening point in the range of 40° to 200° C.
Claim 6
Dependent Claim
30 words
A film according to claim 1, wherein said thermoplastic resin in a state forming a film has a constitution falling between substantially amorphous level and a degree, 15%, of crystallinity.
Claim 7
Dependent Claim
36 words
A film according to claim 1, wherein said thermoplastic resin has, as an additive component, at least one monomer copolymerized therewith in an amount of not less than 10 mol% and not more than 40 mol%.
Claim 8
Dependent Claim
24 words
A film according to claim 1, wherein said thermoplastic resin is a thermoplastic resin having copolymerized polyesters and copolymerized polyamides as main components thereof.
Claim 9
Dependent Claim
39 words
A film according to claim 7, wherein said copolymerized polyesters and copolymerized polyamides have as an additive component at least one monomer copolymerized therewith in an amount of not less than 10 mol% and not more than 40 mol%.
Claim 10
Dependent Claim
30 words
A film according to claim 7, wherein said thermoplastic resin in a state forming a film has a constitution falling between substantially amorphous level and a degree, 15%, of crystallinity.
Claim 11
Dependent Claim
21 words
A film according to claim 1, wherein said thermoplastic resin has a substantially amorphous copolymerized polyester as a main component thereof.
Claim 12
Dependent Claim
39 words
A film according to claim 1, wherein said thermal shrinkage (X%) of the film at 100° C. falls in the range of 30≦X≦80 and said thermal shrinkage stress (Y g/mm 2 ) thereof falls in the range of 100≦Y≦450.
Claim 13
Dependent Claim
112 words
A highly sensitive stencil sheet excellent in low-energy perforation property, which stencil sheet comprises a film 0.5 to 15 μm in thickness consisting of a thermoplastic resin having a coefficient of temperature and melt viscosity (ΔT/Δ log VI) of not more than 100 and exhibiting a thermal shrinkage (X%) at 100° C. and a thermal shrinkage stress (Y g/mm 2 ) respectively falling in the ranges of the formulas; 15≦X≦80 and 75≦Y≦500, and both falling in the range of the formula; -8X+400≦Y≦-10X+1000; and a porous supporting member permitting permeation therethrough of printing ink, avoiding substantial degeneration under heating conditions existing during the perforation of said film, and having said film laminated thereon.
Claim 14
Dependent Claim
112 words
A highly sensitive stencil sheet excellent in low-energy perforation property, which stencil sheet comprises a film 0.5 to 15 μm in thickness consisting of a thermoplastic resin having a coefficient of temperature and melt viscosity (ΔT/Δ log VI) of not more than 100 and exhibiting a thermal shrinkage (X%) at 100° C. and a thermal shrinkage stress (Y g/mm 2 ) respectively falling in the ranges of the formulas; 15≦X≦80 and 75≦Y≦500, and both falling in the range of the formula; -8X+400≦Y≦-10X+1000; and a porous supporting member permitting permeation therethrough of printing ink, avoiding substantial degeneration under heating conditions existing during the perforation of said film, and having said film laminated thereon.
Claim 15
Dependent Claim
23 words
A stencil sheet according to claim 12, wherein said thermoplastic resin has a degree of crystallinity in the range of 0 to 30%.
Claim 16
Dependent Claim
24 words
A stencil sheet according to claim 12, wherein said thermoplastic resin has a Vicat softening point in the range of 40° to 200° C.
Claim 17
Dependent Claim
27 words
A stencil sheet according to claim 12, wherein said film of thermoplastic resin has a constitution falling between substantially amorphous level and a degree, 15%, of crystallinity.
Claim 18
Dependent Claim
28 words
A stencil sheet according to claim 12, wherein said thermoplastic resin is selected from among the thermoplastic resins having copolymerized polyesters and copolymerized polyamides as main components thereof.
Claim 19
Dependent Claim
23 words
A stencil sheet according to claim 10 or claim 11, wherein said thermoplastic resin is formed mainly of a substantially amorphous copolymerized polyester.
Claim 20
Dependent Claim
45 words
A stencil sheet according to claim 12, wherein said porous supporting member is selected from among thin tissues obtained by combining and bundling fibers of basis weight of 30 to 3 (g/m 2 ) and woven fabrics obtained by weaving fibers 500 to 15 mesh.
Claim 21
Dependent Claim
31 words
A stencil sheet according to claim 12, wherein said film and said porous supporting member are bonded to each other with an adhesive composition of 0.1 to 8 (g/m 2 ).
Claim 22
Dependent Claim
101 words
A perforated film comprising a film prepared by perforating a film comprising a thermoplastic resin having a coefficient of temperature and melt viscosity (ΔT/Δ log VI) of not more than 100 and a thermal shrinkage (X%) at 100° C. and a thermal shrinkage stress (Y g/mm 2 ) at 100° C. falling respectively in the ranges of the formulas; 15≦X≦80 and 75≦Y≦500; and both falling in the range of the formula; -8X+400≦Y≦-10X+1000, having a thickness in the range of 0.5 to 15 μm, and possessing substantially discontinuous perforations 1 to 200 dots/mm at least in one direction of a perforated area.
Claim 23
Dependent Claim
101 words
A perforated film comprising a film prepared by perforating a film comprising a thermoplastic resin having a coefficient of temperature and melt viscosity (ΔT/Δ log VI) of not more than 100 and a thermal shrinkage (X%) at 100° C. and a thermal shrinkage stress (Y g/mm 2 ) at 100° C. falling respectively in the ranges of the formulas; 15≦X≦80 and 75≦Y≦500; and both falling in the range of the formula; -8X+400≦Y≦-10X+1000, having a thickness in the range of 0.5 to 15 μm, and possessing substantially discontinuous perforations 1 to 200 dots/mm at least in one direction of a perforated area.
References Cited (Backward Citations)
US3595166A
Cited
US3696742A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-08-23 | 1992-02-22 | 1992-08-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-08-23 | 1996-02-22 | 1996-08-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-08-23 | 2000-02-22 | 2000-08-23 | $7700.00 | Window Closed / Lapsed |